Volume Expansion Factor and Growth Efficiency of Anodic Alumina Formed in Sulphuric Acid
Source abstract
Abstract
The growth of anodic alumina in sulphuric acid is investigated at constant current on bulk and sputtering-deposited aluminium. The ratio of the thickness of the film to the thickness of oxidized aluminium is shown to increase with increase of the current density (from 0.5 to 50 mA cm−2) and with decrease of the electrolyte temperature (from 20 to 0°C). In addition, the sulphur content of the films and the efficiency of film formation increase. It is suggested that pores are generated primarily by dissolution at current densities below ∼2 mA cm−2, with flow of film material dominating at higher current densities.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Anodic Oxide Films and Nanostructures · Smart Materials for Construction · Concrete Corrosion and Durability
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (47)
Show source-provided references
1. Wernick · 1996
2. Keller · J. Electrochem. Soc. · 1953 · 100 · 41110.1149/1.2781142 ↗
3. Hoar · J. Phys. Chem. Solids · 1959 · 9 · 9710.1016/0022-3697(59)90199-4 ↗
4. O’Sullivan · Proc. R. Soc. London · 1970 · 317 · 51110.1098/rspa.1970.0129 ↗
5. Cherki · J. Electrochem. Soc. · 1973 · 120 · 78410.1149/1.2403563 ↗
6. Siejka · J. Electrochem. Soc. · 1977 · 124 · 88310.1149/1.2133446 ↗
7. Lee · Nature Mater. · 2006 · 5 · 74110.1038/nmat1717 ↗
8. Lee · Nat. Nanotechnol. · 2008 · 3 · 23410.1038/nnano.2008.54 ↗
9. Moutarlier · Appl. Surf. Sci. · 2003 · 206 · 23710.1016/S0169-4332(02)01240-0 ↗
10. Boisier · Surf. Coat. Technol. · 2009 · 203 · 342010.1016/j.surfcoat.2009.05.008 ↗
11. Wood · Electrochim. Acta · 1970 · 15 · 186510.1016/0013-4686(70)85024-1 ↗
12. Vrublevsky · Appl. Surf. Sci. · 2004 · 222 · 21510.1016/j.apsusc.2003.08.014 ↗
13. Skeldon · Electrochem. Solid-State Lett. · 2006 · 9 · B4710.1149/1.2335938 ↗
14. Doolittle · Nucl. Instrum. Methods Phys. Res. B · 1985 · 9 · 34410.1016/0168-583X(85)90762-1 ↗
15. Mayer · 1999 · p. 541
16. Amsel · Anal. Chem. · 1967 · 39 · 168910.1021/ac50157a027 ↗
17. Vickridge · Nucl. Instrum. Methods Phys. Res. B · 2002 · 190 · 57410.1016/S0168-583X(01)01303-9 ↗
18. Vickridge · Nucl. Instrum Methods Phys. Res. B · 1990 · 45 · 610.1016/0168-583X(90)90772-M ↗
19. Ono · 2000 · p. 398
20. Cuff · J. Inst. Met. · 1958–1959 · 87 · 248–1959
21. Aerts · Electrochim. Acta · 2009 · 54 · 27010.1016/j.electacta.2008.08.004 ↗
22. Nagayama · Corros. Sci. · 1972 · 12 · 13310.1016/S0010-938X(72)90850-5 ↗
23. Nagayama · Electrochim. Acta · 1967 · 12 · 109710.1016/0013-4686(67)80105-1 ↗
24. Hunter · J. Electrochem. Soc. · 1954 · 101 · 51410.1149/1.2781147 ↗
25. Konno · Electrochim. Acta · 1980 · 25 · 166710.1016/0013-4686(80)80020-X ↗
26. Brown · J. Electrochem. Soc. · 1973 · 120 · 109610.1149/1.2403637 ↗
27. Davies · J. Electrochem. Soc. · 1965 · 112 · 67510.1149/1.2423662 ↗
28. Khalil · Electrochim. Acta · 1986 · 31 · 12910.1016/0013-4686(86)80148-7 ↗
29. Lu · Corros. Sci. · 2004 · 46 · 281710.1016/j.corsci.2004.03.021 ↗
30. Iglesias-Rubianes · Corros. Sci. · 2003 · 45 · 290510.1016/S0010-938X(03)00116-1 ↗
31. Thompson · Philos. Mag. B · 1987 · 55 · 65110.1080/13642818708218371 ↗
32. Skeldon · Surf. Interface Anal. · 1983 · 5 · 24710.1002/sia.v5:6 ↗
33. Shimizu · Electrochim. Acta · 2000 · 45 · 180510.1016/S0013-4686(99)00397-7 ↗
34. Thompson · Nature (London) · 1981 · 290 · 23010.1038/290230a0 ↗
35. Nielsch · Nano Lett. · 2002 · 2 · 67710.1021/nl025537k ↗
36. Patermarakis · J. Solid State Electrochem. · 2009 · 13 · 183110.1007/s10008-008-0745-6 ↗
37. Hebert · J. Electrochem. Soc. · 2009 · 156 · C27510.1149/1.3151835 ↗
38. Jessensky · Appl. Phys. Lett. · 1998 · 22 · 117310.1063/1.121004 ↗
39. Li · J. Appl. Phys. · 1998 · 84 · 602310.1063/1.368911 ↗
40. Skeldon · Philos. Mag. B · 1989 · 60 · 51310.1080/13642818908205924 ↗
41. Habazaki · J. Electrochem. Soc. · 1996 · 143 · 246510.1149/1.1837032 ↗
42. Iglesias-Rubianes · Corros. Sci. · 2001 · 43 · 221710.1016/S0010-938X(01)00022-1 ↗
43. Garcia-Vergara · Corros. Sci. · 2007 · 49 · 377210.1016/j.corsci.2007.03.036 ↗
44. Garcia-Vergara · J. Electrochem. Soc. · 2007 · 154 · C54010.1149/1.2756971 ↗
45. Houser · Nature Mater. · 2009 · 8 · 41510.1038/nmat2423 ↗
46. Barkey · J. Electrochem. Soc. · 2010 · 157 · C38810.1149/1.3484095 ↗
47. Oh · J. Electrochem. Soc. · 2011 · 158 · C7110.1149/1.3532778 ↗