Kinetics and Pore Formation of the Sodium Metal Anode on NASICON‐Type Na_3.4Zr₂Si_2.4P_0.6O₁₂ for Sodium Solid‐State Batteries

Abstract In recent years, many efforts have been made to introduce reversible alkali metal anodes using solid electrolytes in order to increase the energy density of next‐generation batteries. In this respect, Na_3.4Zr₂Si_2.4P_0.6O₁₂ is a promising solid electrolyte for solid‐state sodium batteries, due to its high ionic conductivity and apparent stability versus sodium metal. The formation of a kinetically stable interphase in contact with sodium metal is revealed by time‐resolved impedance analysis, in situ X‐ray photoelectron spectroscopy, and transmission electron microscopy. Based on pressure‐ and temperature‐dependent impedance analyses, it is concluded that the Na|Na_3.4Zr₂Si_2.4P_0.6O₁₂ interface kinetics is dominated by current constriction rather than by charge transfer. Cross‐sections of the interface after anodic dissolution at various mechanical loads visualize the formed pore structure due to the accumulation of vacancies near the interface. The temporal evolution of the pore morphology after anodic dissolution is monitored by time‐resolved impedance analysis. Equilibration of the interface is observed even under extremely low external mechanical load, which is attributed to fast vacancy diffusion in sodium metal, while equilibration is faster and mainly caused by creep at increased external load. The presented information provides useful insights into a more profound evaluation of the sodium metal anode in solid‐state batteries.