The Potential for the Creation of a High Areal Capacity Lithium-Sulfur Battery Using a Metal Foam Current Collector

A high areal capacity lithium-sulfur battery making use of mass produced aluminum metal foam as a current collector was investigated. A sulfur/Ketjenblack (KB) composite was filled and deposited into the aluminum foam current collector via a predetermined filling procedure, resulting in high sulfur loading. The value for this loading was found to be 17.7 mg sulfur/cm 2 by using carboxymethyl cellulose and styrene butadiene rubber (CMC + SBR) as a binder. An operating single-layer pouch-type cell with an S/KB-CMC+SBR on Al foam cathode was created as a result of this synthesis and found to possess an unprecedentedly high areal capacity of 21.9 mAh/cm 2 . On the basis of the achieved areal capacity, the energy density of a theoretical lithium-sulfur battery was estimated with the assumption of an electrolyte/sulfur ratio of 2.7 μL/mg. This was calculated upon 100% of the pore volume in the S/KB-CMC + SBR on Al foam cathodes and polyolefin separator, along with the inclusion of the weights of the tabs for the current lead and pouch film packaging in the case of a seven-layer pouch-type battery. With this calculation, it was determined that the creation of a lithium-sulfur battery with an energy density of greater than 200 Wh/kg is plausible.