Formation ranges of icosahedral, amorphous and crystalline phases in rapidly solidified Ti–Zr–Hf–Ni alloys
Source abstract
Abstract
From the quaternary Ti-Zr-Hf-Ni phase diagram. the cross-section at 20 at % Ni was selected for investigation. The icosahedral quasicrystalline, crystalline and amorphous phases were observed to form in nine kinds of rapidly solidified (TixZryHfz)(80)Ni-20 (x + y + z = 1) alloys at different compositions. The quasilattice constants of 0.519 and 0.531 nm were obtained for the icosahedral phase formed in the melt-spun Ti40Zr20Hf20Ni20 and Ti20Zr40Hf20Ni20 alloys. respectively. The icosahedral phase formed in the melt-spun Ti40Zr20Hf20Ni20 alloy especially is thermodynamically stable. The supercooled liquid region of the Ti20Zr20Hf40Ni20 glassy alloy reached 64 K. From these results a comparison of quasicrystal-forming and glass-forming abilities, was carried out. The quasicrystal-forming ability was reduced and glass-forming ability was improved with an increase in Hf and Zr contents in the (TixZryHfz)(80)Ni-20 alloys. On the other hand. an increase in Ti content caused an improvement in quasicrystal-forming ability.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Quasicrystal Structures and Properties · Metallic Glasses and Amorphous Alloys · Mineralogy and Gemology Studies
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (28)
Show source-provided references
1. Shechtman · Phys Rev Lett · 1984 · 53 · 195110.1103/PhysRevLett.53.1951 ↗
2. Sainfort · C R Acad Sci Paris · 1985 · 10 · 689
3. Tsai · Jpn J Appl Phys · 1987 · 26 · L150510.1143/JJAP.26.L1505 ↗
4. Tsai · Jpn J Appl Phys · 1988 · 27 · L158710.1143/JJAP.27.L1587 ↗
5. Guo · Phil Mag Lett · 2002 · 82 · 34910.1080/09500830210135580 ↗
6. Guo · Phys Rev B · 2000 · 62 · 605
7. Koster · Appl Phys Lett · 1996 · 69 · 17910.1063/1.117364 ↗
8. Xing · Appl Phys Lett · 1998 · 73 · 211010.1063/1.122394 ↗
9. Inoue · J Mater Res · 2000 · 15 · 219510.1557/JMR.2000.0316 ↗
10. Louzguine · Appl Phys Lett · 2000 · 76 · 342410.1063/1.126667 ↗
11. Li · Appl Phys Lett · 2000 · 77 · 52810.1063/1.127033 ↗
12. Louzguine · Scripta Mater · 2003 · 48 · 132510.1016/S1359-6462(03)00018-6 ↗
13. Louzguine · J Alloys Comp · 2003 · 361 · 15310.1016/S0925-8388(03)00409-2 ↗
14. Kelton · Appl Phys Lett · 1997 · 70 · 323010.1063/1.119133 ↗
15. Polk · Acta Metall · 1978 · 26 · 109710.1016/0001-6160(78)90137-2 ↗
16. Aoki · Proc Int Conf Rapidly Quench Metals IV · 1981 · 2 · 1649
17. Buschow · J Appl Phys · 1979 · 50 · 634810.1063/1.325724 ↗
18. Kelton · J Non-Cryst Solids · 2002 · 312-214 · 30510.1016/S0022-3093(02)01691-5 ↗
19. Chebotnikov · Proc Ninth Conf Rapidly Quench Metastable Mater · 1997 · 414
20. Huett · Phil Mag Lett · 2002 · 82 · 19110.1080/09500830110121054 ↗
21. Elser · Phys Rev B · 1985 · 32 · 489210.1103/PhysRevB.32.4892 ↗
22. Altounian · J Appl Phys · 1987 · 61 · 14910.1063/1.338847 ↗
23. Brandes · 1992 · 11
24. Louzguine · Scripta Mater · 2004 · 50 · 97310.1016/j.scriptamat.2004.01.005 ↗
25. Saida · Mat Trans · 2001 · 42-8 · 149710.2320/matertrans.42.1497 ↗
26. Saida · Mat Trans · 2003 · 44-10 · 197110.2320/matertrans.44.1971 ↗
27. Basu · Mat Res Soc Symp Proc · 2003 · 754 · CC12.6.1
28. Takeuchi · Mater Trans JIM · 2000 · 41 · 137210.2320/matertrans1989.41.1372 ↗