Evaluation of two surfacing methods on black spruce wood in relation to gluing performance
Source abstract
Abstract
Surface quality and gluing performance of black spruce samples prepared by peripheral straight-edge knife planing and sanding were studied. Four wavelengths (1.5, 1.9, 3.1, and 6.5 mm) and four rake angles (15°, 20°, 25°, and 30°) were tested for peripheral planing. Three feed speeds (4, 10.5, and 17 m/min) and three grit size sandpapers (80, 100, and 120) were studied for sanding. The resulting surfaces were glued with an isocyanate adhesive and tested to evaluate their gluing performance (shear strength and percent wood failure). Results revealed that planing with a rake angle of 20° and wavelengths of up to 3.1 mm produced wood surfaces with adequate glueline shear strength. Sanding with 80-grit sandpaper produced the best glueline shear strength, regardless of feed speed. After accelerated aging, the loss of gluing performance was lower for the sanded samples compared with that of planed samples. In general, sanding process produced better wood surfaces for bonding with the adhesive studied.
Source: europepmc · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Wood Treatment and Properties · Material Properties and Processing · Natural Fiber Reinforced Composites
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (39)
Show source-provided references
1. Follrich J, Vay O, Veigel S, Müller U (2010) Bond strength of end-grain joints and its dependence on surface roughness and adhesive spread. J Wood Sci 56:429–43410.1007/s10086-010-1118-1 ↗
2. Shida S, Hiziroglu S (2010) Evaluation of shear strength of Japanese wood species as function of surface roughness. For Prod J 60:400–404
3. Hernández RE, de Moura LF (2002) Effects of knife jointing and wear on the planed surface quality of northern red oak wood. Wood Fiber Sci 34:540–552
4. Ebewele RO, River BH, Koutsky JA (1980) Tapered double cantilever beam fracture tests of phenolic-wood adhesive joints. Part II. Effects of surface roughness, the nature of surface roughness, and surface aging on joint fracture energy. Wood Fiber 12:40–65
5. Koch P (1985) Utilization of hardwoods growing on southern pine sites, volume 2—processing. Agriculture Handbook. USDA For Serv For Prod Lab. Madison, WI10.5962/bhl.title.30555 ↗
6. Carrano AL, Taylor JB, Lemaster R (2004) Machining-induced subsurface damage of wood. For Prod J 54:85–91
7. Hernández RE, Bustos C, Fortin Y, Beaulieu J (2001) Wood machining properties of white spruce from plantation forests. For Prod J 51:82–88
8. Hernández RE, Constantineau S, Fortin Y (2011) Wood machining properties of poplar hybrid clones from different sites following various drying treatments. Wood Fiber Sci 43:394–411
9. Malkoçoğlu A (2007) Machining properties and surface roughness of various wood species planed in different conditions. Build Environ 42:2562–256710.1016/j.buildenv.2006.08.028 ↗
10. Hernández RE, Naderi N (2001) Effect of knife jointing on the gluing properties of wood. Wood Fiber Sci 33:292–301
11. Hernández RE, Rojas G (2002) Effects of knife jointing and wear on the planed surface quality of sugar maple wood. Wood Fiber Sci 34:293–305
12. Iskra P, Hernández RE (2009) The influence of cutting parameters on the surface quality of routed paper birch and surface roughness prediction modeling. Wood Fiber Sci 41:28–37
13. Taylor JB, Carrano AL, Lemaster RL (1999) Quantification of process parameters in a wood sanding operation. For Prod J 49:41–46
14. Saloni DE, Lemaster RL, Jackson SD (2005) Abrasive machining process characterization on material removal rate, final surface texture, and power consumption for wood. For Prod J 55:35–41
15. de Moura LF, Hernández RE (2006) Effects of abrasive mineral, grit size and feed speed on the quality of sanded surfaces of sugar maple wood. Wood Sci Technol 40:517–53010.1007/s00226-006-0070-0 ↗
