A mesoscale solidification simulation of fusion welding in aluminum–magnesium–silicon alloys
Source abstract
Abstract
Abstract A 3-D granular model has been developed to simulate solidification during fusion welding of Al alloys. The model simulates the gradual development of the weld mushy zone composed of both continuous liquid films and solidifying grains by coupling thermal fields based on the Rosenthal equation, a modified Voronoi tessellation to provide grain structure at the mesoscale, and the evolution of solid fraction within a grain based on the Scheil equation. The shape and geometry of the columnar and equiaxed grains within the weld pool has been characterized from experiments, and therefore the model can be used to link the solidification behaviour of individual grains to the macroscopic properties of the weld. The gradual formation of microscale liquid channels lying along the grain boundaries within the mushy zone is investigated and the role of welding parameters, including amperage and welding speed, on transitions in the semisolid microstructure is explored. The study reveals that the ability of the microscale liquid channels to feed molten metal into the solidifying areas is not uniform through the weld, and is strongly affected by grain size since smaller grains hinder the feeding ability of the mushy zone.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Aluminum Alloy Microstructure Properties · Aluminum Alloys Composites Properties · Advanced Welding Techniques Analysis
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (27)
Show source-provided references
1. Dye · Acta Mater · 2001 · 49 · 68310.1016/S1359-6454(00)00361-X ↗
2. Boettinger · Acta Mater · 2000 · 48 · 4310.1016/S1359-6454(99)00287-6 ↗
3. Vernède · Acta Mater · 2006 · 54 · 402310.1016/j.actamat.2006.04.035 ↗
4. Fallah · Acta Mater · 2012 · 60 · 163310.1016/j.actamat.2011.12.009 ↗
5. Montiel · Acta Mater · 2012 · 60 · 592510.1016/j.actamat.2012.07.035 ↗
6. Zhong · J Cryst Growth · 2009 · 311 · 477810.1016/j.jcrysgro.2008.11.047 ↗
7. Bordreuil · Comput Mater Sci · 2014 · 82 · 44210.1016/j.commatsci.2013.09.067 ↗
8. Vernède · Acta Mater · 2007 · 55 · 170310.1016/j.actamat.2006.10.031 ↗
9. Sistaninia · Acta Mater · 2012 · 60 · 390210.1016/j.actamat.2012.03.036 ↗
10. Sistaninia · Acta Mater · 2012 · 60 · 679310.1016/j.actamat.2012.08.057 ↗
11. Vernède · Philos Mag · 2006 · 86 · 377910.1080/14786430500228705 ↗
12. Phillion · Int J Cast Met Res · 2009 · 22 · 24010.1179/136404609X367849 ↗
13. Mathier · Modell Simul Mater Sci Eng · 2004 · 12 · 47910.1088/0965-0393/12/3/009 ↗
14. Phillion · Acta Mater · 2008 · 56 · 432810.1016/j.actamat.2008.04.055 ↗
15. Zaragoci Silva l · IOP C Ser Mater Sci Eng · 2012 · 33 · 01205410.1088/1757-899X/33/1/012054 ↗
16. Kou · 2003
17. Bonifaz · Acta Mater · 2009 · 57 · 178510.1016/j.actamat.2008.12.022 ↗
18. http://math.lbl.gov/voro++/doc/.
19. Brenner · 1994
20. Yan · Acta Mater · 2002 · 50 · 219910.1016/S1359-6454(01)00431-1 ↗
21. Wang · Acta Mater · 2010 · 58 · 541110.1016/j.actamat.2010.06.013 ↗
22. Clyne · Metall Trans A · 1981 · 12A · 96510.1007/BF02643477 ↗
23. Sistaninia · Acta Mater · 2013 · 61 · 383110.1016/j.actamat.2013.03.021 ↗
24. Vernède · Acta Mater · 2009 · 57 · 155410.1016/j.actamat.2008.12.006 ↗
25. Niel · Sci Technol Weld Joi · 2013 · 18 · 15410.1179/1362171812Y.0000000072 ↗
26. Coniglio · Int Mater Rev · 2013 · 58 · 37510.1179/1743280413Y.0000000020 ↗
27. Rappaz · Metall Mater Trans A · 1999 · 30A · 44910.1007/s11661-999-0334-z ↗