Al2O3/Mo composite and its tribological behavior against AISI201 stainless steel at elevated temperatures
Source abstract
Abstract
Abstract Al 2 O 3 -reinforced molybdenum (Mo) composites were successfully prepared by powder metallurgy to improve the wear resistance of Mo components at high temperature. The reinforced Al 2 O 3 particles are uniformly distributed in the Mo matrix; thus, the Al 2 O 3 /Mo composite is harder than monolithic Mo. The friction coefficients of both monolithic Mo and the Al 2 O 3 /Mo composite decrease by 37% and 42%, respectively, at 700 °C compared with those at room temperature (self-lubricating phenomenon). This phenomenon is attributed to the formation of very soft MoO 3 and FeMoO 4 metal oxides on the friction surface at high temperature. The Al 2 O 3 /Mo composite has better wear resistance than monolithic Mo at both room temperature and at 700 °C. The notable resistance of the composite particularly at 700 °C can be attributed to its increased hardness and the soft tribofilm forming on the worn surface.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (25)
Show source-provided references
1. Densification and grain growth during isothermal sintering of Mo and mechanically alloyed Mo-TZM10.1016/j.actamat.2009.05.013 ↗
2. Investigation of solid solution hardening in molybdenum alloys10.1016/j.ijrmhm.2010.05.010 ↗
3. Tietz · 1965 · 18
4. The hotter the engine, the better10.1126/science.1179327 ↗
5. Joining of molybdenum and its application10.1016/j.ijrmhm.2010.06.008 ↗
6. A review of refractory metal alloys and mechanically alloyed-oxide dispersion strengthened steels for space nuclear power systems10.1016/j.jnucmat.2004.10.118 ↗
7. A study of hot deformation behavior and microstructural characterization of Mo-TZM alloy10.1016/j.jnucmat.2008.12.049 ↗
8. Preparation of nanostructured high-temperature TZM alloy by mechanical alloying and sintering10.1016/j.ijrmhm.2010.09.003 ↗
9. Studies on the development of protective coating on TZM alloy and its subsequent characterization10.1016/j.jmatprotec.2007.12.075 ↗
10. Microstructure and strengthening mechanisms of molybdenum alloy wires doped with lanthanum oxide particles10.1016/j.ijrmhm.2008.06.007 ↗
11. Ichinose · 1987
12. Lubrication behavior of Y-TZP/Al2O3/Mo nanocomposites at high temperature10.1016/j.wear.2010.01.009 ↗
13. Characterization of Al2O3 composites with Mo particulates10.1016/S0965-9773(98)00135-4 ↗
14. Fabrication and mechanical behaviour of A12O3/Mo nanocomposites10.1007/BF00356661 ↗
15. Sliding wear of Cr–A12O3–ZrO2 and Mo–A12O3–ZrO2 composites10.1016/j.jeurceramsoc.2004.03.013 ↗
16. Wear behaviour of Al2O3–Mo and Al2O3–Nb composites10.1016/j.wear.2007.01.010 ↗
17. Investigation on alumina/molybdenum particulate composites10.1106/2PCG-JEFH-5A1E-1J7H ↗
18. Effects of friction laws on metal forming processes10.1016/j.triboint.2008.06.012 ↗
19. Microstructural and mechanical properties of nanocrystalline spinel and related composites10.1016/S0272-8842(01)00071-2 ↗
20. Grain size effect on the mechanical properties of transparent spinel ceramics10.1016/j.jeurceramsoc.2012.09.024 ↗
21. Recrystallization induced plasticity in austenite and ferrite10.1016/j.msea.2012.02.022 ↗
22. Synthesis and characterization of a high-temperature oxide lubricant10.1007/BF00366870 ↗
23. Consideration of lubricants for temperature above 1000F
24. Effects of the solute concentration on the deformation characteristics of Fe–Mo solid solutions in the power-law creep regime at 1100K10.1016/0921-5093(88)90047-0 ↗
25. Prediction of mechanical properties of Fe–Cr–Mo sintered steel in relationship with microstructure10.1016/j.matdes.2011.10.011 ↗