A Broad Stability Investigation of Nb-Doped SrCoO_2.5+δas a Reversible Oxygen Electrode for Intermediate-Temperature Solid Oxide Fuel Cells

The present work reports a systematic study on the structural, thermal, electrical and electrochemical stability of SrCo 1−x Nb x O 2.5+δ series as a potential reversible oxygen-electrode for intermediate-temperature solid oxide fuel cells. The identified best composition is x = 0.10, which exhibits a stable pseudo primitive cubic structure at <700°C and a reversible oxygen redox reaction at 350°C. The conductivity of this material is p -type and also exhibits a peak at 350°C, implying that the electron hole conduction is closely associated with the oxygen nonstoichiometry. Electrochemical impedance spectroscopy analysis indicates a low polarization resistance rate-limited by a slower surface O 2 dissociation step. Overall, the material is thermally stable and oxygen redox reversible below 700°C, above which a catalytically less active brownmillerite SrCoO 2.5 is formed.