SiC single fibre full-fragmentation during straining in a Ti–6Al–4V matrix studied by synchrotron X-rays
Source abstract
Abstract
High spatial resolution synchrotron X-ray strain measurements and radiography/tomography have been combined to study the progressive fragmentation process during a single fibre full-fragmentation test. In this manner it has been possible to observe the fragmentation sequence and to determine the interfacial shear stress as a function of position along the fibre. The SCS-6 fibre failed after it was elastically strained locally to 1.5%. The interfacial frictional shear strength inferred from the longitudinal strain profile of the broken fibre was calculated to be around 200 MPa, whereas a conventional post mortem full fragmentation analysis based on the mean fragment length would have incorrectly given a value of ~700 MPa. This is due to the degradation of the fibre strength after the initial fibre fracture event. After failure, interface sliding was observed along considerable lengths of the fibre matrix interface. Upon unloading some reverse frictional sliding was found to take place. The morphology of the fibre cracks as well as the occurrence of matrix cracks as the sample approaches saturation fragmentation were also determined from radiographic and tomographic images. © 2002 Acta Materialia Inc. Published by Elsevier Science B.V. All rights reserved.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Aluminum Alloys Composites Properties · Advanced ceramic materials synthesis · Microstructure and mechanical properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (31)
Show source-provided references
1. Clyne · 1993 · 470
2. Hooker · Mater. Sci. Tech. · 2000 · 16 · 72510.1179/026708300101508414 ↗
3. Majumbar · 1997 · 113
4. Rauchs G, Thomason PF, Withers PJ. Int J Fracture, submitted for publication.
5. Yang · Scripta metall. mater. · 1990 · 24 · 46910.1016/0956-716X(90)90184-I ↗
6. Kieschke · 1990 · 325
7. Le Petitcorps · Compos. Sci. Technol · 1989 · 35 · 20710.1016/0266-3538(89)90096-1 ↗
8. Clyne · 1993 · 180
9. Huang · Compos. Sci. Tech. · 1994 · 52 · 50510.1016/0266-3538(94)90033-7 ↗
10. Ward-Close · J. Mater. Sci. · 1990 · 25 · 431510.1007/BF00581090 ↗
11. Maire E, Cloetens P., Lormand G., Fougères R10.1016/S1359-6454(99)00024-5 ↗
12. Cloetens · J. Appl. Phys. · 1997 · 81 · 587810.1063/1.364374 ↗
13. Piggott · 1980
14. Desaeger · Compos. Sci. Technol. · 1992 · 43 · 37910.1016/0266-3538(92)90061-7 ↗
15. Young · Compos. Sci. Technol. · 1995 · 53 · 41110.1016/0266-3538(95)00030-5 ↗
16. Kelly · J. Mech. Phys. Solids · 1965 · 13 · 32910.1016/0022-5096(65)90035-9 ↗
17. Oshawa · J. Appl. Polym. Sci. · 1978 · 2 · 3203
18. Pang JWL. Private communication. Manchester Materials Science Centre, University of Manchester & UMIST, Grosvenor St., Manchester Ml 7HS.
19. Maire · Acta mater. · 2001 · 49 · 15310.1016/S1359-6454(00)00218-4 ↗
20. Withers · Acta mater. · 1998 · 46 · 658510.1016/S1359-6454(98)00297-3 ↗
21. Nye · 1985
22. Noyan · 1987
23. Laffargue J, Bowen P. IRC in materials for high performance applications. Private communication. School of Metallurgy and Materials, University of Birmingham, Birmingham BI5 2TT; 2001.
24. Intergranular stresses in Zircaloy-2 with rod texture10.1016/S1359-6454(98)00385-1 ↗
25. Bache · Mater. Sci. Eng. A · 1998 · 257 · 13910.1016/S0921-5093(98)00832-6 ↗
26. International Conference MECA–SENS: Stress Evaluation by Neutron and Synchrotron Radiation, 2000; Reims10.1080/10238160108200165 ↗
27. Majumdar · Compos. B: Eng · 1998 · 29 · 13110.1016/S1359-8368(97)00004-8 ↗
28. Rauchs G, Preuss M, Withers PJ. Acta mater., in press.
29. Blackburn · Trans. ASM · 1969 · 62 · 398
30. Bennett · Compos. A: Appl. Sci. Manuf · 1998 · 29 · 107110.1016/S1359-835X(98)00045-1 ↗
31. McDonald S, Preuss M, Maire E, Buffiere J-Y, Mummery PM, Withers PJ. Mater Sci Tech, in press.