Enhancement of the Corrosion Protection Properties of a Hybrid Sol-Gel Based Silane Film through Impregnation of Functionalized Graphene Oxide Nanosheets
Source abstract
Abstract
This study focused on the effect of graphene oxide (GO) nanofillers on the sol-gel based silane coating corrosion protection performance enhancement. A mixture of tethyltriethoxysilane (MTES) and tetraethylorthosilicate (TEOS) silane precursors was used for preparation of composite matrix. The GO nanosheets were functionalized by 3-aminopropyl triethoxysilane (APTES, AGO nanofillers) and 3-(triethoxysilyl)propyl isocyanate (TEPI, IGO nanofillers) silanes to improve their compatibility with the silane matrix. The corrosion protection performance of the coatings was investigated by salt spray and electrochemical impedance spectroscopy (EIS). It was found that AGO and IGO nanofillers improved the corrosion resistance of the coating due to better compatibility with silane matrix and excellent barrier properties. Also with increasing the amount of nanofiller from 0.2 to 0.4 g/L, the corrosion protection performance of the nanocomposite coatings decreased.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Corrosion Behavior and Inhibition · ZnO doping and properties · Conducting polymers and applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (60)
Show source-provided references
1. 10.1016/j.electacta.2013.05.04110.1016/j.electacta.2013.05.041 ↗
2. Narayanan · Reviews in Advanced Materials Science · 2005 · 9 · 130
3. Majdi M. R. Danaee I. Afghahi S. S. S. , Materials Research, 0 (2017).
4. 10.1016/j.corsci.2015.05.05610.1016/j.corsci.2015.05.056 ↗
5. 10.1016/j.electacta.2015.10.16710.1016/j.electacta.2015.10.167 ↗
6. 10.1007/s10800-008-9517-310.1007/s10800-008-9517-3 ↗
7. 10.1016/j.corsci.2014.10.03510.1016/j.corsci.2014.10.035 ↗
8. 10.1016/j.corsci.2011.10.03110.1016/j.corsci.2011.10.031 ↗
9. 10.1016/j.porgcoat.2015.06.00310.1016/j.porgcoat.2015.06.003 ↗
10. 10.1039/C5RA24823J10.1039/C5RA24823J ↗
11. 10.1016/j.corsci.2008.10.00510.1016/j.corsci.2008.10.005 ↗
12. 10.1016/j.surfcoat.2015.01.05010.1016/j.surfcoat.2015.01.050 ↗
13. 10.1016/j.porgcoat.2016.11.01610.1016/j.porgcoat.2016.11.016 ↗
14. 10.1016/j.carbon.2015.05.09410.1016/j.carbon.2015.05.094 ↗
15. 10.1016/j.corsci.2015.02.02810.1016/j.corsci.2015.02.028 ↗
16. 10.1016/j.ijadhadh.2015.09.00710.1016/j.ijadhadh.2015.09.007 ↗
17. 10.1016/j.jiec.2014.09.03610.1016/j.jiec.2014.09.036 ↗
18. 10.1016/j.surfcoat.2013.10.01410.1016/j.surfcoat.2013.10.014 ↗
19. 10.1007/s11998-010-9300-310.1007/s11998-010-9300-3 ↗
20. 10.1016/S1002-0721(08)60212-410.1016/S1002-0721(08)60212-4 ↗
21. 10.1016/j.clay.2015.05.00910.1016/j.clay.2015.05.009 ↗
22. 10.1016/j.porgcoat.2016.07.00810.1016/j.porgcoat.2016.07.008 ↗
23. 10.1007/s11998-011-9391-510.1007/s11998-011-9391-5 ↗
24. 10.1002/sia.524910.1002/sia.5249 ↗
25. 10.1016/j.porgcoat.2015.08.00910.1016/j.porgcoat.2015.08.009 ↗
26. 10.1016/j.porgcoat.2003.07.00810.1016/j.porgcoat.2003.07.008 ↗
27. 10.1016/j.surfcoat.2010.05.02710.1016/j.surfcoat.2010.05.027 ↗
28. 10.1016/j.corsci.2008.01.01810.1016/j.corsci.2008.01.018 ↗
29. 10.1007/s10971-011-2536-210.1007/s10971-011-2536-2 ↗
30. 10.1016/j.surfcoat.2013.03.00510.1016/j.surfcoat.2013.03.005 ↗
31. 10.1021/cm504309910.1021/cm5043099 ↗
32. 10.1149/2.1051613jes10.1149/2.1051613jes ↗
33. 10.1016/j.carbon.2009.01.00910.1016/j.carbon.2009.01.009 ↗
34. 10.1039/C3CS60303B10.1039/C3CS60303B ↗
35. 10.1016/j.cej.2016.07.03710.1016/j.cej.2016.07.037 ↗
36. 10.1016/j.corsci.2017.04.01110.1016/j.corsci.2017.04.011 ↗
37. 10.1016/j.corsci.2015.11.03310.1016/j.corsci.2015.11.033 ↗
38. 10.1016/j.polymer.2013.06.02710.1016/j.polymer.2013.06.027 ↗
39. 10.1002/adma.20080027910.1002/adma.200800279 ↗
40. 10.1016/j.carbon.2006.06.00410.1016/j.carbon.2006.06.004 ↗
41. 10.1016/j.compositesa.2015.04.01310.1016/j.compositesa.2015.04.013 ↗
42. 10.1016/j.apsusc.2011.12.08510.1016/j.apsusc.2011.12.085 ↗
43. 10.1109/JSEN.2016.252420410.1109/JSEN.2016.2524204 ↗
44. 10.1016/j.porgcoat.2017.05.00810.1016/j.porgcoat.2017.05.008 ↗
45. 10.1016/j.cej.2015.07.02710.1016/j.cej.2015.07.027 ↗
46. 10.1016/j.apsusc.2013.04.11210.1016/j.apsusc.2013.04.112 ↗
47. 10.1039/c2jm16656a10.1039/c2jm16656a ↗
48. 10.1039/C5NR04702A10.1039/C5NR04702A ↗
49. 10.1039/c3ra42104j10.1039/c3ra42104j ↗
50. 10.1088/0957-4484/24/36/36570510.1088/0957-4484/24/36/365705 ↗
51. 10.1039/C5NJ01477H10.1039/C5NJ01477H ↗
52. 10.1590/S1516-1439200700040001310.1590/S1516-14392007000400013 ↗
53. 10.1016/j.matchemphys.2014.03.00510.1016/j.matchemphys.2014.03.005 ↗
54. 10.1016/j.molstruc.2010.12.01710.1016/j.molstruc.2010.12.017 ↗
55. 10.1016/j.jorganchem.2008.12.02710.1016/j.jorganchem.2008.12.027 ↗
56. 10.1002/pi.141510.1002/pi.1415 ↗
57. 10.1016/j.saa.2010.08.04910.1016/j.saa.2010.08.049 ↗
58. 10.1016/0021-9797(90)90067-X10.1016/0021-9797(90)90067-X ↗
59. Zand · International Journal of Electrochemical Science · 2013 · 8 · 4927
60. 10.1016/j.porgcoat.2003.08.01510.1016/j.porgcoat.2003.08.015 ↗