Effects of impregnation with Imersol-aqua on the modulus of elasticity in bending of laminated wood materials
Source abstract
Abstract
Abstract The aim of this study was to investigate the impacts of impregnation with Imersol-aqua on the modulus of elasticity in bending (MOE) of some laminated wood materials. For this aim, oriental beech ( Fagus orientalis Lipsky), oak ( Quercus petrea Liebl.), Scotch pine ( Pinus sylvestris Lipsky), oriental spruce ( Picea orientalis Lipsky) and Uludag fir ( Abies bornmulleriana Lipsky) wood materials impregnated with Imersol-aqua according to ASTM D 1413-99 and producers’ definition. Laminated wood samples were produced from impregnated wood materials according to TS EN 386 in the five ply form (4 mm each) from oriental beech, oak, Scotch pine, Uludag fir and oriental spruce wood by using Desmodur-VTKA adhesive. The MOE values were measured according to TS EN 408. Consequently, the MOE of impregnated + laminated ( I + L W ) softwoods, pine, spruce and fir increased, respectively by 8.07%, 2.62% and 2.45% whereas the MOE of laminated + laminated hardwoods, beech and oak decreased, respectively by 5.06% and 4.37% with respect to laminated control samples ( L W ). Considering the interaction of wood type and process, the MOE was obtained from laminated oriental beech, whereas the lowest was found for impregnated Uludag fir. In consequence, in the massive construction and furniture elements that the MOE after the impregnation and lamination ( I + L W ) is of great concern, oriental beech and Scotch pine materials could be recommended.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Wood Treatment and Properties · Natural Fiber Reinforced Composites · Materials Engineering and Processing
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (23)
Show source-provided references
1. Technological properties of laminated black pine (Pinus nigra var. pallasiana)
2. Potential uses of laminated veneer lumber in furniture
3. Döngel N. Impacts of bending strength the species of wood, adhesive type and number of layer in laminated wood materials. MS thesis, Gazi University Institute of Science and Technology, Turkey, 1999.
4. Keskin H. Technological properties of laminated wood materials and possibilities of using them in woodworking industry. PhD thesis, Gazi University Institute of Science and Technology, Turkey, 2001.
5. Richardson · 1987
6. Studies of the degradation and protection of wood surfaces10.1007/BF00194471 ↗
7. The effect of two accelerated treating methods on wood strength
8. Investigations of the influence of wood preservatives on strength
9. Mechanical properties of longleaf pine treated water-born salt preservatives
10. Effect of treatment conditions using the hot-cold method of impregnation pine wood with water solution of static bending of treated wood
11. Özçifci A. Technological properties of laminated wood materials impregnated with some chemicals. PhD thesis, Gazi University Institute of Science and Technology, Turkey, 2001.
12. Hickson’s Timber Impregnation Co. (GB) Ltd., Into the 21st Century, Imersol-aqua brochure, Hickson timber treatments datasheet, 2000; 2:1–4.
13. Bonding strength of some adhesives in wood materials impregnated with Imersol-aqua
14. TS 2472. Assessment volume density for the mechanical and physical tests of woods. TSE, Ankara, 1976.
15. TS 2471. Assessment of humidity for the mechanical and physical tests of woods. TSE, Ankara, 1976.
16. ASTM D 1413-99. Standard test method of testing wood preservatives by laboratory soil block cultures. ASTM Standards 1976.
17. TS 344. General methods for the conservation of wood materials. TSE, Ankara, 1981.
18. TS 345. Test methods for determining the impacts of wood impregnation materials. TSE, Ankara, 1974.
19. TS EN 386. Glued laminated timber – Performance requirements and minimum production requirements. TSE, Ankara, 1999.
20. TS EN 408. Timber structures, test methods – Solid timber and glued laminated timber – Determination of some physical and mechanical properties. TSE, Ankara, 1997.
21. Functional natural polymers: A new dimensional creativity in lignocellulosic chemistry
22. Bonding strength of poly(vinylacetate)-based adhesive in some wood materials treated with impregnation10.1002/(SICI)1097-4628(20000531)76:9<1472::AID-APP11>3.0.CO;2-O ↗
23. Kollman · 1968 · Vol. 1