Formation of Porous Anodic Films on Carbon Steels and Their Application to Corrosion Protection Composite Coatings Formed with Polypyrrole

The growth behavior of nanoporous anodic films on carbon steel containing 0.213 mass% carbon has been examined. The films were grown by anodizing in an ethylene glycol (EG) electrolyte containing 0.1 mol dm −3 NH 4 F and 0.5 mol dm −3 H 2 O. The steel contains carbide precipitates with sizes in the range 50–800 nm. The anodic film formed on the carbide phase grew more slowly and was more chemically soluble during anodizing, resulting in submicrometer pits on the anodic film. The nanoporous morphology of the anodic films formed on an α-Fe matrix resembled those formed on iron. Heat treatment of the anodized specimens caused transformation of the chemically soluble fluoride-containing amorphous or poorly crystalline anodic films to crystalline oxide films containing α-Fe 2 O 3 and Fe 3 O 4 . Polypyrrole (PPy) was electropolymerized on the transformed surfaces to form a corrosion-protective composite coating. The resultant specimens coated with the composite coating showed improved durability compared to passivated steel with a PPy coating.