Improving the Degradation Resistance and Surface Biomineralization Ability of Calcium Phosphate Coatings on a Biodegradable Magnesium Alloy via a Sol-Gel Spin Coating Method
Source abstract
Abstract
Bioactive calcium phosphate (CaP) coatings have been applied on biodegradable magnesium (Mg) and its alloys to provide a suitable degradation rate for orthopedic applications. However, the porous CaP coatings formed in the aqueous solution owns poor degradation resistance and thus short in vivo valid life. This paper reports a sol-gel spin coating method to prepare hydroxyapatite (HA, Ca 10 (PO 4 ) 6 (OH) 2 ) and fluorine doping HA sealing coatings on a porous CaP coating. The effects of fluorine content on the degradation and biomineralization behaviors of the composite coatings were studied. It reveals that the homogeneous and stable sol-gel coating, especially the fluorapatite coating could significantly improve the degradation resistance and surface biomineralization ability of the porous CaP coating on the Mg alloy.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Magnesium Alloys: Properties and Applications · Bone Tissue Engineering Materials · Layered Double Hydroxides Synthesis and Applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (44)
Show source-provided references
1. 10.1016/j.mser.2014.01.00110.1016/j.mser.2014.01.001 ↗
2. 10.1038/nm.416210.1038/nm.4162 ↗
3. 10.1016/j.biomaterials.2005.10.00310.1016/j.biomaterials.2005.10.003 ↗
4. 10.1016/j.biomaterials.2004.09.04910.1016/j.biomaterials.2004.09.049 ↗
5. 10.1073/pnas.151823811310.1073/pnas.1518238113 ↗
6. 10.1016/j.cossms.2009.04.00110.1016/j.cossms.2009.04.001 ↗
7. 10.1016/j.jmbbm.2017.08.03510.1016/j.jmbbm.2017.08.035 ↗
8. 10.1039/C4TB01934B10.1039/C4TB01934B ↗
9. 10.1016/j.actbio.2012.04.01210.1016/j.actbio.2012.04.012 ↗
10. 10.1016/j.actbio.2014.02.02610.1016/j.actbio.2014.02.026 ↗
11. 10.1016/j.actbio.2011.10.01610.1016/j.actbio.2011.10.016 ↗
12. 10.1016/j.actbio.2013.10.03610.1016/j.actbio.2013.10.036 ↗
13. 10.1016/j.mser.2009.05.00110.1016/j.mser.2009.05.001 ↗
14. 10.1016/S1003-6326(13)62731-410.1016/S1003-6326(13)62731-4 ↗
15. 10.1021/acsbiomaterials.5b0034310.1021/acsbiomaterials.5b00343 ↗
16. 10.1016/j.corsci.2011.03.00810.1016/j.corsci.2011.03.008 ↗
17. 10.1021/acsbiomaterials.6b0001310.1021/acsbiomaterials.6b00013 ↗
18. 10.1016/j.msec.2013.08.00810.1016/j.msec.2013.08.008 ↗
19. 10.1016/j.apsusc.2011.04.08710.1016/j.apsusc.2011.04.087 ↗
20. 10.1149/2.0801609jes10.1149/2.0801609jes ↗
21. 10.1016/j.surfcoat.2016.08.06510.1016/j.surfcoat.2016.08.065 ↗
22. 10.1039/C5RA10315K10.1039/C5RA10315K ↗
23. 10.1016/j.corsci.2013.04.01910.1016/j.corsci.2013.04.019 ↗
24. 10.1016/j.apsusc.2013.06.01510.1016/j.apsusc.2013.06.015 ↗
25. 10.1002/jbm.b.3093210.1002/jbm.b.30932 ↗
26. 10.1016/S0142-9612(03)00607-010.1016/S0142-9612(03)00607-0 ↗
27. 10.1016/j.mseb.2011.08.00710.1016/j.mseb.2011.08.007 ↗
28. 10.1179/1743284712Y.000000018010.1179/1743284712Y.0000000180 ↗
29. 10.1016/j.msec.2013.05.01410.1016/j.msec.2013.05.014 ↗
30. 10.1016/j.jmbbm.2015.11.03110.1016/j.jmbbm.2015.11.031 ↗
31. 10.1016/j.dental.2012.11.00810.1016/j.dental.2012.11.008 ↗
32. 10.1016/j.biomaterials.2010.04.02310.1016/j.biomaterials.2010.04.023 ↗
33. 10.1016/j.biomaterials.2004.10.01910.1016/j.biomaterials.2004.10.019 ↗
34. 10.1149/2.036311jes10.1149/2.036311jes ↗
35. Su · Int. J. Electrochem. Sc. · 2012 · 7 · 1149710.1016/S1452-3981(23)16961-6 ↗
36. 10.1016/j.corsci.2007.01.00110.1016/j.corsci.2007.01.001 ↗
37. 10.1016/j.mseb.2011.08.00710.1016/j.mseb.2011.08.007 ↗
38. 10.1016/0368-2048(80)80022-310.1016/0368-2048(80)80022-3 ↗
39. 10.1016/j.dental.2013.02.00210.1016/j.dental.2013.02.002 ↗
40. 10.1016/j.corsci.2014.04.00810.1016/j.corsci.2014.04.008 ↗
41. 10.1016/j.electacta.2005.08.02610.1016/j.electacta.2005.08.026 ↗
42. 10.1016/j.corsci.2006.10.01610.1016/j.corsci.2006.10.016 ↗
43. 10.1149/2.091205jes10.1149/2.091205jes ↗
44. 10.5006/1.331610610.5006/1.3316106 ↗