Lithium Oxalate as Capacity and Cycle-Life Enhancer in LNMO/Graphite and LNMO/SiG Full Cells

In the present study, we explore the use of lithium oxalate as a "sacrificial salt" in combination with lithium nickel manganese spinel (LNMO) cathodes. By online electrochemical mass spectrometry (OEMS), we demonstrate that the oxidation of lithium oxalate to CO 2 (corresponding to 525 mAh/g) occurs quantitatively around 4.7 V vs. Li/Li + . LNMO/graphite cells containing 2.5 or 5 wt% lithium oxalate show an up to ∼11% higher initial discharge capacity and less capacity fade over 300 cycles (12% and 8% vs. 19%) compared to cells without lithium oxalate. In LNMO/SiG full-cells with an FEC-containing electrolyte solution, lithium oxalate leads to a better capacity retention (45% vs 20% after 250 cycles) and a higher coulombic efficiency throughout cycling (∼1%) compared to cells without lithium oxalate. When CO 2 from lithium oxalate oxidation is removed after formation, a similar capacity fading as in LNMO/SiG cells without lithium oxalate is observed. Hence, we attribute the improved cycling performance to the presence of CO 2 in the cells. Further analysis (e.g., FEC consumption by 19 F-NMR) indicate that CO 2 is an effective SEI-forming additive for SiG anodes, and that a combination of FEC and CO 2 has a synergistic effect on the lifetime of full-cells with SiG anodes.