Copper Dissolution in Overdischarged Lithium-ion Cells: X-ray Photoelectron Spectroscopy and X-ray Absorption Fine Structure Analysis

Christopher E. Hendricks, Azzam N. Mansour, Daphne A. Fuentevilla, Gordon H. Waller, Jonathan K. Ko, Michael G. Pecht

Abstract

In some applications, such as military or back-up energy applications, lithium-ion batteries can undergo storage for multiple years without use. If the batteries are not properly maintained, the pack voltage can decrease over time due to cell self-discharge, battery management system power requirements, and parasitic loads. However, lithium-ion batteries have a recommended discharge voltage limit corresponding to a nominal 0% state of charge, and if discharged below this limit, they will experience an overdischarge condition which can lead to dissolution of the copper current collector and introduce potential safety and performance issues. This paper investigates the nature of copper dissolution in overdischarged lithium-ion batteries including the relative concentration and chemical state of the copper found in overdischarged batteries through characterization by X-ray photoelectron spectroscopy and X-ray absorption fine structure spectroscopy.
Source: crossref · Quality: baseline

Research context

OpenAlex topics: Advancements in Battery Materials · Advanced Battery Technologies Research · Extraction and Separation Processes

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (24)

Show source-provided references
1. Electrochemical stability of copper in lithium-ion battery electrolytes10.1149/1.1393619 ↗
2. Electrochemical stability of graphite-coated copper in lithium-ion battery electrolytes10.1149/1.1394007 ↗
3. Quantitation of the dissolution of battery-grade copper foils in lithium-ion battery electrolytes by flame atomic absorption spectroscopy10.1016/j.electacta.2003.09.022 ↗
4. Quantitation of the dissolution of the graphite-coated copper foil in lithium-ion battery electrolytes by flame absorption spectroscopy10.1016/j.electacta.2003.09.020 ↗
5. In situ temperature evolution and failure mechanisms of LiNi0.33Mn0.33Co0.33O2 cell under over-discharge conditions10.1149/2.0791810jes ↗
6. Elucidating copper dissolution phenomenon in li-ion cells under overdischarge extremes10.1149/2.0671809jes ↗
7. Failure investigations of LiFePO4 cells in over-discharge conditions10.1149/2.039306jes ↗
8. Lithium ion battery cells under abusive discharge conditions: electrode potential development and interactions between positive and negative electrode10.1016/j.jpowsour.2017.07.044 ↗
9. Mechanism of the entire overdischarge process and overdischarge-induced internal short circuit in lithium-ion batteries10.1038/srep30248 ↗
10. Effects of overdischarge on performance and thermal stability of a Li-ion cell10.1016/j.jpowsour.2006.03.043 ↗
11. Opportunities for near zero volt storage of lithium ion batteries10.1039/C6EE00836D ↗
12. Quantifying the impact of overdischarge on large-format lithium-ion cells10.1149/06920.0001ecst ↗
13. Copper dissolution investigations in large-format lithium-ion cells
14. Effect of overdischarge on swelling and recharge performance of lithium ion cells10.1002/cjoc.200890286 ↗
15. Gas generation mechanism due to electrolyte decomposition in commercial lithium-ion cell10.1016/S0378-7753(98)00234-1 ↗
16. Performance loss of lithium ion polymer batteries subjected to overcharge and overdischarge abuse
17. A general discussion of li-ion battery safety10.1149/2.F03122if ↗
18. ATHENA, ARTEMIS, HEPHAESTUS: data analysis for X-ray absorption spectroscopy using IFEFFIT10.1107/S0909049505012719 ↗
19. Structure of copper (II) hydroxide10.1107/S0108270190006230 ↗
20. Villars · 1985 · 1994310.1002/crat.2170221117 ↗
21. Decomposition of copper compounds in X-ray photoelectron spectrometers10.1366/0003702844555016 ↗
22. X-ray photoelectron studies on some oxides and hydroxides of cobalt, nickel, and copper10.1021/ac60363a034 ↗
23. The stability of CuO and Cu2O surfaces during argon sputtering studied by XPS and AES10.1016/0039-6028(85)90383-8 ↗
24. An XPS study of copper corrosion originated by formic acid vapour at 40% and 80% relative humidity10.1002/1521-4176(200109)52:9<667::AID-MACO667>3.0.CO;2-H ↗