Microstructure and performance of graded Ti(C, N)-based cermets modified by nitriding treatment during different sintering stages
Source abstract
Abstract
Abstract The effects of nitrided treatment during different sintering stages on the microstructure and mechanical properties of Ti(C, N) based cermets were studied. The results showed that: compared with the sample sintered in vacuum, the surface microstructures of these samples which nitrogen gas was introduced in entire stage, heating stage and final sintering stage changed obviously, the porosity greatly increased, and the mechanical properties decreased dramatically. However, the sample which nitrogen gas was introduced at cooling stage had formed an about 10 μm graded surface layer enriched in hard phase and deficient in binder phase, the surface microhardness improved significantly from 14.33 to 18.11 GPa, and the transverse rupture strength (TRS) was basically unchanged.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (26)
Show source-provided references
1. Extending the application areas for titanium carbonitride cermets10.1016/0263-4368(92)90081-C ↗
2. Titanium carbonitride-based cermets: processed and properties10.1016/0921-5093(93)90588-6 ↗
3. Ti(C, N) cermets-metallurgy and properties10.1016/0263-4368(95)00027-G ↗
4. TiMoCN-based cermets: high temperature deformation10.1016/S0263-4368(02)00091-4 ↗
5. Titanium-molybdenum carbonitride as light-weight and wear resistant monolithic material10.1016/S0043-1648(03)00513-1 ↗
6. Mechanism of plastic deformation of WC–Co and Ti(C, N)–WC–Co10.1016/j.ijrmhm.2005.04.009 ↗
7. Characterization of oxide scales to evaluate high temperature oxidation of Ti(C, N)-based cermets in static air10.1016/j.jallcom.2010.07.031 ↗
8. Early high temperature oxidation behaviour of Ti(C, N)-based cermets in air10.1016/j.corsci.2010.05.028 ↗
9. Functionally graded hardmetals10.1016/S0925-8388(02)00232-3 ↗
10. Gradient zones in WC–Ti(C, N)–Co-based cemented carbides: experimental study and computer simulations10.1016/S1359-6454(00)00029-X ↗
11. Influence of nitridation on surface microstructure and properties of graded cemented carbides with Co and Ni binders10.1016/j.surfcoat.2008.06.179 ↗
12. Fundamentals of liquid phase sintering for modern cermets and functionally graded cemented carbonitrides (FGCC)10.1016/S0263-4368(00)00041-X ↗
13. Microstructure development during sintering and heat-treatment of cemented carbides and cermets10.1016/S0254-0584(00)00441-7 ↗
14. Microstructure and performance of a cermet material heat-treated in nitrogen10.1016/S1359-6454(00)00212-3 ↗
15. Microstructure of the surface zone in a heat-treated cermet material10.1016/S0263-4368(98)00047-X ↗
16. Characterization of functionally gradient Ti(C, N)-based cermets fabricated by vacuum liquid phase sintering and nitriding treatment during cooling10.1016/j.ijrmhm.2014.05.003 ↗
17. The surface microstructure of TiC–(Ti, W)C–WC–Ni cermets sintered in a nitrogen atmosphere10.1016/j.msea.2010.08.006 ↗
18. Effect of cubic carbide composition and sintering parameters on the formation of wear resistant surfaces on cemented carbides10.1016/j.ijrmhm.2011.05.004 ↗
19. Effect of nitrogen content on microstructure and mechanical properties of Ti(C, N)-based cermets10.1016/j.jallcom.2013.03.138 ↗
20. Effects of TiC/TiN addition on the microstructure and mechanical properties of ultra-fine grade Ti(C, N)-Ni cermets10.1016/j.jeurceramsoc.2005.12.010 ↗
21. Effect of VC addition on sinterability and microstructure of ultrafine Ti(C, N)-based cermets in spark plasma sintering10.1016/j.jallcom.2007.05.091 ↗
22. Effect of carbon addition on the densification behavior, microstructure evolution and mechanical properties of Ti(C, N)-based cermets10.1016/j.ceramint.2015.12.097 ↗
23. Carbide/binder interfaces in Ti(CN)-(Ti, W)C/(Ti, W)(CN)-based cermets10.1016/j.jallcom.2015.10.121 ↗
24. Formation of core/rim structures in Ti (C, N)-WC-Ni cermets via a dissolution and precipitation process10.1111/j.1151-2916.2000.tb01415.x ↗
25. The effect of WC, Mo2C, TaC content on the microstructure and properties of ultra-fine TiC0.7N0.3 cermet10.1016/j.matdes.2006.03.005 ↗
26. Microstructure characterization and mechanical properties of Ti(C, N)-based cermets with AlN addition10.1016/j.ceramint.2014.12.068 ↗