Passivity Breakdown of Titanium in LiBr Solutions
Source abstract
Abstract
The passive behavior of titanium and its susceptibility to undergo localized attack in different LiBr solutions at 25°C have been investigated using different electrochemical techniques: potentiodynamic polarization curves, potentiostatic passivation tests, EIS measurements and Mott-Schottky analysis. In low and moderately concentrated LiBr solutions, the breakdown potential E b decreased with increasing bromide concentrations, while in highly concentrated LiBr solutions, E b increased with increasing LiBr concentration. In the most concentrated LiBr solution (11.42M) Ti did not undergo passivity breakdown even at 9 V Ag/AgCl . This observation can be explained by a a decrease in the activity of water in highly concentrated LiBr solutions.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Hydrogen embrittlement and corrosion behaviors in metals · Corrosion Behavior and Inhibition · Nuclear Materials and Properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (73)
Show source-provided references
1. Been J. Grauman J. S. , in: Uhlig's Corrosion Handbook, 2nd ed., Winston Revie R. (ed.), 863-885, Wiley Interscience, New York (2000).
2. 10.1016/j.corsci.2006.07.00710.1016/j.corsci.2006.07.007 ↗
3. 10.1016/j.electacta.2005.05.05110.1016/j.electacta.2005.05.051 ↗
4. 10.1016/0013-4686(95)00465-310.1016/0013-4686(95)00465-3 ↗
5. 10.1016/j.electacta.2005.02.12110.1016/j.electacta.2005.02.121 ↗
6. 10.5006/1.328051110.5006/1.3280511 ↗
7. 10.1016/j.corsci.2006.08.01010.1016/j.corsci.2006.08.010 ↗
8. 10.1016/S0010-938X(00)00105-010.1016/S0010-938X(00)00105-0 ↗
9. 10.1016/j.corsci.2009.06.03510.1016/j.corsci.2009.06.035 ↗
10. 10.1016/j.corsci.2005.10.01310.1016/j.corsci.2005.10.013 ↗
11. 10.1016/j.tsf.2010.10.07110.1016/j.tsf.2010.10.071 ↗
12. 10.1016/j.matchemphys.2010.12.02810.1016/j.matchemphys.2010.12.028 ↗
13. 10.1149/1.302100810.1149/1.3021008 ↗
14. 10.1134/S102319350702001210.1134/S1023193507020012 ↗
15. 10.1016/j.electacta.2012.04.15810.1016/j.electacta.2012.04.158 ↗
16. Roberge P. R. , Handbook of Corrosion Engineering, p. 756, McGraw-Hill, New York (2000).
17. 10.1021/j100044a03410.1021/j100044a034 ↗
18. 10.1149/1.139336410.1149/1.1393364 ↗
19. 10.1016/0010-938X(64)90041-110.1016/0010-938X(64)90041-1 ↗
20. 10.5006/1.328783910.5006/1.3287839 ↗
21. 10.1016/j.corsci.2010.12.02110.1016/j.corsci.2010.12.021 ↗
22. 10.1149/1.205478310.1149/1.2054783 ↗
23. 10.1149/1.240325310.1149/1.2403253 ↗
24. 10.1016/0010-938X(90)90120-T10.1016/0010-938X(90)90120-T ↗
25. 10.1016/j.electacta.2011.09.03410.1016/j.electacta.2011.09.034 ↗
26. 10.1016/S1364-0321(01)00003-X10.1016/S1364-0321(01)00003-X ↗
27. Lee R. J. DiGuilio R. M. Jeter S. M. Teja A. S. , ASHRAE Tran., 96(1), (1990).
28. 10.5006/1.329351610.5006/1.3293516 ↗
29. 10.1016/S0196-8904(03)00006-210.1016/S0196-8904(03)00006-2 ↗
30. 10.1016/j.ijrefrig.2004.09.00610.1016/j.ijrefrig.2004.09.006 ↗
31. 10.1063/1.325310810.1063/1.3253108 ↗
32. Prausnitz J. M. Lichtenthaler R. N. Azevedo E. G. , Molecular Thermodynamics of Fluid-Phase Equilibria, p. 517, Prentice Hall, Upper Saddle River, NJ (1999).
