Facet and energy predictions in grain boundaries: Lattice matching and molecular dynamics

Many material properties can be traced back to properties of their grain boundaries. Grain boundary energy (GBE), as a result, is a key quantity of interest in the analysis and modeling of microstructure. A standard method for calculating grain boundary energy is molecular dynamics (MD); however, on-the-fly MD calculations are not tenable due to the extensive computational time required. Lattice matching (LM) is a reduced-order method for estimating GBE quickly; however, it has only been tested against a relatively limited set of data, and does not have a suitable means for assessing error. In this work, we use the recently published dataset of Homer et al. [1] to assess the performance of LM over the full range of GB space, and to equip LM with a metric for error estimation. LM is used to generate energy estimates, along with predictions of facet morphology, for each of the 7,304 boundaries in the Homer dataset. In keeping with prior work, it is observed that LM predictions of low energy boundaries matches well with MD results. Moreover, there is a good general agreement between LM and MD, and it is apparent that the error scales approximately linearly with the predicted energy value; this makes it possible to establish an empirical estimate on error for future LM calculations. An essential part of the LM method is the faceting relaxation, which corrects the expected energy by convexification across the compact space (S2) of boundary plane orientations. The original Homer dataset did not allow for faceting, but upon extended annealing, it was shown that facet patterns similar to those predicted by LM were emerging.