Studies of Several Pickling and Activation Processes for Electroless Ni-P Plating on AZ31 Magnesium Alloy
Source abstract
Abstract
Several chromium-free pickling and activation processes were investigated in order to develop an eco-friendly pretreatment for electroless Ni-P plating on magnesium alloy. The coatings obtained from etching only in H 3 PO 4 solution exhibit poor adhesion due to the existance of an interlayer. Meanwhile, a corrosion model of Mg alloy in H 3 PO 4 solution was proposed. When fluoride was added into the pickling solution, the adhesion of the coatings was also unsatisfied because of the bad mechanical interlocking action. By comparison, the coatings obtained from pickling in H 3 PO 4 solution followed by NH 4 HF 2 activation displayed wonderful properties in both adhesion and corrosion resistance.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Magnesium Alloys: Properties and Applications · Electrodeposition and Electroless Coatings · Corrosion Behavior and Inhibition
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (50)
Show source-provided references
1. Schumann S. Friedrich H. , in Magnesium Technology, Metallurgy, Design Data, Applications, Friedrich H. E. Mordike B. L. , Editors, p. 499, Springer–Verlag, Berlin, Germany (2006).
2. 10.1007/s11998-011-9336-z10.1007/s11998-011-9336-z ↗
3. 10.1016/j.surfcoat.2014.01.02210.1016/j.surfcoat.2014.01.022 ↗
4. 10.1016/j.corsci.2007.02.00610.1016/j.corsci.2007.02.006 ↗
5. 10.1016/j.corsci.2012.08.03710.1016/j.corsci.2012.08.037 ↗
6. 10.1016/S0010-938X(99)00076-110.1016/S0010-938X(99)00076-1 ↗
7. 10.1016/j.corsci.2008.12.01510.1016/j.corsci.2008.12.015 ↗
8. 10.1016/j.corsci.2009.03.01410.1016/j.corsci.2009.03.014 ↗
9. 10.1016/j.corsci.2004.09.01810.1016/j.corsci.2004.09.018 ↗
10. 10.1016/j.corsci.2009.04.02510.1016/j.corsci.2009.04.025 ↗
11. 10.1016/j.surfcoat.2014.03.04310.1016/j.surfcoat.2014.03.043 ↗
12. 10.1016/j.surfcoat.2013.06.10010.1016/j.surfcoat.2013.06.100 ↗
13. 10.1016/j.apsusc.2011.01.01610.1016/j.apsusc.2011.01.016 ↗
14. 10.1016/j.surfcoat.2012.12.03910.1016/j.surfcoat.2012.12.039 ↗
15. 10.1016/j.surfcoat.2013.05.04710.1016/j.surfcoat.2013.05.047 ↗
16. 10.1016/j.corsci.2006.08.02510.1016/j.corsci.2006.08.025 ↗
17. 10.1016/S0925-8388(01)01899-010.1016/S0925-8388(01)01899-0 ↗
18. 10.1016/j.jallcom.2013.03.10710.1016/j.jallcom.2013.03.107 ↗
19. 10.1016/j.corsci.2013.10.02410.1016/j.corsci.2013.10.024 ↗
20. 10.1016/j.corsci.2012.03.03010.1016/j.corsci.2012.03.030 ↗
21. 10.1016/j.corsci.2009.12.01010.1016/j.corsci.2009.12.010 ↗
22. 10.1016/j.apsusc.2009.11.06210.1016/j.apsusc.2009.11.062 ↗
23. 10.1016/j.corsci.2010.03.00210.1016/j.corsci.2010.03.002 ↗
24. 10.1016/j.surfcoat.2008.05.03710.1016/j.surfcoat.2008.05.037 ↗
25. 10.1016/j.surfcoat.2005.05.02310.1016/j.surfcoat.2005.05.023 ↗
26. 10.1016/j.surfcoat.2004.12.00110.1016/j.surfcoat.2004.12.001 ↗
27. 10.1016/S0257-8972(03)00866-110.1016/S0257-8972(03)00866-1 ↗
28. 10.1016/j.apsusc.2008.01.14410.1016/j.apsusc.2008.01.144 ↗
29. 10.1016/j.tsf.2006.02.02310.1016/j.tsf.2006.02.023 ↗
30. 10.1016/j.jallcom.2008.06.06710.1016/j.jallcom.2008.06.067 ↗
31. 10.1016/j.corsci.2011.10.02810.1016/j.corsci.2011.10.028 ↗
32. 10.1149/1.304024310.1149/1.3040243 ↗
33. 10.1016/j.jallcom.2007.12.04110.1016/j.jallcom.2007.12.041 ↗
34. 10.1149/2.069207jes10.1149/2.069207jes ↗
35. 10.1016/j.corsci.2009.06.04510.1016/j.corsci.2009.06.045 ↗
36. 10.1179/0020296712Z.0000000003710.1179/0020296712Z.00000000037 ↗
37. 10.1016/j.surfcoat.2013.04.01110.1016/j.surfcoat.2013.04.011 ↗
38. 10.1016/j.surfcoat.2005.12.01210.1016/j.surfcoat.2005.12.012 ↗
39. 10.1016/j.surfcoat.2011.02.05110.1016/j.surfcoat.2011.02.051 ↗
40. 10.1016/j.corsci.2009.03.00510.1016/j.corsci.2009.03.005 ↗
41. 10.1016/j.corsci.2010.01.02010.1016/j.corsci.2010.01.020 ↗
42. 10.1016/j.corsci.2013.03.02110.1016/j.corsci.2013.03.021 ↗
43. 10.1149/2.012309jes10.1149/2.012309jes ↗
44. Martyak N. M. McCaskie J. E. , Removal of orthophosphite ions from electroless nickel plating baths: U. S. Pat. 6,048,585[P]. 2000–4–11.
45. 10.1179/0020296712Z.0000000006110.1179/0020296712Z.00000000061 ↗
46. Initial deposition mechanism of electroless nickel plating on magnesium alloys10.1080/00202967.2001.11871356 ↗
47. 10.1016/S1003-6326(09)60440-410.1016/S1003-6326(09)60440-4 ↗
48. 10.1016/j.jallcom.2004.07.08310.1016/j.jallcom.2004.07.083 ↗
49. 10.1016/j.surfcoat.2010.04.04010.1016/j.surfcoat.2010.04.040 ↗
50. 10.1016/j.surfcoat.2005.07.00110.1016/j.surfcoat.2005.07.001 ↗