Hydroxyapatite/Titania Composite Coatings on Biodegradable Magnesium Alloy for Enhanced Corrosion Resistance, Cytocompatibility and Antibacterial Properties
Source abstract
Abstract
Calcium phosphate (CaP) coatings have been widely studied as a biocompatible coating on biodegradable magnesium (Mg) alloys to improve the corrosion resistance and bioactivity for orthopedic application. However, the porous structure of CaP coatings formed in the aqueous solution cannot achieve the ideal long-time corrosion resistance. In this work, a titania (TiO 2 ) coating was prepared on the hydroxyapatite (HA) coated Mg alloy by a sol-gel method. The in vitro degradation results of electrochemical measurements and immersion test show that the corrosion resistance of HA coated Mg alloy was further improved by the TiO 2 sol-gel coatings. Furthermore, a systematic investigation of in vitro cytocompatibility and antibacterial properties of the samples was performed. The composite coating significantly enhanced cell adhesion and growth compared to the HA coating and uncoated Mg alloy. Meanwhile, the result of plate-counting method demonstrates that the antibacterial rate of the composite coating against E. coil and S.aureus reached 99.5 ± 0.3% and 99.8 ± 0.2%, respectively. These results suggest that the HA/TiO 2 composite coatings effectively enhanced the corrosion resistance, in vitro cytocompatibility and antibacterial properties of Mg alloy and porous CaP-based coating, potentially widening the application of Mg alloys in the biomedical field.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Magnesium Alloys: Properties and Applications · Aluminum Alloys Composites Properties · Corrosion Behavior and Inhibition
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (69)
Show source-provided references
1. 10.1016/j.actbio.2012.06.03710.1016/j.actbio.2012.06.037 ↗
2. 10.1016/j.actbio.2017.03.02210.1016/j.actbio.2017.03.022 ↗
3. 10.1021/am501119k10.1021/am501119k ↗
4. 10.1016/j.mser.2014.01.00110.1016/j.mser.2014.01.001 ↗
5. 10.1016/j.pmatsci.2013.08.00210.1016/j.pmatsci.2013.08.002 ↗
6. 10.1016/j.biomaterials.2004.09.04910.1016/j.biomaterials.2004.09.049 ↗
7. 10.1016/j.biomaterials.2014.04.04410.1016/j.biomaterials.2014.04.044 ↗
8. 10.1016/j.corsci.2014.09.00810.1016/j.corsci.2014.09.008 ↗
9. 10.1016/j.actbio.2011.11.01410.1016/j.actbio.2011.11.014 ↗
10. 10.1016/j.biomaterials.2016.10.01710.1016/j.biomaterials.2016.10.017 ↗
11. 10.1016/j.corsci.2016.10.01010.1016/j.corsci.2016.10.010 ↗
12. 10.1016/j.jmst.2017.07.01910.1016/j.jmst.2017.07.019 ↗
13. 10.1016/j.msea.2018.06.00210.1016/j.msea.2018.06.002 ↗
14. 10.1016/j.actbio.2013.11.01610.1016/j.actbio.2013.11.016 ↗
15. 10.1016/j.jmbbm.2011.05.02610.1016/j.jmbbm.2011.05.026 ↗
16. 10.1016/j.corsci.2013.06.01110.1016/j.corsci.2013.06.011 ↗
17. 10.1016/j.actbio.2013.02.04110.1016/j.actbio.2013.02.041 ↗
18. 10.1016/j.actbio.2014.10.01810.1016/j.actbio.2014.10.018 ↗
19. 10.1021/acsami.6b0052710.1021/acsami.6b00527 ↗
20. 10.1016/j.jmbbm.2017.08.03510.1016/j.jmbbm.2017.08.035 ↗
