The three-dimensional structure of flexible resorcinol-formaldehyde aerogels investigated by means of holotomography
Source abstract
Abstract
Organic aerogels based on resorcinol-formaldehyde gels display remarkable properties due to their pronounced nanoporosity. Therefore, studies towards the understanding of their structure-property-relationship are of high value for the design of improved materials. X-ray tomography is a technique that has been used for the structural elucidation of porous materials, but so far no highly resolved three-dimensional structures of resorcinol-formaldehyde gels have been obtained under the classical absorption-based experimental X-ray setup. This paper reports on the successful analysis of a superflexible resorcinol-formaldehyde aerogel using zoom holotomography that yielded images with an unprecedented resolution in the sub-micrometer range. The preparation of suitable powder from monolithic superflexible resorcinol-formaldehyde, the experimental conditions for tomography, and data-processing to obtain a 3D-image of the dried gel sample are described. Macropores above ca. 75 nm could be identified and visualized. They were shown to adopt almost spherical shape and to display a low connectivity. A quantitative analysis of the pore space revealed that most of the identified pores are small macropores (diameter < 0.5 µm), yet most pore volume is located in larger macropores of 1–4 µm diameter.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Aerogels and thermal insulation · Mesoporous Materials and Catalysis · Catalysis and Oxidation Reactions
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (39)
Show source-provided references
1. Aegerter MA, Leventis N, Koebel MM (eds) (2011) Aerogels handbook. Springer, New York, NY
2. Lu X, Arduini-Schuster MC, Kuhn J, Nilsson O, Fricke J, Pekala RW (1992) Thermal conductivity of monolithic organic aerogels. Science 255(5047):971–97210.1126/science.255.5047.971 ↗
3. Pekala RW, Alviso CT, LeMay JD (1990) Organic aerogels: microstructural dependence of mechanical properties in compression. J Non Cryst Solids 125(1–2):67–7510.1016/0022-3093(90)90324-F ↗
4. Lu X, Caps R, Fricke J, Alviso CT, Pekala RW (1995) Correlation between structure and thermal conductivity of organic aerogels. J Non Cryst Solids 188(3):226–23410.1016/0022-3093(95)00191-3 ↗
5. Reichenauer G (2011) Structural characterization of aerogels. In: Aegerter MA, Leventis N, Koebel MM (eds) Aerogels handbook. Springer, New York, NY, p 449–49810.1007/978-1-4419-7589-8_21 ↗
6. Barrett EP, Joyner LG, Halenda PP (1951) The determination of pore volume and area distributions in porous substances. I. computations from nitrogen isotherms. J Am Chem Soc 73(1):373–38010.1021/ja01145a126 ↗
7. Fu B, Luo H, Wang F, Churu G, Chu KT, Hanan JC, Sotiriou-Leventis C, Leventis N, Lu H (2011) Simulation of the microstructural evolution of a polymer crosslinked templated silica aerogel under high-strain-rate compression. J Non Cryst Solids 357(10):2063–207410.1016/j.jnoncrysol.2011.02.049 ↗
8. Rege A, Schestakow M, Karadagli I, Ratke L, Itskov M (2016) Micro-mechanical modelling of cellulose aerogels from molten salt hydrates. Soft Matter 12(34):7079–708810.1039/C6SM01460G ↗
9. Reichenauer G, Scherer GW (2000) Nitrogen adsorption in compliant materials. J Non Cryst Solids 277(2–3):162–17210.1016/S0022-3093(00)00304-5 ↗
10. Landers J, Gor GY, Neimark AV (2013) Density functional theory methods for characterization of porous materials. Colloids Surf A 437:3–3210.1016/j.colsurfa.2013.01.007 ↗
11. Giesche H (2006) Mercury porosimetry: a general (practical) overview. Part Part Syst Charact 23(1):9–1910.1002/ppsc.200601009 ↗
12. Johnston GP, Smith DM, Melendez I, Hurd AJ (1990) Compression effects in mercury porosimetry. Powder Technol 61(3):289–29410.1016/0032-5910(90)80093-E ↗
13. Scherer GW, Smith DM, Stein D (1995) Deformation of aerogels during characterization. J Non Cryst Solids 186:309–31510.1016/0022-3093(95)00058-5 ↗
14. Holzer L, Indutnyi F, Gasser PH, Münch B, Wegmann M (2004) Three-dimensional analysis of porous BaTiO3 ceramics using FIB nanotomography. J Microsc 216(1):84–9510.1111/j.0022-2720.2004.01397.x ↗
15. Wilson JR, Kobsiriphat W, Mendoza R, Chen H-Y, Hiller JM, Miller DJ, Thornton K, Voorhees PW, Adler SB, Barnett SA (2006) Three-dimensional reconstruction of a solid-oxide fuel-cell anode. Nat Mater 5(7):541–54410.1038/nmat1668 ↗
16. Ziegler C, Thiele S, Zengerle R (2011) Direct three-dimensional reconstruction of a nanoporous catalyst layer for a polymer electrolyte fuel cell. J Power Sources 196(4):2094–209710.1016/j.jpowsour.2010.09.044 ↗
17. Balach J, Miguel F, Soldera F, Acevedo DF, Mücklich F, Barbero CA (2012) A direct and quantitative image of the internal nanostructure of nonordered porous monolithic carbon using FIB nanotomography. J Microsc 246(3):274–27810.1111/j.1365-2818.2012.03615.x ↗
