Stability and Rate Capability of Al Substituted Lithium-Rich High-Manganese Content Oxide Materials for Li-Ion Batteries

The structures, electrochemical properties and thermal stability of Al-substituted lithium-excess oxides, Li1.2Ni0.16 Mn0.56Co 0.08− y Al y O2 ( y = 0, 0.024, 0.048, 0.08), are reported, and compared to the stoichiometric compounds, LiNizMnzCo1−2zO2. A solid solution was found up to at least y = 0.06. Aluminum substitution improves the poor thermal stability while preserving the high energy density of lithium-excess oxides. However, these high manganese compositions are inferior to the lithium stoichiometric materials, LiNi z Mn z Co 1−2 z O2 ( z = 0.333, 0.4), in terms of both power and thermal stability.