Ultrasonic-Assisted Electroless Ni-P Plating on Dual Phase Mg-Li Alloy
Source abstract
Abstract
An ultrasonic-assisted method for electroless Ni-P plating on dual-phase Mg-Li alloy is proposed. Environmentally-friendly Ce(NO 3 ) 3 -KMnO 4 solution was successfully applied for the pre-treatment. Uniform and compact Ni-P coatings with fine structures have been successfully obtained. The Ni-P coatings are mixed with amorphous-crystalline features and well adhered to the substrates. The corrosion resistances were investigated by electrochemical impedance spectroscopy, open circuit potential, potentiodynamic polarization and hydrogen evolution tests. The results indicate that ultrasonic processing significantly improves the corrosion resistance of Ni-P coatings due to the formation of uniform, dense and fine structures, which strengthen the passive film.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Magnesium Alloys: Properties and Applications · Corrosion Behavior and Inhibition · Hydrogen Storage and Materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (61)
Show source-provided references
1. 10.1016/S0040-6031(01)00534-210.1016/S0040-6031(01)00534-2 ↗
2. 10.1016/j.scriptamat.2006.11.01710.1016/j.scriptamat.2006.11.017 ↗
3. 10.1016/S0921-5093(96)10460-310.1016/S0921-5093(96)10460-3 ↗
4. 10.1016/j.msea.2005.08.08810.1016/j.msea.2005.08.088 ↗
5. 10.1016/j.matlet.2005.12.03810.1016/j.matlet.2005.12.038 ↗
6. 10.1016/j.corsci.2009.03.01410.1016/j.corsci.2009.03.014 ↗
7. 10.1016/j.corsci.2009.04.02510.1016/j.corsci.2009.04.025 ↗
8. 10.1016/S0925-8388(01)01899-010.1016/S0925-8388(01)01899-0 ↗
9. 10.1016/S0257-8972(03)00866-110.1016/S0257-8972(03)00866-1 ↗
10. 10.1016/j.corsci.2011.07.00610.1016/j.corsci.2011.07.006 ↗
11. 10.1016/j.surfcoat.2007.07.09410.1016/j.surfcoat.2007.07.094 ↗
12. 10.1179/1743278212Y.000000007210.1179/1743278212Y.0000000072 ↗
13. 10.1016/j.jallcom.2007.12.04110.1016/j.jallcom.2007.12.041 ↗
14. 10.1016/S1003-6326(11)60999-010.1016/S1003-6326(11)60999-0 ↗
15. 10.1016/j.surfcoat.2013.03.02410.1016/j.surfcoat.2013.03.024 ↗
16. 10.1016/j.tsf.2011.01.03210.1016/j.tsf.2011.01.032 ↗
17. 10.1016/j.msea.2006.06.10710.1016/j.msea.2006.06.107 ↗
18. 10.4028/www.scientific.net/AMR.271-273.78510.4028/www.scientific.net/AMR.271-273.785 ↗
19. 10.3321/j.issn:1002-185X.2009.07.00710.3321/j.issn:1002-185X.2009.07.007 ↗
20. 10.1002/maco.20100605010.1002/maco.201006050 ↗
21. 10.1016/j.cap.2009.10.01110.1016/j.cap.2009.10.011 ↗
22. 10.1016/j.surfcoat.2008.08.07410.1016/j.surfcoat.2008.08.074 ↗
23. 10.1016/j.corsci.2012.10.01310.1016/j.corsci.2012.10.013 ↗
24. 10.1016/j.corsci.2009.08.01210.1016/j.corsci.2009.08.012 ↗
25. 10.1016/j.surfcoat.2006.07.08010.1016/j.surfcoat.2006.07.080 ↗
26. 10.1016/j.corsci.2006.08.02510.1016/j.corsci.2006.08.025 ↗
27. 10.1016/j.electacta.2004.04.02310.1016/j.electacta.2004.04.023 ↗
28. 10.1016/j.surfcoat.2014.03.04310.1016/j.surfcoat.2014.03.043 ↗
29. 10.1016/j.surfcoat.2004.12.00910.1016/j.surfcoat.2004.12.009 ↗
30. 10.1179/174591910X1264605576533010.1179/174591910X12646055765330 ↗
31. 10.1016/j.electacta.2011.07.08610.1016/j.electacta.2011.07.086 ↗
32. 10.1016/j.surfcoat.2010.11.02110.1016/j.surfcoat.2010.11.021 ↗
33. Li · The Chinese Journal of Nonferrous Metals(China) · 1998 · 8 · 573
34. 10.1016/j.tsf.2004.02.10010.1016/j.tsf.2004.02.100 ↗
35. 10.1016/S0041-624X(99)00215-210.1016/S0041-624X(99)00215-2 ↗
36. 10.1016/S0257-8972(01)01683-810.1016/S0257-8972(01)01683-8 ↗
37. 10.1108/0305612121119500310.1108/03056121211195003 ↗
38. 10.1179/174591911X1317050014767010.1179/174591911X13170500147670 ↗
39. 10.1007/978-94-007-5533-8_210.1007/978-94-007-5533-8_2 ↗
40. 10.1016/j.corsci.2013.10.02410.1016/j.corsci.2013.10.024 ↗
41. 10.1002/adem.20050001310.1002/adem.200500013 ↗
42. 10.1016/j.surfcoat.2012.12.03910.1016/j.surfcoat.2012.12.039 ↗
43. 10.1179/02670840222501001010.1179/026708402225010010 ↗
44. Taheri R. , Evaluation of electroless nickel-phosphorus (EN) coatings, Ph. D. Thesis, the University of Saskatchewan (2002).
45. 10.1016/j.matchemphys.2010.01.04210.1016/j.matchemphys.2010.01.042 ↗
46. 10.1016/S1003-6326(09)60440-410.1016/S1003-6326(09)60440-4 ↗
47. 10.1016/j.corsci.2009.03.01110.1016/j.corsci.2009.03.011 ↗
48. 10.1016/j.corsci.2013.07.04610.1016/j.corsci.2013.07.046 ↗
49. 10.1016/j.tsf.2007.10.00810.1016/j.tsf.2007.10.008 ↗
50. 10.1016/j.apsusc.2004.05.14310.1016/j.apsusc.2004.05.143 ↗
51. 10.1007/s40195-013-0162-410.1007/s40195-013-0162-4 ↗
52. 10.1016/j.matdes.2010.06.02110.1016/j.matdes.2010.06.021 ↗
53. 10.1016/j.matchar.2009.10.00610.1016/j.matchar.2009.10.006 ↗
54. 10.1016/j.electacta.2007.09.02610.1016/j.electacta.2007.09.026 ↗
55. 10.1016/j.ultsonch.2010.02.01410.1016/j.ultsonch.2010.02.014 ↗
56. 10.1016/j.scitotenv.2008.12.03110.1016/j.scitotenv.2008.12.031 ↗
57. 10.1016/j.dyepig.2004.06.01210.1016/j.dyepig.2004.06.012 ↗
58. 10.1126/science.247.4949.143910.1126/science.247.4949.1439 ↗
59. 10.1016/j.ultsonch.2004.06.00210.1016/j.ultsonch.2004.06.002 ↗
60. Parkinson R. , Nickel Development Institute, (1997).
61. Duncan · Plat. Surf. Finish. · 1996 · 83 · 65