The strength properties of alkali-activated silica fume mortars

In this study, the strength properties of alkali-activated silica fume (SF) mortars were investigated. The crushed limestone sand with maximum size of 0-5 mm and the sodium meta silicate ($Na_2SiO_3$) used to activate the binders were kept constant in the mortar mixtures. The mortar specimens using the replacement ratios of 0, 25, 50, 75 and 100% SF by weight of cement together with $Na_2SiO_3$ at a constant rate were produced in addition to the control mortar produced by only cement. Moreover, the mortar specimens using the replacement ratio of 4% titanium dioxide ($TiO_2$) by weight of cement in the same mixture proportions were produced. The prismatic specimens produced from eleven different mixtures were de-moulded after a day, and the wet or dry cure was applied on the produced specimens at laboratory condition until the specimens were used for flexural strength ($f_fs$) and compressive strength ($f_c$) measurement at the ages of 7, 28 and 56 days. The $f_fs$ and $f_c$ values of mortars applied the wet or dry cure were compared with the results of control mortar. The findings revealed that the $f_c$ results of the alkali activated 50% SF mortars were higher than that of mortar produced with Portland cement only. It was found that the $f_fs$ and $f_c$ of alkali-activated SF mortars cured in dry condition was averagely 4% lower than that of alkali-activated SF mortars cured in wet condition.