Impact of Testing Method on Safety Assessment of Aged Li-Ion Cells: Part II – Aged Cells Without Li Plating

Understanding the safety profile of aged Li-ion batteries is essential for developing effective battery management and hazard mitigation strategies. However, most safety assessments have focused on fresh batteries, with just a few calorimetry studies on aged batteries with metal oxide positive electrodes. This study provides a broad assessment of commercial 18650-type Li-ion batteries with NCA, NMC, and LFP positive electrodes, both uncycled and aged under conditions that promoted solid electrolyte interphase (SEI) growth as the dominant degradation mechanism. The cells underwent mechanical (nail penetration, crush), electrical (overcharge, overdischarge), and thermal (accelerating rate calorimetry) abuse tests. Safety was rated on general characteristics such as mass loss, maximum temperature, and EUCAR (European Council for Automotive R&D) hazard level, as well as characteristics specific to individual abuse tests. Generally, aged cells with SEI growth exhibited similar or improved safety compared to uncycled cells, contrasting with our previous findings on NCA cells with Li plating as the dominant aging mechanism (Part I of this series). Yet, some tests and characteristics indicated reduced aged cell safety, such as earlier triggering of mechanical failure. These results emphasize the need to examine aged battery safety across diverse empirical techniques, degradation modes, and chemistries.