Influence of tantalum on the microstructure and properties of Ti(C,N)-Ni cermets
Source abstract
Abstract
Abstract Several (Ti,Ta)(C,N) cermets were prepared from Ti(C,N) and Ta powder with or without Ni. For comparison, Ti(C,N) with Ni were also prepared. The mixed powders were sintered at 1400–1500 °C by FAST/SPS up to a density higher than 99% theoretical density. The addition of Ta delays densification of Ti(C,N)-Ni cermets due to the formation of intermetallic phases. During sintering, the Ta was incorporated into the Ti(C,N), forming solid solution, thus changing the core-rim structure of the Ti(C,N) cermets. On the other hand, the Ta additions result in grain refinement and improved hardness (from 16.1 GPa to 17.8 GPa) and fracture toughness (from 5.5 MPa.m 1/2 to 6.9 MPa.m 1/2 ).
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (19)
Show source-provided references
1. Transition Metal Solid-state Chemistry
2. Transition Metal Carbides, Nitrides, and Carbonitrides
3. Effect of carbides on the microstructure and properties of Ti(C, N)-based ceramics10.1111/j.1151-2916.1999.tb02216.x ↗
4. Microstructure of hot-pressed Ti(C, N)-based cermets10.1016/S0955-2219(02)00120-6 ↗
5. Ti(C, N) Cermets - Metallurgy and Properties10.1016/0263-4368(95)00027-G ↗
6. Titanium-carbonitride-based hard alloys for cutting tools10.1016/0025-5416(88)90724-0 ↗
7. Composition, microstructure, properties and cutting performances of cermets
8. Electro-discharge machining performance of TiCN-based cermets10.1016/j.ijrmhm.2006.07.001 ↗
9. Formation of Core/Rim Structures in Ti(C,N)-WC-Ni Cermets via a Dissolution and Precipitation Process10.1111/j.1151-2916.2000.tb01415.x ↗
10. Effect of carbides on the microstructure and properties of Ti(C, N)-based ceramics10.1111/j.1151-2916.1999.tb02216.x ↗
11. Effect of tantalum on the properties and structure of hard alloys based on titanium carbonitride10.1007/BF02675885 ↗
12. Microstructure and mechanical properties of a (Ti, W, Ta, Mo)(C, N)-(Co, Ni) type cermet
13. Effect of Ta on structure and mechanical properties of (Ti, Ta, W)(C, N)–Co cermets10.1016/S0263-4368(01)00042-7 ↗
14. Indentation fracture of WC-Co cermets10.1007/BF00555296 ↗
15. Storms · 1967 · 387
16. On the sintering of Ti(C, N)-30wt% Ni and TiNx-TiCy-30wt% Ni mixed powder compacts10.2497/jjspm.27.125 ↗
17. Preparation of (Ti, Ta)(C, N) by Mechanical Alloying10.1016/j.ijrmhm.2012.04.013 ↗
18. Singleton · Bull Alloy Phase Diagr · 1989 · 10 · 12110.1007/BF02881419 ↗
19. Naidoo · 2012