Corrosion Resistance Studies of Cerium Conversion Coating with a Fluoride-Free Pretreatment on AZ91D Magnesium Alloy
Source abstract
Abstract
An alternative of toxic hydrofluoric acid (HF) commonly used in the pretreatment process of magnesium (Mg) alloys prior to the conversion coating treatment in a cerium (Ce) nitrate and hydrogen peroxide bath was systematically investigated in this study. Comparing with the HF- and HCl-pretreated samples, the corrosion film formed in the vanadate solution at pH 8 effectively retarded the reaction rate of the Ce conversion coating. As a result, the average size and population density of blisters on the Ce conversion coating were markedly reduced. Both the electrochemical impedance spectroscopy and salt spray test showed that the Ce conversion coating with improved corrosion resistance can be made on the AZ91D that was pretreated in the vanadate solution for 120 s. Consequently, the vanadate solution is a feasible alternative to the HF solution for the pretreatment of the AZ91D prior to the Ce conversion coating treatment.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Magnesium Alloys: Properties and Applications · Corrosion Behavior and Inhibition · Metal and Thin Film Mechanics
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (66)
Show source-provided references
1. 10.2320/matertrans.42.115410.2320/matertrans.42.1154 ↗
2. 10.1016/S0925-8388(01)01899-010.1016/S0925-8388(01)01899-0 ↗
3. Biestek T. Weber J. , Electrolytic and Chemical Conversion Coatings, 1st ed. Portcullis Poland, 208 (1976).
4. 10.1149/1.183653310.1149/1.1836533 ↗
5. 10.1149/1.183823410.1149/1.1838234 ↗
6. 10.1149/1.139183810.1149/1.1391838 ↗
7. 10.1149/1.142489610.1149/1.1424896 ↗
8. 10.1149/1.216478710.1149/1.2164787 ↗
9. 10.1016/0010-938X(95)00078-X10.1016/0010-938X(95)00078-X ↗
10. 10.5006/1.328395110.5006/1.3283951 ↗
11. 10.1016/j.corsci.2004.11.02310.1016/j.corsci.2004.11.023 ↗
12. 10.1016/j.corsci.2007.04.01110.1016/j.corsci.2007.04.011 ↗
13. 10.1016/j.electacta.2007.08.01510.1016/j.electacta.2007.08.015 ↗
14. 10.1016/j.electacta.2008.01.00910.1016/j.electacta.2008.01.009 ↗
15. 10.1016/S0010-938X(99)00076-110.1016/S0010-938X(99)00076-1 ↗
16. 10.1016/S0257-8972(03)00336-010.1016/S0257-8972(03)00336-0 ↗
17. 10.1016/j.corsci.2004.06.01610.1016/j.corsci.2004.06.016 ↗
18. 10.1149/1.184537110.1149/1.1845371 ↗
19. 10.2320/matertrans.47.102010.2320/matertrans.47.1020 ↗
20. 10.1016/j.corsci.2008.03.01510.1016/j.corsci.2008.03.015 ↗
21. 10.1016/j.corsci.2009.08.00310.1016/j.corsci.2009.08.003 ↗
22. 10.1016/j.corsci.2010.02.03610.1016/j.corsci.2010.02.036 ↗
23. 10.1016/j.matchemphys.2006.08.00710.1016/j.matchemphys.2006.08.007 ↗
24. 10.5006/1.356363910.5006/1.3563639 ↗
25. 10.1149/2.091205jes10.1149/2.091205jes ↗
26. 10.2320/matertrans.42.121910.2320/matertrans.42.1219 ↗
27. 10.2320/matertrans.42.123710.2320/matertrans.42.1237 ↗
28. Hinton · Met. Forum. · 1984 · 7 · 211
29. Wilson L. Hinton B. R. W. , Patent WO 88/06639 (1988).
30. 10.1016/0040-6090(95)06932-110.1016/0040-6090(95)06932-1 ↗
31. 10.1016/S0169-4332(00)00873-410.1016/S0169-4332(00)00873-4 ↗
32. 10.1016/S0257-8972(02)00062-210.1016/S0257-8972(02)00062-2 ↗
33. 10.1016/S0257-8972(03)00742-410.1016/S0257-8972(03)00742-4 ↗
34. 10.1016/j.apsusc.2006.03.01010.1016/j.apsusc.2006.03.010 ↗
35. 10.1016/j.electacta.2008.05.03910.1016/j.electacta.2008.05.039 ↗
36. 10.1016/j.surfcoat.2008.01.02710.1016/j.surfcoat.2008.01.027 ↗
37. 10.1016/j.surfcoat.2009.05.01910.1016/j.surfcoat.2009.05.019 ↗
38. 10.1016/j.tsf.2009.03.04610.1016/j.tsf.2009.03.046 ↗
39. 10.1016/j.apsusc.2008.10.11010.1016/j.apsusc.2008.10.110 ↗
40. 10.1149/1.353782110.1149/1.3537821 ↗
41. 10.1149/2.jes11358510.1149/2.jes113585 ↗
42. Environment, Health and Safety Information for the Berkeley Campus Fact Sheet on Hydrofluoric Acid (2008).
43. ASTM B 117-03, Standard Practice for Operating Salt Spray (Fog) Apparatus, American Society for Testing and Materials, ASTM International, Philadelphia, USA (2003).
44. 10.1149/1.361143010.1149/1.3611430 ↗
45. 10.1016/S0010-938X(01)00118-410.1016/S0010-938X(01)00118-4 ↗
46. 10.1016/j.corsci.2006.11.00710.1016/j.corsci.2006.11.007 ↗
47. 10.1016/j.corsci.2011.07.02110.1016/j.corsci.2011.07.021 ↗
48. 10.1016/j.electacta.2007.05.02210.1016/j.electacta.2007.05.022 ↗
49. 10.1016/S0013-4686(01)00476-510.1016/S0013-4686(01)00476-5 ↗
50. 10.1016/j.corsci.2011.01.00810.1016/j.corsci.2011.01.008 ↗
51. 10.1016/S0010-938X(97)00090-510.1016/S0010-938X(97)00090-5 ↗
52. 10.1149/1.240105610.1149/1.2401056 ↗
53. 10.1016/j.corsci.2011.07.03710.1016/j.corsci.2011.07.037 ↗
54. 10.1016/j.porgcoat.2004.07.00110.1016/j.porgcoat.2004.07.001 ↗
55. 10.1016/j.electacta.2006.12.03210.1016/j.electacta.2006.12.032 ↗
56. 10.1016/0010-938X(87)90079-510.1016/0010-938X(87)90079-5 ↗
57. 10.1016/0013-4686(88)85045-X10.1016/0013-4686(88)85045-X ↗
58. 10.1016/0013-4686(91)85196-E10.1016/0013-4686(91)85196-E ↗
59. 10.1016/j.electacta.2008.06.06910.1016/j.electacta.2008.06.069 ↗
60. 10.1016/j.corsci.2011.07.02110.1016/j.corsci.2011.07.021 ↗
61. 10.1016/j.corsci.2011.05.02710.1016/j.corsci.2011.05.027 ↗
62. 10.1016/j.apsusc.2004.03.25010.1016/j.apsusc.2004.03.250 ↗
63. 10.1149/1.290777210.1149/1.2907772 ↗
64. 10.5006/1.328773310.5006/1.3287733 ↗
65. Pourbaix M. , Atlas of Electrochemical Equilibria in Aqueous Solutions, 2nd ed., NACE, Houston, Texas (1974).
66. Lide D. R. , CRC Handbook of Chemistry and Physics, 74th ed. CRC Press, Boca Raton, Florida (1993).