Effects of temperature-induced lattice distortion and phase evolution on electromagnetic wave absorption in high-entropy powders
Source abstract
Abstract
The formation of a single-phase high-entropy boride induced an increased lattice distortion rate, which subsequently enhanced the electromagnetic wave absorption performance.
Only a short abstract or summary was supplied by the source.
Source: crossref · Quality: short
Affiliations
State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan, 430070, China
School of Materials Science and Engineering, Wuhan University of Technology, Wuhan, 430070, China
Hubei Longzhong Laboratory, Xiangyang 441000, Hubei, China
State Key Laboratory of High Performance Ceramics, Shanghai Institute of Ceramics, Shanghai 200050, China
Funding
National Natural Science Foundation of China
References (43)
Show source-provided references
1. Ma · Crit. Rev. Solid State Mater. Sci. · 2022 · 48 · 72610.1080/10408436.2022.2118663 ↗
2. Zhang · J. Mater. Sci. Technol. · 2023 · 132 · 4210.1016/j.jmst.2022.05.046 ↗
3. Jian · ACS Appl. Mater. Interfaces · 2019 · 11 · 1586910.1021/acsami.8b22448 ↗
4. Zhang · J. Magn. Magn. Mater. · 2020 · 494 · 16582810.1016/j.jmmm.2019.165828 ↗
5. Wang · Carbon · 2018 · 140 · 69610.1016/j.carbon.2018.09.006 ↗
6. Qi · Natl. Sci. Rev. · 2025 · nwaf39410.1093/nsr/nwaf394 ↗
7. Zhang · J. Mater. Sci. Technol. · 2021 · 87 · 15510.1016/j.jmst.2021.01.059 ↗
8. Wang · Mater. Today Nano. · 2025 · 29 · 10057210.1016/j.mtnano.2025.100572 ↗
9. Zhang · J. Adv. Ceram. · 2021 · 10 · 129910.1007/s40145-021-0505-y ↗
10. Zhang · J. Alloys Compd. · 2023 · 966 · 17159310.1016/j.jallcom.2023.171593 ↗
11. Zeng · Mater. Today Commun. · 2025 · 43 · 11167010.1016/j.mtcomm.2025.111670 ↗
12. Mallik · J. Eur. Ceram. Soc. · 2012 · 32 · 254510.1016/j.jeurceramsoc.2012.02.013 ↗
13. Gu · Matter · 2025 · 8 · 10200410.1016/j.matt.2025.102004 ↗
14. Qin · J. Appl. Phys. · 2012 · 111 · 06130110.1063/1.3688435 ↗
15. Cheng · J. Materiomics · 2021 · 7 · 123310.1016/j.jmat.2021.02.017 ↗
16. Gong · J. Mater. Sci. · 2022 · 57 · 921810.1007/s10853-022-07238-0 ↗
17. Liu · J. Adv. Ceram. · 2025 · 14 · 922103010.26599/JAC.2025.9221030 ↗
18. Yang · J. Mater. Sci. Technol. · 2024 · 178 · 13310.1016/j.jmst.2023.08.034 ↗
19. Yang · J. Asian Ceram. Soc. · 2021 · 9 · 127510.1080/21870764.2021.1966978 ↗
20. Nan · J. Mater. Sci.: Mater. Electron. · 2022 · 33 · 16488
21. Zhu · J. Mater. Chem. · 2011 · 21 · 1358110.1039/c1jm11747e ↗
22. Yang · Ceram. Int. · 2023 · 49 · 1952310.1016/j.ceramint.2023.02.170 ↗
23. Zhang · Ultramicroscopy · 2019 · 202 · 11410.1016/j.ultramic.2019.04.007 ↗
24. Wang · Sci. Adv. · 2024 · 10 · eadp437210.1126/sciadv.adp4372 ↗
25. Burke · Surf. Interface Anal. · 2004 · 11 · 35310.1002/sia.740110614 ↗
26. Ci · Nat. Mater. · 2010 · 9 · 43010.1038/nmat2711 ↗
27. Aydoğdu · J. Eur. Ceram. Soc. · 2003 · 23 · 302110.1016/S0955-2219(03)00092-X ↗
28. Guo · Adv. Compos. Hybrid Mater. · 2025 · 8 · 20710.1007/s42114-024-01209-6 ↗
29. Green · J. Materiomics · 2019 · 5 · 50310.1016/j.jmat.2019.07.003 ↗
30. Sun · Adv. Mater. · 2014 · 26 · 812010.1002/adma.201403735 ↗
31. Jin · Nano Res. · 2024 · 17 · 729010.1007/s12274-024-6745-8 ↗
32. Xia · Adv. Funct. Mater. · 2022 · 32 · 220459110.1002/adfm.202204591 ↗
33. Wang · ACS Nano · 2012 · 6 · 1100910.1021/nn304630h ↗
34. Guo · J. Eur. Ceram. Soc. · 2008 · 28 · 127910.1016/j.jeurceramsoc.2007.08.009 ↗
35. Neuman · J. Eur. Ceram. Soc. · 2021 · 41 · 743410.1016/j.jeurceramsoc.2021.08.004 ↗
36. Liu · Compos. Pt. B-Eng. · 2024 · 287 · 11186810.1016/j.compositesb.2024.111868 ↗
37. Bai · npj 2D Mater. Appl · 2019 · 3 · 3210.1038/s41699-019-0115-5 ↗
38. Qi · Sci. Rep. · 2016 · 6 · 2831010.1038/srep28310 ↗
39. Wu · Nano-Micro Lett. · 2022 · 14 · 17110.1007/s40820-022-00906-5 ↗
40. Gupta · Carbon · 2019 · 152 · 15910.1016/j.carbon.2019.06.002 ↗
41. Zou · J. Mater. Sci. Teechnol. · 2026 · 242 · 22610.1016/j.jmst.2025.05.005 ↗
42. Qiu · Acta Mater. · 2025 · 288 · 12081710.1016/j.actamat.2025.120817 ↗
43. Chen · Chem. Eng. J. · 2023 · 452 · 13911010.1016/j.cej.2022.139110 ↗