Facile Preparation and Electrochemical Properties of V2O5-Graphene Composite Films as Free-Standing Cathodes for Rechargeable Lithium Batteries
Source abstract
Abstract
Free-standing, flexible V 2 O 5 -graphene composite films were prepared by simple filtration of aqueous dispersions of V 2 O 5 nanowires and graphene sheets. V 2 O 5 nanowires were preferentially oriented along the plane of the film as they were sandwiched between stacked graphene sheets in the composite film. The V 2 O 5 content in the composites was adjusted simply by varying the relative amount of the dispersions. Thermal annealing at 300°C increased the conductivity of the composite films. Due to their integrated structure and high flexibility, the composite films were directly usable as flexible electrodes. In binder-free, sandwich-type lithium battery cells, a composite film containing 75.8 wt% V 2 O 5 delivered discharge capacities of 283 mAh g −1 and 252 mAh g −1 at a current density of 50 mA g −1 during the first and 50 th cycles, respectively. Owing to its higher conductivity, a composite film containing 42.8 wt% V 2 O 5 delivered a discharge capacity of 189 mAh g −1 at 750 mA g −1 . The good performance resulted from the integrated structure of the V 2 O 5 network embedded in stratified graphene nanosheets, with V 2 O 5 as the Li + host and graphene nanosheets providing the electron pathway. These composite films are promising candidates for electrical energy storage applications that require flexible electrodes.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Advancements in Battery Materials · Supercapacitor Materials and Fabrication · Transition Metal Oxide Nanomaterials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (37)
Show source-provided references
1. 10.1002/adma.20070224210.1002/adma.200702242 ↗
2. 10.1016/j.electacta.2005.04.04510.1016/j.electacta.2005.04.045 ↗
3. 10.1021/cm900764n10.1021/cm900764n ↗
4. 10.1021/jp103704y10.1021/jp103704y ↗
5. 10.1016/j.carbon.2009.06.04510.1016/j.carbon.2009.06.045 ↗
6. 10.1016/j.elecom.2010.08.00810.1016/j.elecom.2010.08.008 ↗
7. 10.1016/j.elecom.2008.08.05110.1016/j.elecom.2008.08.051 ↗
8. 10.1021/jp106340310.1021/jp1063403 ↗
9. 10.1016/j.elecom.2010.12.00210.1016/j.elecom.2010.12.002 ↗
10. 10.1002/adma.20090428510.1002/adma.200904285 ↗
11. 10.1002/aenm.20110022110.1002/aenm.201100221 ↗
12. 10.1021/cr020731c10.1021/cr020731c ↗
13. 10.1149/1.142579110.1149/1.1425791 ↗
14. 10.1021/nl103343w10.1021/nl103343w ↗
15. 10.1016/j.materresbull.2011.09.02510.1016/j.materresbull.2011.09.025 ↗
16. 10.1021/jp049182010.1021/jp0491820 ↗
17. 10.1088/0022-3727/42/14/14540210.1088/0022-3727/42/14/145402 ↗
18. 10.1002/adma.20090358610.1002/adma.200903586 ↗
19. 10.1021/jp060904s10.1021/jp060904s ↗
20. 10.1021/ja991085a10.1021/ja991085a ↗
21. 10.1002/adfm.20050066210.1002/adfm.200500662 ↗
22. 10.1039/c1ee01353j10.1039/c1ee01353j ↗
23. 10.1039/c1ra00258a10.1039/c1ra00258a ↗
24. 10.1039/c1nr10879d10.1039/c1nr10879d ↗
25. 10.1039/c2cc16239c10.1039/c2cc16239c ↗
26. 10.1039/c0ee00640h10.1039/c0ee00640h ↗
27. 10.1021/ja01539a01710.1021/ja01539a017 ↗
28. 10.1021/jp903588710.1021/jp9035887 ↗
29. 10.1021/ja806499w10.1021/ja806499w ↗
30. van der Pauw · Philips Tech. Rev. · 1958 · 20 · 220
31. 10.1039/b917103g10.1039/b917103g ↗
32. 10.1016/j.carbon.2008.08.01310.1016/j.carbon.2008.08.013 ↗
33. 10.1007/BF0110742010.1007/BF01107420 ↗
34. 10.1016/j.cplett.2009.01.05010.1016/j.cplett.2009.01.050 ↗
35. 10.1021/cm100477v10.1021/cm100477v ↗
36. 10.1021/ma100572e10.1021/ma100572e ↗
37. Stauffer D. Aharony A. , Introduction to percolation theory. 2nd revised edition. (Taylor & Francis, London, 2003), p. 89.