16. Carrano AL, Taylor JB, Lemaster R (2002) Parametric characterization of peripheral sanding. For Prod J 52:44–50
17. Sinn G, Gindl M, Reiterer A, Stanzl-Tschegg S (2004) Changes in the surface properties of wood due to sanding. Holzforschung 58:246–25110.1515/HF.2004.038 ↗
18. Jokerst RW, Stewart HA (1976) Knife-versus abrasive-planed wood: quality of adhesive bonds. Wood Fiber 8:107–113
19. Caster D, Kutscha N, Leick G (1985) Gluability of sanded lumber. For Prod J 35:45–52
20. de Meijer M, Thurich K, Militz H (1998) Comparative study on penetration characteristics of modern wood coatings. Wood Sci Technol 32:347–36510.1007/BF00702791 ↗
21. Cool J, Hernández RE (2011) Evaluation of four surfacing methods on black spruce wood in relation to Poly(vinyl acetate) gluing performance. Wood Fiber Sci 43:194–205
22. Kilic M, Hiziroglu S, Burdurlu E (2006) Effect of machining on surface roughness of wood. Build Environ 41:1074–107810.1016/j.buildenv.2005.05.008 ↗
23. Hernández RE, Cool J (2008) Evaluation of three surfacing methods on paper birch wood in relation to water- and solvent-borne coating performance. Wood Fiber Sci 40:459–469
24. Richter K, Feist WC, Knaebe MT (1995) The effect of surface roughness on the performance of finishes. Part 1. Roughness characterization and stain performance. For Prod J 45:91–97
25. Lihra T, Ganev S (1999) Machining properties of eastern species and composite panels. Forintek Canada Corp., Project No. 2306, Quebec, Canada, p 62
26. ASTM D 1666 (2004) Standard methods for conducting machining tests of wood and wood base materials. American Society for Testing and Materials, Philadelphia
27. Cool J, Hernández RE (2012) Characteristics of peripheral-planed black spruce wood surfaces in relation to water-borne coating performance. For Prod J 62:124–133
28. ISO 4287 (1997) Geometrical product specifications (GPS). Surface texture. Profile method. Terms. Definitions and surface texture parameters. International Standards Organization. British Standards Institute, London
29. ISO 13565-2 (1996) Geometrical product specifications (GPS). Surface texture. Profile method: surfaces having stratified functional properties. Part 2: height characterization using the linear material ratio curve. International Standards Organization. British Standards Institute, London
30. ISO/DTS 16610-31 (2007) Geometrical product specifications (GPS)—filtration. Part 31: robust profile filters. Gaussian regression filters. In draft. International Standards Organization
31. ASTM D 3434 (2000) Standard test method for multiple-cycle accelerated aging test (automatic boil test) for exterior wet use wood adhesives. American Society for Testing and Materials, West Conshohocken, PA
32. ASTM D 905 (2003) Strength properties of adhesive bonds in shear by compression loading. American Society for Testing and Materials, Philadelphia
33. Marra AA (1992) Bond performance: testing and evaluation. In Technology of wood bonding principles in practice. Van Nostrand Reinhold, New York, pp 377–410
34. SAS Institute (2007) SAS/Stat user’s guide, release 9.2 edn. SAS Institute Inc., Cary
35. Cool J, Hernández RE (2011) Improving the sanding process of black spruce wood for surface quality and water-based coating adhesion. For Prod J 61(5):372–380
36. Tabachnick BG, Fidell LS (2007) Using multivariate statistics, 5th edn. Pearson, Allyn and Bacon, Boston, p 980
37. Cool J, Hernández RE (2011) Performance of three alternative surfacing processes on black spruce wood and their effects on water-based coating adhesion. Wood Fiber Sci 43:365–378
38. Iskra P, Hernández RE (2012) Analysis of cutting forces in straight-knife peripheral cutting of wood. Wood Fiber Sci 44:134–144
39. Hernández RE (1994) Effect of two wood surfacing methods on the gluing properties of sugar maple and white spruce. For Prod J 44:63–66