18. Balach J, Soldera F, Acevedo DF, Mücklich F, Barbero CA (2013) A direct and quantitative three-dimensional reconstruction of the internal structure of disordered mesoporous carbon with tailored pore size. Microsc Microanal 19(3):745–75010.1017/S1431927613000238 ↗
19. Maire E (2012) X-ray tomography applied to the characterization of highly porous materials. Annu Rev Mater Res 42(1):163–17810.1146/annurev-matsci-070511-155106 ↗
20. Haghgoo M, Plougonven E, Yousefi AA, Pirard J-P, Léonard A, Job N (2012) Use of X-ray microtomography to study the homogeneity of carbon nanotube aqueous suspensions and carbon nanotube/polymer composites. Carbon 50(4):1703–170610.1016/j.carbon.2011.11.031 ↗
21. Laskowski J (2016) Synthese und eigenschaften von Aerogel-Aerogel-Verbundwerkstoffen. Dissertation, Rheinisch-Westfälische Technische Hochschule Aachen
22. Mokso R, Cloetens P, Maire E, Ludwig W, Buffière J-Y (2007) Nanoscale zoom tomography with hard x rays using Kirkpatrick-Baez optics. Appl Phys Lett 90(14):14410410.1063/1.2719653 ↗
23. Kenesei P, Biermann H, Borbély A (2005) Structure–property relationship in particle reinforced metal–matrix composites based on holotomography. Scr Mater 53(7):787–79110.1016/j.scriptamat.2005.06.015 ↗
24. Girardin E, Renghini C, Dyson J, Calbucci V, Moroncini F, Albertini G (2011) Characterization of porosity in a laser sintered MMCp using X-ray synchrotron phase contrast microtomography. Mater Sci Appl 2:1322–1330
25. Sar J, Celikbilek O, Villanova J, Dessemond L, Martin CL, Djurado E (2015) Three dimensional analysis of Ce0.9Gd0.1O1.95–La0.6Sr0.4Co0.2Fe0.8O3−δ oxygen electrode for solid oxide cells. J Eur Ceram Soc 35(16):4497–450510.1016/j.jeurceramsoc.2015.08.019 ↗
26. Hubert M, Laurencin J, Cloetens P, da Silva JC, Lefebvre-Joud F, Bleuet P, Nakajo A, Siebert E (2016) Role of microstructure on electrode operating mechanisms for mixed ionic electronic conductors: from synchrotron-based 3D reconstruction to electrochemical modeling. Solid State Ion 294:90–10710.1016/j.ssi.2016.07.001 ↗
27. Cloetens P, Mache R, Schlenker M, Lerbs-Mache S (2006) Quantitative phase tomography of arabidopsis seeds reveals intercellular void network. Proc Natl Acad Sci USA 103(39):14626–1463010.1073/pnas.0603490103 ↗
28. Schwan M, Tannert R, Ratke L (2016) New soft and spongy resorcinol–formaldehyde aerogels. J Supercrit Fluids 107:201–20810.1016/j.supflu.2015.09.010 ↗
29. Pekala RW, Kong FM (1989) A Synthetic route to organic aerogels - mechanism, structure, and properties. J Phys 50(C-4):C433–C440
30. Brunauer S, Emmett PH, Teller E (1938) Adsorption of gases in multimolecular layers. J Am Chem Soc 60(2):309–31910.1021/ja01269a023 ↗
31. Heyn E (1903) Short reports from the metallurgical laboratory of the royal mechanical and testing institute of Charlottenburg. Metallographist 6:39–70
32. Zabler S, Cloetens P, Guigay J-P, Baruchel J, Schlenker M (2005) Optimization of phase contrast imaging using hard x rays. Rev Sci Instrum 76(7):07370510.1063/1.1960797 ↗
33. Labiche J-C, Mathon O, Pascarelli S, Newton MA, Ferre GG, Curfs C, Vaughan G, Homs A, Carreiras DF (2007) Invited article: the fast readout low noise camera as a versatile x-ray detector for time resolved dispersive extended x-ray absorption fine structure and diffraction studies of dynamic problems in materials science, chemistry, and catalysis. Rev Sci Instrum 78(9):09130110.1063/1.2783112 ↗
34. Cloetens P, Ludwig W, Baruchel J, Van Dyck D, Van Landuyt J, Guigay JP, Schlenker M (1999) Holotomography: Quantitative phase tomography with micrometer resolution using hard synchrotron radiation x rays. Appl Phys Lett 75(19):2912–291410.1063/1.125225 ↗
35. Bracewell RN, Riddle AC (1967) Inversion of fan-beam scans in radio astronomy. Astron J 150(2):427–43410.1086/149346 ↗
36. Piedboeuf M-LC, Léonard AF, Traina K, Job N (2015) Influence of the textural parameters of resorcinol–formaldehyde dry polymers and carbon xerogels on particle sizes upon mechanical milling. Colloids Surf A 471:124–13210.1016/j.colsurfa.2015.02.014 ↗
37. Tannert R, Schwan M, Ratke L (2015) Reduction of shrinkage and brittleness for resorcinol-formaldehyde aerogels by means of a pH-controlled sol–gel process. J Supercrit Fluids 106:57–6110.1016/j.supflu.2015.06.021 ↗
38. Moreno-Castilla C, Carrasco-Marín F, Dawidziuk M (2012) Carbon aerogel-supported Pt catalysts for the hydrogenolysis and isomerization of n-Butane: influence of the carbonization temperature of the support and Pt particle size. Catalysts 2(4):42210.3390/catal2040422 ↗
39. Wickenheisser M, Herbst A, Tannert R, Milow B, Janiak C (2015) Hierarchical MOF-xerogel monolith composites from embedding MIL-100(Fe,Cr) and MIL-101(Cr) in resorcinol-formaldehyde xerogels for water adsorption applications. Microporous Mesoporous Mater 215:143–15310.1016/j.micromeso.2015.05.017 ↗