SiC/SiCwoven fabric laminates: Design, manufacturing, mechanical properties
Source abstract
Abstract
Abstract The SiC/SiCwf laminate design has been targeted to achieve increased residual compressive stress in thin SiCwf layers and small residual tensile stress in thick SiC layers, that would lead to a significant increase of the apparent fracture toughness of the composite. The laminates have been manufactured using rolling and hot pressing techniques. The measured apparent fracture toughness of laminates showed a significant increase over the monolith SiC ceramics. Thus, while the intrinsic fracture toughness of pure SiC ceramics is in the range of 2–3 MPa m1/2, significant increase up to 6–8 MPa m1/2 was achieved for the layered ceramics. A crack shielding by compressive residual stress was a main mechanism responsible for the significant toughening of the SiC/SiCwf laminate.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Advanced ceramic materials synthesis · Aluminum Alloys Composites Properties · Advanced Surface Polishing Techniques
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (18)
Show source-provided references
1. Crack arrest in Si3N4-based layered composites with residual stress10.1016/j.compscitech.2004.02.007 ↗
2. Toughening of layered ceramic composites with residual surface compression: effect of layer thickness10.1016/S0013-7944(00)00096-5 ↗
3. Apparent fracture toughness in Si3N4-based laminates with residual compressive or tensile stresses in surface layers10.1016/j.actamat.2004.09.022 ↗
4. Materials properties determining the resistance of ceramics to high velocity penetration10.1063/1.342659 ↗
5. Mechanics of penetration and perforation10.1016/0020-7225(78)90066-6 ↗
6. Yaroshenko V, Orlovskaya N, Einarsrud M.-A, Kovylayev V. Processing of multilayered Si3N4–TiN hot-pressed ceramic composites. In: Proceedings of NATO ARW ‘multilayered and fibre-reinforced composites: problems and prospects’. Dordrecht, Kluwer; 1998.10.1007/978-94-007-0868-6_18 ↗
7. Orlovskaya N, Kuebler J, Subbotin V, Lugovy M. Design of Si3N4-based ceramic laminates by the residual stresses. J Mater Sci 2005;40:5443–50.10.1007/s10853-005-1918-7 ↗
8. Crack bifurcation features in laminar specimens with fixed total thickness10.1016/S0266-3538(02)00040-4 ↗
9. Laminar ceramics that exhibit a threshold strength10.1126/science.286.5437.102 ↗
10. Crack bifurcation in laminar ceramic composites10.1111/j.1151-2916.1996.tb08003.x ↗
11. Residual stresses in alumina–zirconia laminates10.1016/S0955-2219(99)00103-X ↗
12. Toughening of layered ceramic composites with residual surface compression10.1111/j.1151-2916.1996.tb07883.x ↗
13. Orlovskaya N, Lugovy M, Subbotin V, Radchenko A, Adams J, Chheda M, et al. Robust design and manufacturing of ceramic laminates with controlled thermal residual stresses for enhanced toughness. J Mater Sci 2005;40:5483–90.10.1007/s10853-005-1923-x ↗
14. Ceramic tool materials. Gnesin, Kiev GG, editors. Tekhnika; 1991 [in Russian].
15. Improvement of the mechanical properties of hot-pressed silicon–carbide–fiber-reinforced silicon carbide composites by polycarbosilane impregnation10.1016/S0266-3538(01)00031-8 ↗
16. Kuebler · Ceram Eng Sci Proc · 1997 · 18 · 15510.1002/9780470294444.ch18 ↗
17. Kuebler J. In: Jenkins MG, Quinn GD, editor. ASTM STP 1409, J.A. Salem. West Conshohocken, PA, ASTM, ISBN 0-8031-2880-0; 2002. p. 93.
18. Factors affecting threshold strength in laminar ceramics containing thin compressive layers10.1111/j.1151-2916.2002.tb00249.x ↗