33. 10.1039/b400473f10.1039/b400473f ↗
34. 10.1016/j.chemosphere.2003.09.01610.1016/j.chemosphere.2003.09.016 ↗
35. 10.5006/1.327759110.5006/1.3277591 ↗
36. 10.1016/j.corsci.2011.01.01310.1016/j.corsci.2011.01.013 ↗
37. 10.1016/S0013-4686(01)00664-810.1016/S0013-4686(01)00664-8 ↗
38. 10.1149/1.212759210.1149/1.2127592 ↗
39. 10.1149/1.183764310.1149/1.1837643 ↗
40. 10.1149/1.206909610.1149/1.2069096 ↗
41. 10.1351/pac19997106095110.1351/pac199971060951 ↗
42. 10.1016/j.electacta.2010.11.00510.1016/j.electacta.2010.11.005 ↗
43. 10.1016/j.electacta.2005.02.10310.1016/j.electacta.2005.02.103 ↗
44. 10.1016/j.electacta.2010.09.07710.1016/j.electacta.2010.09.077 ↗
45. 10.1016/j.jnucmat.2008.06.00410.1016/j.jnucmat.2008.06.004 ↗
46. 10.1016/0013-4686(89)87086-010.1016/0013-4686(89)87086-0 ↗
47. 10.1016/0013-4686(95)00427-010.1016/0013-4686(95)00427-0 ↗
48. 10.1016/S0013-4686(98)00372-710.1016/S0013-4686(98)00372-7 ↗
49. 10.1016/0010-938X(95)00084-W10.1016/0010-938X(95)00084-W ↗
50. 10.1016/j.apsusc.2005.02.13510.1016/j.apsusc.2005.02.135 ↗
51. 10.1016/j.corsci.2007.06.00910.1016/j.corsci.2007.06.009 ↗
52. 10.1016/j.corsci.2007.08.01310.1016/j.corsci.2007.08.013 ↗
53. 10.1016/j.electacta.2011.11.02410.1016/j.electacta.2011.11.024 ↗
54. 10.1016/j.electacta.2013.02.02410.1016/j.electacta.2013.02.024 ↗
55. 10.1149/1.209689410.1149/1.2096894 ↗
56. 10.1590/S1516-1439200600040000810.1590/S1516-14392006000400008 ↗
57. 10.1016/S0022-0728(84)80324-110.1016/S0022-0728(84)80324-1 ↗
58. 10.1016/j.electacta.2010.07.02810.1016/j.electacta.2010.07.028 ↗
59. 10.5006/1.331593310.5006/1.3315933 ↗
60. 10.1149/1.183861510.1149/1.1838615 ↗
61. Fernández-Domene · Int. J. Electrochem. Sc. · 2011 · 6 · 329210.1016/S1452-3981(23)18252-6 ↗
62. 10.1016/j.corsci.2007.05.02010.1016/j.corsci.2007.05.020 ↗
63. 10.1016/S0378-3812(01)00734-810.1016/S0378-3812(01)00734-8 ↗
64. 10.1149/1.209691310.1149/1.2096913 ↗
65. 10.1007/s10008-008-0649-510.1007/s10008-008-0649-5 ↗
66. Beck K. O. , Titanium anodizing process, US Patent 2,949, 411 (1960).
67. 10.1016/0376-4583(82)90033-410.1016/0376-4583(82)90033-4 ↗
68. 10.1021/ed070p17610.1021/ed070p176 ↗
69. 10.1016/S1350-4533(01)00050-910.1016/S1350-4533(01)00050-9 ↗
70. 10.2320/matertrans.43.314210.2320/matertrans.43.3142 ↗
71. 10.1007/s10853-005-2802-110.1007/s10853-005-2802-1 ↗
72. 10.1002/col.2040310.1002/col.20403 ↗
73. 10.1007/s11665-011-9860-010.1007/s11665-011-9860-0 ↗