Microtwinning in highly nonstoichiometric VO thin films

Abstract Both pulsed-DC biased and commercial ion-beam sputtered VO x thin films maintain a face-centered-cubic nanocrystalline phase, even for stoichiometries of x > 1.5, which is well outside the bulk equilibrium solubility range for cubic VO x . Many of these highly nonstoichiometric films exhibit a high density of microtwins, which give rise to unusual fine structure in the selected-area electron diffraction patterns, namely: an additional defect ring; a significant broadening of the {2 0 0} ring; pairs of parallel rod features which are tangent to the additional defect ring; and additional fine-structure features between the {2 0 0} and {2 2 0} rings. The formation of the microtwins is correlated with the coalescence of vanadium vacancies along the {1 1 1} twin planes in the crystalline lattice.