Effect of ER:YAG Laser Irradiation on the Load-Bearing Capacity and Reliability of All-Ceramic Zirconia Crowns
Source abstract
Abstract
Background: This study evaluated the effect of Erbium:Yttrium–Aluminum–Garnet (Er:YAG) laser irradiation on the fracture load, failure mode, and reliability of monolithic and porcelain-veneered zirconia crowns. Methods: Monolithic ultra-translucent zirconia crowns (5YZ-M, n = 30) and porcelain-veneered zirconia crowns (3YZ-V, n = 30) were divided into control (Ctrl-no surface treatment) and Er:YAG laser irradiation (Las) groups (n = 15). Las was performed on the cementation surface (250 mJ, 10 Hz, 2.5 W for 30 s). Crowns were adhesively cemented onto dentin-analog abutments and subjected to compressive load-to-failure testing. Data were analyzed by two-way ANOVA, Tukey’s post hoc test, and Weibull analysis (α = 0.05). Fractographic analysis was performed. Results: Laser irradiation did not affect the fracture load (p = 0.183). Monolithic crowns (5YZ-M) showed significantly higher fracture load than veneered crowns (3YZ-V) (p < 0.001). There was no effect of the interaction between factors (p = 0.150). The m-values were similar among groups, while the L0 of 3YZ-V-Ctrl was significantly lower than that of 5YZ-M. Veneered restorations predominantly showed chipping and delamination; whereas, monolithic crowns mainly exhibited catastrophic failures. Fracture origins were mostly located at the occlusal loading area. Conclusions: Er:YAG laser irradiation of the cementation surface did not affect the load-bearing capacity or structural reliability of zirconia crowns.
Source: crossref · Quality: baseline
Research context
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Post-Graduation Program in Dentistry, University of Passo Fundo (UPF), Passo Fundo 99052-900, RS, Brazil
Special Laboratory of Lasers in Dentistry (LELO), School of Dentistry–USP, São Paulo 05508-000, SP, Brazil
Division of Dentistry, School of Medical Science, The University of Manchester, Manchester M13 9PL, UK
Funding
FAPESP
References (43)
Show source-provided references
1. Novel zirconia materials in dentistry10.1177/0022034517737483 ↗
2. Ultra-translucent zirconia processing and aging effect on microstructural, optical, and mechanical properties10.1016/j.dental.2022.02.016 ↗
3. Flexural strength and reliability of translucent zirconia for monolithic crowns: A systematic review
4. Ceramic materials in dentistry: Historical evolution and current practice10.1111/j.1834-7819.2010.01299.x ↗
5. Clinical outcomes of tooth-supported monolithic zirconia versus porcelain-veneered zirconia fixed dental prostheses: A systematic review and meta-analysis10.1007/s00784-023-05219-4 ↗
6. Systematic review evaluating the influence of the prosthetic material type on the clinical outcomes of implant-supported fixed dental prostheses10.1111/clr.14103 ↗
7. Monolithic zirconia as a valid alternative to metal-ceramic implant-supported restorations: A systematic review and meta-analysis
8. Durability of resin bonding to translucent zirconia materials: An in vitro study10.1016/j.prosdent.2025.03.017 ↗
9. Alshali, R.Z., Alqahtani, M.A., Alturki, B.N., Algizani, L.I., Batarfi, A.O., Alshamrani, Z.K., Faden, R.M., Bukhary, D.M., and Altassan, M.M. (2024). Effect of air-particle abrasion and methacryloyloxydecyl phosphate primer on fracture load of thin zirconia crowns: An in vitro study. Front. Dent. Med., 5.10.3389/fdmed.2024.1501909 ↗
10. Particle air abrasion on 3Y-TZP and 5Y-TZP zirconia: Evaluation of surface characteristics and bonding performance
11. Effect of airborne-particle abrasion protocols and MDP primer on bonding durability of highly translucent zirconia
12. Adhesion to dental ceramics10.1007/s40496-014-0030-y ↗
13. Valente, F., Mavriqi, L., and Traini, T. (2020). Effects of 10-MDP based primer on shear bond strength between zirconia and new experimental resin cement. Materials, 13.10.3390/ma13010235 ↗
14. Łagodzińska, P., Witzler, M., Rupp, F., Pabst, A.M., Stawarczyk, B., and Liebermann, A. (2023). Influence of alumina airborne-particle abrasion on zirconia surface properties and mechanical performance. Coatings, 13.10.3390/coatings13101691 ↗
15. Kim, H.K., Yoo, K.W., Kim, S.J., and Jung, C.H. (2021). Phase transformations and subsurface changes in three dental zirconia grades after sandblasting with various Al2O3 particle sizes. Materials, 14.10.3390/ma14185321 ↗
16. Optical behavior and clinical indications of high-translucency zirconia ceramics: A contemporary review
17. Improving fracture resistance of 5Y-PSZ-based zirconia restorations: Effect of restoration design and surface treatment
18. Reliability and mode of failure of bonded monolithic and multilayer ceramics10.1016/j.dental.2016.11.014 ↗
19. Cyclic contact fatigue resistance of ceramics for monolithic and multilayer dental restorations10.1016/j.dental.2020.02.006 ↗
20. Çelik, Ç.S., Kılıçarslan, M.A., Deniz, S.T., Mumcu, E., and Özkan, P. (2025). Effect of hydrothermal aging on mechanical and optical properties of 3Y-TZP, 4Y-TZP and 5Y-TZP zirconia. Materials, 18.
