Oxidation of WC-TiC-TaC-Co hard materials at relatively low temperature
Source abstract
Abstract
Abstract The oxidation behavior of WC-TiC-TaC-Co hard materials was investigated at 300–900 °C. The results indicate that the oxidation reactions have been occurred as low as 350 °C. The mass gain is slight at 350–600 °C but increases significantly above 600 °C. The Co binder is preferential oxidized to CoWO4 due to WC solution. Besides, WC and (W, Ti, Ta)C are oxidized to WO3 and mixture of TiO2 and TaxOy, respectively, until 400 °C. Lots of defects on the surface of WO3 accelerate substrate oxidation. On the contrary, the compact layer of the mixture prevents the inner oxidation and significantly enhances the oxidation resistance. A gradual increase in oxidation temperature causes a rapid growth of Co oxide and also promotes the deterioration of WO3. In contrast, the compact layer of the solid solution shows higher thermal stability.
Source: openaire · Quality: candidate unverified · Source record ↗
References (38)
Show source-provided references
1. Materials science of cemented carbides—an overview10.1016/S0261-3069(01)00007-3 ↗
2. Effect of TaC on plastic deformation of WC-Co and Ti(C, N)-WC-Co10.1016/j.ijrmhm.2005.04.009 ↗
3. Characterisation of WC–Co with cubic carbide additions10.1016/j.ijrmhm.2008.11.007 ↗
4. Microstructure and mechanical properties of WC-10Co cemented carbide containing VC or (Ta, Nb) C and fracture toughness evaluation using different models10.1016/j.ijrmhm.2011.10.004 ↗
5. Properties of sintered WC-TiC-Co hard alloys containing tantalum carbide10.1007/BF00774339 ↗
6. Effect of TaC and TiC on the friction and dry sliding wear of WC-6wt.% Co cemented carbides against steel counterfaces10.1016/j.ijrmhm.2013.02.009 ↗
7. Microstructural and mechanical characterization of high energy ball milled and sintered WC-10wt% Co-xTaC nano powders10.1016/j.ijrmhm.2009.02.001 ↗
8. Sintering of WC-10% Co nano powders containing TaC and VC grain growth inhibitors10.1016/S1003-6326(11)60825-X ↗
9. A comparison of the microstructures of WC-VC-TiC-Co and WC-VC-Co cemented carbides10.1016/j.ijrmhm.2006.05.001 ↗
10. Effect of TiC whisker addition on properties of YG10F alloy10.1016/S1003-6326(07)60260-X ↗
11. Role of tantalum in the TiC-WC-TaC-Co hard metals. I. Effect of tantalum concentration on the composition and properties of the carbide and cobalt phases in the TiC-WC-TaC-Co hard metals10.1007/BF00794418 ↗
12. The role of tantalum in TiC-WC-TaC-Co sintered carbides. II. Influence of tantalum content on the structure and properties of TiC-WC-TaC-Co three-phase sintered carbides10.1007/BF00813963 ↗
13. Advances in powder technology
14. Radiation thermometry applied to temperature measurement in the cutting process10.1088/0957-0233/18/11/022 ↗
15. Oxidation behaviour of hard and binder phase modified WC-10Co cemented carbides10.1007/BF00729663 ↗
16. On the existence of a thermal contact resistance at the tool-chip interface in dry cutting of AISI 1045: formation mechanisms and influence on the cutting process10.1016/j.applthermaleng.2012.06.047 ↗
17. Temperature fields in a chip during high-speed orthogonal cutting—an experimental investigation10.1016/j.ijmachtools.2006.11.012 ↗
18. Oxidation-induced strength degradation of WC-Co hardmetals10.1016/S0263-4368(01)00033-6 ↗
19. Oxidation behavior of WC-Co10.1016/0921-5093(95)10145-4 ↗
20. Liquid phase sintering and oxidation resistance of WC-Ni-Co-Cr cemented carbides10.1016/j.ijrmhm.2010.02.010 ↗
21. Oxidation of WC-Co, WC-Ni and WC-Co-Ni hard metals in the temperature range 500–800°C10.1016/0263-4368(96)00009-1 ↗
22. Comparison of the oxidation behaviour of WC-Co and WC-Ni-Co-Cr cemented carbides10.1016/j.corsci.2011.05.006 ↗
23. Oxidation of tungsten carbide powders in air10.1016/j.ijrmhm.2013.05.001 ↗
24. Oxidation of ultrafine-cemented carbide prepared from nanocrystalline WC-10Co composite powder10.1016/j.ceramint.2007.07.029 ↗
25. Non-isothermal oxidation kinetics of WC-6Co cemented carbides in air10.1016/j.ijrmhm.2013.02.003 ↗
26. Influence of WC replacement by TiC and (Ta, Nb) C on the oxidation resistance of Co-based cemented carbides10.1016/j.ijrmhm.2008.12.009 ↗
27. Kinetics inversion in isothermal oxidation of uncoated WC-based carbides between 450 and 800°C10.1016/j.corsci.2008.12.022 ↗
28. Thermal oxidation behavior of WC-Co hard metal machining tool tip scraps10.1016/j.jmatprotec.2012.01.009 ↗
29. Early high temperature oxidation behaviour of Ti (C, N)-based cermets in air10.1016/j.corsci.2010.05.028 ↗
30. Enhanced oxidation resistance of Ti (C, N)-based cermets containing Ta10.1016/j.corsci.2014.03.007 ↗
31. Oxidation resistance and phase constituents in the brazing interface of WC-TiC-Co hard alloys10.1016/S0924-0136(02)00037-7 ↗
32. Experimental study of invariant equilibria in the Co-WC and Co-WC-Me (Me=Ti, Ta, Nb) systems10.1007/s11669-001-0073-3 ↗
33. Effect of cubic phase composition on gradient zone formation in cemented carbides10.1016/S0263-4368(01)00043-9 ↗
34. Nickel in hardmetals10.1016/0263-4368(92)90056-8 ↗
35. An ESCA study of the termination of the passivation of elemental metals10.1021/j100505a006 ↗
36. An X-ray photoelectron spectroscopic study of certain oxides
37. Low temperature oxidation behavior of reactively sputtered TiN by x-ray photoelectron spectroscopy and contact resistance measurements10.1116/1.573679 ↗
38. The role of aluminum additions in the oxidation and wear of a TaC: C low-friction coating10.1016/j.surfcoat.2009.03.008 ↗