Pulsed Electroreduction of CO 2 on Silver Electrodes

A large degree of selectivity of reduction products of has been achieved on Ag electrodes by a pulsed technique in which the anodic ( V a ) and the cathodic ( V c ) bias were found to be key parameters. The maximum faradaic efficiencies for CO, , and were, respectively, 70% ( V c = −2.0 V, V a = −0.125 V), 55% (−2.25 V, −0.4 V), 3.1% (−2.25 V, −0.4 V), 3.1% (−2.25 V, −0.4 V), and 22% (−2.25 V, −0.5 V). The total value of 58.1% for and formation recorded on the Ag electrode is comparable with that for and formation on the Cu electrode, which has long been considered as a unique metal for and formation. In addition, in the potential range where and are preferentially produced, the formation of HCOOH was found to be almost zero. The selectivity was ascribed to be due to the extent of the surface coverage of adsorbed hydrogen, which can be controlled by the anodic bias.