21. The impact of aging and thickness on flexural strength and translucency of high-translucency zirconia ceramics
22. Salama, A.A., Shehab, K.A., Bushra, S.S., and Hamza, F.S. (2024). The effect of aging on the translucency of contemporary zirconia materials. BMC Oral Health, 24.10.1186/s12903-024-04465-6 ↗
23. Mirt, B., Stawarczyk, B., Özcan, M., Liebermann, A., and Rupp, F. (2024). Surface damage and mechanical reliability of translucent zirconia after airborne-particle abrasion. Materials, 17.
24. Failure behavior of zirconia crowns subjected to air abrasion with different particle sizes10.1590/0103-6440202304998 ↗
25. Pantea, M., Witzler, M., Rupp, F., Stawarczyk, B., and Liebermann, A. (2025). Effects of different surface treatments and accelerated aging on zirconia phase composition and bond durability. Materials, 18.
26. Effect of airborne-particle abrasion with a novel spherical abrasive on the zirconia surface10.1016/j.prosdent.2021.12.022 ↗
27. Effect of Er laser surface treatment on surface properties and shear-bond strength of resin-cement to three translucent zirconia: An in vitro study10.1007/s43939-024-00101-w ↗
28. Yoon, J.Y., Park, J.M., Kim, M., Oh, G.J., Kim, J.H., and Kim, W.C. (2025). Improving zirconia-resin cement bonding through laser surface texturing. Materials, 18.10.3390/prosthesis7010019 ↗
29. Influence of Er laser surface treatment on flexural and bond strengths to glass-infiltrated zirconia-reinforced ceramic10.1007/s10103-020-03205-w ↗
30. Garcia-Sanz, V., Paredes-Gallardo, V., Mendoza-Yero, O., Carbonell-Leal, M., Albaladejo, A., Montiel-Company, J.M., and Bellot-Arcís, C. (2018). The effects of lasers on bond strength to ceramic materials: A systematic review and meta-analysis. PLoS ONE, 13.10.1371/journal.pone.0190736 ↗
31. Bonding and debonding of zirconia using laser approaches10.11607/ijp.7991 ↗
32. Effect of laser irradiation on bond strength between zirconia and resin cement or veneer ceramic: A systematic review and meta-analysis10.4103/jips.jips_590_20 ↗
33. Oliveira, A.R., Ziglioli, N.U., Marocho, S.M.S., Satterthwaite, J., and Borba, M. (2024). Effect of the CAD/CAM Milling Protocol on the Fracture Behavior of Zirconia Monolithic Crowns. Materials, 17.10.3390/ma17122981 ↗
34. Effect of various lasers on the bond strength of two zirconia ceramics10.1089/pho.2014.3841 ↗
35. Effect of Er laser irradiation on bonding property of zirconia ceramics to resin cement10.1089/pho.2013.3489 ↗
36. Is the Er laser affect the surface characteristics and bond strength of Y-TZP?10.1590/0103-6440202104739 ↗
37. Evaluation of surface topography of zirconia ceramic after Er laser etching10.1089/pho.2014.3730 ↗
38. Tzanakakis, E.C., Skoulas, E., Pepelassi, E., Koidis, P., and Tzoutzas, I.G. (2021). The use of lasers in dental materials: A review. Materials, 14.10.3390/ma14123370 ↗
39. Tzanakakis, E.G.C., Beketova, A., Papadopoulou, L., Kontonasaki, E., and Tzoutzas, I.G. (2021). Novel femto laser patterning of high translucency zirconia as an alternative to conventional particle abrasion. Dent. J., 9.10.3390/dj9020020 ↗
40. Effects of different frequencies of Er: YAG laser on the bonding properties of zirconia ceramic10.1007/s10103-022-03660-7 ↗
41. Influence of surface finishing on fracture load and failure mode of glass ceramic crowns10.1016/j.prosdent.2016.12.012 ↗
42. Evaluation of the surface roughness and morphologic features of Y-TZP ceramics after different surface treatments10.1089/pho.2008.2293 ↗
43. Friction Tuning of Interlayer Exciton Recombination in Van der Waals Heterostructures10.1002/adma.202502986 ↗