21. 10.5006/1.356363910.5006/1.3563639 ↗
22. 10.1016/j.corsci.2018.02.05110.1016/j.corsci.2018.02.051 ↗
23. 10.1016/j.actbio.2018.08.03010.1016/j.actbio.2018.08.030 ↗
24. 10.1016/j.corsci.2012.08.05210.1016/j.corsci.2012.08.052 ↗
25. 10.1016/j.biomaterials.2016.01.01610.1016/j.biomaterials.2016.01.016 ↗
26. 10.1016/j.actbio.2013.10.01210.1016/j.actbio.2013.10.012 ↗
27. 10.1016/j.actbio.2013.10.03610.1016/j.actbio.2013.10.036 ↗
28. 10.1016/j.actbio.2014.09.02610.1016/j.actbio.2014.09.026 ↗
29. 10.1021/acsbiomaterials.6b0001310.1021/acsbiomaterials.6b00013 ↗
30. 10.1016/j.matdes.2018.03.06110.1016/j.matdes.2018.03.061 ↗
31. 10.1016/j.actbio.2009.12.00910.1016/j.actbio.2009.12.009 ↗
32. 10.1016/j.surfcoat.2016.08.06510.1016/j.surfcoat.2016.08.065 ↗
33. 10.1016/j.corsci.2013.03.01710.1016/j.corsci.2013.03.017 ↗
34. 10.1016/j.corsci.2015.10.01010.1016/j.corsci.2015.10.010 ↗
35. 10.1021/am404574t10.1021/am404574t ↗
36. 10.1149/2.0901803jes10.1149/2.0901803jes ↗
37. 10.1016/j.biomaterials.2014.05.07410.1016/j.biomaterials.2014.05.074 ↗
38. 10.1016/j.surfcoat.2010.07.01310.1016/j.surfcoat.2010.07.013 ↗
39. 10.1021/am500206g10.1021/am500206g ↗
40. 10.1016/j.apsusc.2007.10.10710.1016/j.apsusc.2007.10.107 ↗
41. 10.1016/j.tsf.2013.03.10210.1016/j.tsf.2013.03.102 ↗
42. 10.1016/j.corsci.2010.04.00210.1016/j.corsci.2010.04.002 ↗
43. 10.1016/j.jmbbm.2015.11.03110.1016/j.jmbbm.2015.11.031 ↗
44. 10.1016/j.ceramint.2013.11.11910.1016/j.ceramint.2013.11.119 ↗
45. 10.1149/2.0801609jes10.1149/2.0801609jes ↗
46. 10.1149/2.036311jes10.1149/2.036311jes ↗
47. Su · Int. J. Electrochem. Sci. · 2012 · 7 · 1149710.1016/S1452-3981(23)16961-6 ↗
48. 10.1016/j.corsci.2007.01.00110.1016/j.corsci.2007.01.001 ↗
49. 10.1016/j.corsci.2009.10.01610.1016/j.corsci.2009.10.016 ↗
50. Paint A. C. D.-O. , M. Related Coatings and Applications, Standard test methods for measuring adhesion by tape test, ASTM International (2009).
51. 10.1007/s10856-013-4982-610.1007/s10856-013-4982-6 ↗
52. 10.1016/j.matchar.2006.11.03010.1016/j.matchar.2006.11.030 ↗
53. 10.1021/la00018a01410.1021/la00018a014 ↗
54. 10.1002/jbm.121210.1002/jbm.1212 ↗
55. 10.1016/j.corsci.2006.10.01610.1016/j.corsci.2006.10.016 ↗
56. 10.1016/j.corsci.2016.04.05210.1016/j.corsci.2016.04.052 ↗
57. 10.1016/j.apsusc.2012.10.14610.1016/j.apsusc.2012.10.146 ↗
58. 10.1016/j.corsci.2017.01.02510.1016/j.corsci.2017.01.025 ↗
59. 10.1016/j.pmatsci.2017.04.01110.1016/j.pmatsci.2017.04.011 ↗
60. 10.1016/j.surfcoat.2006.07.05210.1016/j.surfcoat.2006.07.052 ↗
61. 10.1016/j.surfcoat.2017.06.02710.1016/j.surfcoat.2017.06.027 ↗
62. 10.1016/j.corsci.2015.11.02910.1016/j.corsci.2015.11.029 ↗
63. 10.1016/j.cossms.2009.04.00110.1016/j.cossms.2009.04.001 ↗
64. 10.1021/am200394410.1021/am2003944 ↗
65. 10.1016/j.biomaterials.2015.02.09610.1016/j.biomaterials.2015.02.096 ↗
66. 10.1039/C5TB01319D10.1039/C5TB01319D ↗
67. 10.1016/j.actbio.2009.10.00710.1016/j.actbio.2009.10.007 ↗
68. 10.1016/j.matlet.2011.07.10910.1016/j.matlet.2011.07.109 ↗
69. 10.1021/nn300934k10.1021/nn300934k ↗