Effect of secondary carbides addition on the microstructure and mechanical properties of (Ti, W, Mo, V)(C, N)-based cermets
Source abstract
Abstract
Abstract (Ti, W, Mo, V)(C, N)-based cermets were prepared by mixing Mo2C, WC and TaC with ultrafine (Ti, W, Mo, V)(C, N) powders, and then processed via a conventional P/M technique. The effect of Mo2C, WC and TaC on the microstructure and mechanical properties of (Ti, W, Mo, V)(C, N)–8 wt.% Ni–7 wt.% Co systems was investigated. The Mo2C content was varied from 0 to 10 wt.% and additive WC or TaC was added at a level of 5 wt.% with Mo2C addition. The results show that the densification of (Ti, W, Mo, V)(C, N)–8 wt.% Ni–7 wt.% Co cermets was improved significantly by the addition of Mo2C. With the increase of Mo2C content, there is a coarsening tendency in the microstructure of (Ti, 20W, 15Mo, 0.2V)(C, N)–8Ni–7Co system, but the refinement for (Ti, 15W, 5Mo, 0.2V)(C, N)–8Ni–7Co. TaC addition decreases the density of (Ti, 15W, 5Mo, 0.2V)(C, N)–10Mo2C–8Ni–7Co cermet and thus weakens its bending strength. (Ti, 15W, 5Mo, 0.2V)(C, N)–10Mo2C–5WC–8Ni–7Co cermet has optimal mechanical properties: bending strength of 1999 MPa, hardness (Hv) of 1677 MPa and toughness of 9.95 MPa m1/2 respectively by adding WC, which is due to its ultrafine and weak core/rim structure.
Source: openaire · Quality: candidate unverified · Source record ↗
References (19)
Show source-provided references
1. Microstructure of hot-pressed Ti (C, N)-based cermets10.1016/S0955-2219(02)00120-6 ↗
2. High temperature mechanical behaviour of Ti(C, N)–Mo–Co cermets10.1016/S0263-4368(98)00033-X ↗
3. A study of cermets' wear behaviour10.1016/S0043-1648(96)07397-8 ↗
4. TiMoCN based cermets: Part II. Microstructure and room temperature mechanical properties10.1016/S0263-4368(03)00011-8 ↗
5. Cutting performances, mechanical property and microstructure of ultra-fine grade Ti(C, N)-based cermets10.1016/j.ijrmhm.2005.09.001 ↗
6. Titanium carbonitride-based cermets: processes and properties10.1016/0921-5093(93)90588-6 ↗
7. Effect of nanocrystalline binder on the microstructure and mechanical properties of ultrafine Ti(CN) cermets10.1016/S0921-5093(03)00506-9 ↗
8. Effect of ultra-fine powders on the microstructure of Ti(CN)–xWC–Ni cermets10.1016/j.actamat.2003.11.021 ↗
9. Analytical electron microscopy of the core/rim structure in titanium carbonitride cermets10.1016/0263-4368(92)90047-6 ↗
10. Toughened ultrafine (Ti, W)(CN)–Ni cermets10.1016/j.scriptamat.2004.09.017 ↗
11. Synthesis of (Ti, M1, M2)(CN)–Ni nanocrystalline powders10.1016/j.ijrmhm.2005.05.002 ↗
12. Ultrafine (Ti, M)(C, N)-based cermets with optimal mechanical properties10.1016/j.ijrmhm.2010.08.007 ↗
13. Study on phase evolution during reaction synthesis of ultrafine (Ti, W, Mo, V)(CN)–Ni composite powders10.1016/j.matchemphys.2009.07.021 ↗
14. Influence factors and microstructure evolution during preparation of nanocrystalline (Ti, W, Mo, V)(C, N)–Ni composite powders10.1016/j.ijrmhm.2009.05.010 ↗
15. Hardness to toughness relationship of fine-grained WC–Co hard metals10.1016/S0263-4368(98)00028-6 ↗
16. Some issues in Ti(CN)–WC–TaC cermets10.1016/0921-5093(95)10124-1 ↗
17. The Ti–Mo–C–N system: stability of (Ti, Mo)(C, N)1−x phase10.1016/0925-8388(95)01652-X ↗
18. Fundamentals of liquid phase sintering for modern cements and functionally graded carbonitrides (FGCC)10.1016/S0263-4368(00)00041-X ↗
19. Formation of core/rim structures in Ti(C, N)–WC–Ni cermets via a dissolution and precipitation process10.1111/j.1151-2916.2000.tb01415.x ↗