Dielectric, mechanical and thermal properties of polymer/BaTiO3 composites for embedded capacitor

Abstract Barium titanate (BaTiO3) filled polymethylmethacrylate (PMMA) composites were prepared using the simple solution method followed by hot pressing. The content of BaTiO3 was varied from 0 to 65 vol.%. Scanning electron microscopy showed good dispersion and adhesion of BaTiO3 with the PMMA matrix. The dielectric constant of the composites increased significantly. There was weak dispersion in the dielectric constant of the composites (up to 45 vol.%) with frequency between 100 Hz and 15 MHz. The dissipation factor of the composites increased from 0.021 for pure PMMA to 0.029 for 45 vol.% composites. However, 65 vol.% composite showed dispersion in dielectric constant with increasing frequency and higher dissipation factor. The Lichtenecker equation agreed well with the experimental data. The microhardness and the glass transition temperature of the composites increased approximately 4.7-fold and 42 °C, respectively, compared to pure PMMA. The CTE of the 65 vol.% composite is close to that of copper.