Effect of Al additions on the oxidation behavior of Laves phase NbCr2 alloys at 1373K and 1473K
Source abstract
Abstract
Abstract Effect of Al on oxidation behavior of the Laves phase NbCr 2 based alloys, which are fabricated by hot pressing and mechanical alloying, has been investigated at 1373 K and 1473 K, respectively. The oxidation resistance of the alloyed NbCr 2 alloys increases with Al concentration increasing from 2 to 12 at.%. However, the alloyed NbCr 2 has higher oxidation rate than unalloyed NbCr 2 at 1473 K. When they are oxidized at 1373 K, NbCr 2 –12 at.% Al alloy shows lower oxidation rate than unalloyed NbCr 2 . The mechanism of oxidation has been analyzed using thermodynamic and kinetic.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (14)
Show source-provided references
1. Effects of alloy additions on the microstructure and properties of Cr2Nb alloys10.1016/0921-5093(96)10197-0 ↗
2. Site preference of early transition metal elements in C15 NbCr210.1016/j.actamat.2006.10.020 ↗
3. Point defects in binary Laves phase alloys10.1016/S1359-6454(99)00090-7 ↗
4. Point defects in binary NbCr2 Laves-phase alloys10.1016/S1359-6462(98)00263-2 ↗
5. High temperature mechanical properties of C15 Laves phase Cr2Nb intermetallics10.1016/0921-5093(94)03319-6 ↗
6. Oxidation resistance and mechanical properties of Laves phase reinforced Cr in situ composites10.1016/S0966-9795(00)00046-7 ↗
7. Water vapor and oxygen/sulfur-impurity effects on oxidation and nitridation in single- and two-phase Cr–Nb alloys10.1023/A:1020154620928 ↗
8. Study on scaling of mechanically alloyed and hot pressed NbCr2 Laves phase at 1200°C in air [J]10.1016/j.ijrmhm.2007.04.005 ↗
9. The intermediate and high-temperature oxidation behaviour of (Mo,X)Si2 (X=W, Ta) intermetallic alloys10.1016/S0966-9795(96)00074-X ↗
10. The role of microstructure on pesting during oxidation of MoSi2 and Mo(Si,Al)2 at 773K10.1007/BF01668515 ↗
11. Thermal properties of MoSi2 with minor aluminum substitutions10.1016/j.intermet.2006.03.013 ↗
12. The oxidation of metals at high temperature
13. Oxidation mechanisms for nickel–aluminum alloys at temperatures between 900 and 1300°C
14. Theoretical analysis of the diffusion process determining the oxidation rate of alloys10.1149/1.2779605 ↗