Effect of particle proximity on changing of diffusion mechanism of 3Y-TZP nanoparticles at the initial stage of sintering
Source abstract
Abstract
Abstract In order to evaluate the effect of interparticle contact area on the sintering behavior of 3Y-TZP nanopowder, the shrinkage of powder samples, compacted at different pressures were measured under constant rates of heating. Compaction of zirconia NPs at different pressures allowed to increase the contact area between particles and determined the critical parameters when the volume diffusion mechanism is changing on the grain boundary diffusion. It was found that the volume diffusion mechanism is the dominant densification mechanism at the initial stage of sintering for 3Y-TZP nanopowders at a low relative density of green ceramics, when there are few contacting particles, and the grain boundary diffusion mechanism cannot be realized due to the large diffusion path. The domination of the grain boundary diffusion mechanism during initial stage of sintering of 3Y-TZP nanoparticles was detected in case the contact area between particles increased up to 56%.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (36)
Show source-provided references
1. Synthesis and characterization of zirconia toughened alumina ceramics prepared by co-precipitation method10.1016/j.ceramint.2019.05.121 ↗
2. Microstructure–toughness–wear relationship of tetragonal zirconia ceramics10.1016/S0955-2219(03)00355-8 ↗
3. Zirconia in biomedical applications10.1080/17434440.2016.1230017 ↗
4. Oxygen sensors: materials, methods, designs and applications10.1023/A:1026370729205 ↗
5. A review on recent status and challenges of yttria stabilized zirconia modification to lowering the temperature of solid oxide fuel cells operation10.1002/er.4944 ↗
6. Thin films by consolidation and sintering of nanocrystalline powders10.1016/S0955-2219(96)00095-7 ↗
7. Film formation and sintering of colloidal monoclinic zirconia10.1016/S0022-3093(05)80667-2 ↗
8. Colloidal consolidation of ceramic nanoparticles by pressure filtration10.1111/j.1551-2916.2006.01046.x ↗
9. Pressure consolidation of amorphous ZrO2–Al2O3 by plastic deformation of powder particles10.1016/S1359-6454(02)00058-7 ↗
10. Study of the densification of a nanostructured composite powder part 1: effect of compaction pressure and reinforcement addition10.1016/j.msea.2007.09.034 ↗
11. Compaction and Pressureless sintering of zirconia nanoparticles10.1111/j.1551-2916.2007.01781.x ↗
12. Atomic mechanisms of mass transport in ceramic nuclear fuel materials10.1039/ft9908601243 ↗
13. Sintering kinetics at constant rates of heating: effect of Al2O3 on the initial sintering stage of fine zirconia powder10.1111/j.1551-2916.2005.00620.x ↗
14. Effect of alumina addition on initial sintering of cubic ZrO2 (8YSZ)10.1016/j.ceramint.2009.11.003 ↗
15. Sintering behavior and mechanisms of NiO-doped 8 Mol% yttria stabilized zirconia10.1016/j.jeurceramsoc.2011.03.025 ↗
16. Initial sintering with constant rates of heating10.1111/j.1151-2916.1970.tb12036.x ↗
17. Estimate of the activation energies for boundary diffusion from rate-controlled sintering of pure alumina, and alumina doped with zirconia or Titania10.1111/j.1151-2916.1990.tb05175.x ↗
18. Bulk zirconia nanoceramics prepared by cold isostatic pressing and pressureless sintering
19. Sintering kinetics at constant rates of heating: effect of alumina on the initial sintering stage of Yttria-stabilized cubic zirconia powder10.2109/jcersj.114.763 ↗
20. Sintering mechanism of fine zirconia powders with alumina added by powder mixing and chemical processes10.1007/s10853-008-2493-5 ↗
21. Sintering kinetics at constant rates of heating: mechanism of silica-enhanced sintering of fine zirconia powder10.1111/j.1551-2916.2008.02516.x ↗
22. Calibration curve for quantitative analysis of the monoclinic-tetragonal ZrO2 system by X-ray diffraction
23. Influence of obtaining conditions on kinetics of the initial sintering stage of zirconia nanopowders10.1186/s11671-016-1452-3 ↗
24. Mechanisms of room temperature metastable tetragonal phase stabilisation in zirconia10.1179/174328005X14267 ↗
25. A martensitic phase transition in nanocrystalline 3Y-TZP powders under hydrostatic pressure conditions10.1080/01411594.2012.749988 ↗
26. Effect of mechanical activation on sintering behavior of tetragonal zirconia nanopowders10.1016/j.ceramint.2020.02.193 ↗
27. Influence of Al2O3 addition on sintering and grain growth behavior of 8 Mol% Y2O3-stabilised cubic zirconia (c-ZrO2)10.1016/j.ceramint.2004.01.004 ↗
28. Fabrication of nano Y-TZP materials by superhigh pressure compaction10.1016/S0955-2219(00)00182-5 ↗
29. Powder preparation and compaction behavior of fine-grained Y-TZP10.1007/BF00575369 ↗
30. Impact of pressure in static and dynamic pressing of zirconia ultradisperse powders on compact density and compaction efficiency during sintering10.1016/j.ceramint.2017.09.042 ↗
31. Effect of compaction pressure on the properties of dental machinable zirconia ceramic
32. A first report on sintering diagrams10.1016/0001-6160(74)90167-9 ↗
33. A second report on sintering diagrams10.1016/0001-6160(81)90154-1 ↗
34. Mechanism of alumina-enhanced sintering of fine zirconia powder: influence of alumina concentration on the initial stage sintering10.1111/j.1551-2916.2008.02350.x ↗
35. Initial sintering kinetics of lithium metatitanate at constant rates of heating
36. Apparent activation energy for densification of α-Al2O3 powder at constant heating-rate sintering10.1007/s12034-008-0144-8 ↗