Influence factors and microstructure evolution during preparation of nanocrystalline (Ti, W, Mo, V)(C, N)–Ni composite powders
Source abstract
Abstract
Abstract Nanocrystalline (Ti, W, Mo, V)(C, N)–Ni composite powders with crystalline size of about 35 nm were synthesized at 1300 °C from oxides by a simple and cost-effective route which combines traditional low-energy milling plus carbothermal reduction–nitridation techniques. Influence of main technological parameters was investigated by X-ray diffraction, and microstructure of the milled powders and reaction products was studied by scanning electron microscopy. The results show that the phase evolution of TiO 2 follows TiO 2 → Ti 3 O 5 → Ti(C, N), and (Ti, W, Mo, V)(C, N)–Ni composite powders with higher nitrogen content and smaller crystalline size can be produced by introducing high nitrogen pressure. By contrast with high nitrogen pressure, high synthesizing temperature and long isothermal time can contribute to dissolution of W, Mo and V atoms into Ti(C, N). In addition, synthesizing temperature has a significant effect on the microstructure evolution of (Ti, W, Mo, V)(C, N)–Ni composite powders.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (21)
Show source-provided references
1. Effect of carbon content on the microstructure and mechanical properties of (Ti, W, Ta, Mo)(C, N)–(Co, Ni) cermets10.1016/S0263-4368(98)00074-2 ↗
2. Tool life reliability of cermet inserts in milling tests10.1016/S0924-0136(97)00437-8 ↗
3. Ti(C, N) cermets–metallurgy and properties10.1016/0263-4368(95)00027-G ↗
4. Preparation of Ti(C, N)–WC–TaC solid solution by mechanical alloying technique10.1016/0924-0136(95)91416-Z ↗
5. Reaction sequences and influence factors during preparation of Ti(C, N) powders10.1016/j.jallcom.2006.03.088 ↗
6. Effect of Mo addition on the microstructure and mechanical properties of ultra-fine grade TiC–TiN–WC–Mo2C–Co cermets10.1016/j.ijrmhm.2007.05.005 ↗
7. Effect of WC and group IV carbides on the cutting performance of Ti(C, N) cermet tools10.1016/j.ijmachtools.2003.10.023 ↗
8. Xiong J, Guo Z, Shen B, Cao D. The effect of WC, Mo2C, TaC content on the microstructure and properties of ultra-fine TiC0.7N0.3 cermets. Mater Des 2007;28(5):1689.10.1016/j.matdes.2006.03.005 ↗
9. Gee MG, Reece MJ, Roebuck BJ. High resolution electron microscopy of Ti(C,N) cermets. J Hard Mater 1992;3:119.
10. Jung J, Kang S. Effect of nano-size powders on the microstructure of Ti(C,N)–xWC–Ni Cermets. J Am Ceram Soc 2007;90:2178.10.1111/j.1551-2916.2007.01654.x ↗
11. Mechanochemical synthesis of nanocomposite powder for ultrafine (Ti, Mo)C–Ni cermet without core–rim structure10.1016/j.ijrmhm.2004.06.004 ↗
12. Toughened ultrafine (Ti,W)(CN)–Ni cermets10.1016/j.scriptamat.2004.09.017 ↗
13. Kang S, Jung J. Sintered (Ti, W) C carbides. Scr Mater 2007;56:561.10.1016/j.scriptamat.2006.12.026 ↗
14. Synthesis of (Ti, M1, M2)(CN)–Ni nanocrystalline powders10.1016/j.ijrmhm.2005.05.002 ↗
15. Jha A, Yoon SJ. Formation of titanium carbonitride phases via the reduction of TiO2 with carbon in the presence of nitrogen. J Mater Sci 1999;34:307.10.1023/A:1004457622751 ↗
16. Preparation of ultrafine WC–Co composite powder by in situ reduction and carbonization reactions10.1016/j.ijrmhm.2008.05.001 ↗
17. Kinetics and mechanism of carbothermic reduction of MoO3 to Mo2C10.1016/S0925-8388(97)00212-0 ↗
18. Synthesis of vanadium carbide nanopowders by thermal processing and their characterization10.1016/j.powtec.2007.06.011 ↗
19. Matyi RJ, Schwartz LH, Butt JB. Particle size, particle size distribution and related measurements of supported metal catalysts, Catal Rev Sci Eng 1987;29:41.10.1080/01614948708067547 ↗
20. Carbothermal synthesis of titanium nitride, Part II. The reaction sequence10.1007/BF00541555 ↗
21. On the quantitative analysis of secondary carbide and carbon in (Ti1−xMx)C solid solutions via XRD measurements10.1016/j.ijrmhm.2007.10.001 ↗