Heat Treatment Degrading the Corrosion Resistance of Selective Laser Melted Ti-6Al-4V Alloy
Source abstract
Abstract
Ti-6Al-4V alloy produced by selective laser melting (SLM) was reported to exhibit an inferior corrosion resistance compared with the traditionally processed Grade 5 alloy, due to the formation of high-energy metastable α ' martensite with regard to α martensite. This work manipulates the transformation of α ' martensite to α martensite by heat-treatment in SLM-produced Ti-6Al-4V alloy and studies the effect on its corrosion behavior using electrochemical tests and microstructural analysis. The electrochemical results reveal that the heat-treated SLM-produced samples exhibit a higher corrosion rate than the as-received counterparts. The microstructural characterization results show that the acicular α ' martensite vanishes gradually, and a plate-shaped α phase and a lamellar α + β mixture continuously form with enhancing heat-treatment temperature, which increases the grain size. The relation between changes in grain size and corrosion resistance of SLM-produced Ti-6Al-4V has been discussed in detail.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Additive Manufacturing Materials and Processes · Welding Techniques and Residual Stresses · Titanium Alloys Microstructure and Properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (47)
Show source-provided references
1. 10.1016/j.actamat.2010.02.00410.1016/j.actamat.2010.02.004 ↗
2. 10.1002/adem.20150041910.1002/adem.201500419 ↗
3. 10.1007/s11661-011-0731-y10.1007/s11661-011-0731-y ↗
4. 10.1007/s11661-008-9557-710.1007/s11661-008-9557-7 ↗
5. 10.1016/j.jmbbm.2013.05.01110.1016/j.jmbbm.2013.05.011 ↗
6. 10.1016/j.matdes.2014.05.02110.1016/j.matdes.2014.05.021 ↗
7. 10.1016/j.msea.2013.11.03810.1016/j.msea.2013.11.038 ↗
8. 10.1016/j.scriptamat.2011.03.02410.1016/j.scriptamat.2011.03.024 ↗
9. 10.1016/j.electacta.2017.02.11210.1016/j.electacta.2017.02.112 ↗
10. 10.1016/j.cirp.2007.10.00410.1016/j.cirp.2007.10.004 ↗
11. 10.1016/j.jallcom.2015.11.14110.1016/j.jallcom.2015.11.141 ↗
12. 10.1016/j.matdes.2013.01.03810.1016/j.matdes.2013.01.038 ↗
13. 10.1016/j.actamat.2013.04.03610.1016/j.actamat.2013.04.036 ↗
14. 10.1016/j.jallcom.2012.07.02210.1016/j.jallcom.2012.07.022 ↗
15. 10.1007/s11740-009-0192-y10.1007/s11740-009-0192-y ↗
16. 10.1016/j.ijmachtools.2005.09.00510.1016/j.ijmachtools.2005.09.005 ↗
17. 10.1016/j.ijmachtools.2006.01.02410.1016/j.ijmachtools.2006.01.024 ↗
18. 10.1016/j.msea.2015.06.08810.1016/j.msea.2015.06.088 ↗
19. 10.1016/j.actamat.2016.04.02910.1016/j.actamat.2016.04.029 ↗
20. 10.1016/j.corsci.2013.08.00910.1016/j.corsci.2013.08.009 ↗
21. 10.1016/j.corsci.2009.06.01610.1016/j.corsci.2009.06.016 ↗
22. 10.1016/j.corsci.2009.06.03510.1016/j.corsci.2009.06.035 ↗
23. 10.1016/j.electacta.2006.04.05110.1016/j.electacta.2006.04.051 ↗
24. 10.1016/j.corsci.2011.11.00610.1016/j.corsci.2011.11.006 ↗
25. 10.1016/j.electacta.2006.06.01810.1016/j.electacta.2006.06.018 ↗
26. 10.1016/j.jmbbm.2013.05.01110.1016/j.jmbbm.2013.05.011 ↗
27. 10.1016/j.jallcom.2013.08.18310.1016/j.jallcom.2013.08.183 ↗
28. 10.1016/j.matdes.2016.05.07010.1016/j.matdes.2016.05.070 ↗
29. 10.1007/s11661-011-0731-y10.1007/s11661-011-0731-y ↗
30. 10.1016/j.corsci.2015.10.04110.1016/j.corsci.2015.10.041 ↗
31. 10.1016/j.corsci.2016.06.00910.1016/j.corsci.2016.06.009 ↗
32. 10.1016/j.jmbbm.2008.05.00410.1016/j.jmbbm.2008.05.004 ↗
33. 10.1016/j.biomaterials.2005.07.04110.1016/j.biomaterials.2005.07.041 ↗
34. 10.1016/j.jallcom.2016.02.18310.1016/j.jallcom.2016.02.183 ↗
35. 10.1007/s11706-015-0315-710.1007/s11706-015-0315-7 ↗
36. 10.1016/j.addma.2014.12.00810.1016/j.addma.2014.12.008 ↗
37. 10.1108/1355254081090797410.1108/13552540810907974 ↗
38. 10.1108/1355254101108337110.1108/13552541011083371 ↗
39. 10.1016/j.matdes.2004.10.01710.1016/j.matdes.2004.10.017 ↗
40. 10.1016/j.matdes.2015.03.02810.1016/j.matdes.2015.03.028 ↗
41. 10.1016/j.matdes.2016.02.09410.1016/j.matdes.2016.02.094 ↗
42. 10.1016/j.msec.2015.11.07210.1016/j.msec.2015.11.072 ↗
43. 10.1016/j.matdes.2010.09.00910.1016/j.matdes.2010.09.009 ↗
44. 10.1016/j.msec.2011.02.00510.1016/j.msec.2011.02.005 ↗
45. 10.1016/0010-938X(95)00065-R10.1016/0010-938X(95)00065-R ↗
46. 10.1016/j.msec.2013.01.06810.1016/j.msec.2013.01.068 ↗
47. 10.1016/j.electacta.2010.09.02310.1016/j.electacta.2010.09.023 ↗