Thermoplasticity of sol–gel-derived titanoxanes chemically modified with benzoylacetone

Titanium tetra-n-butoxide was hydrolyzed in the presence of benzoylacetone (BzAc), and the solution obtained was concentrated and served for spin-coating or dropping on substrates, followed by successive drying at 120, 200 and 250 °C. The dried products were transparent and amorphous, and the infrared absorption and Raman spectroscopic studies showed that BzAc forms chelate rings. Thermomechanical analysis showed that the 120 and 200 °C-dried products showed steep, thermoplastic shrinkage at around 30 and 70–85 °C, respectively, whereas the 250 °C-dried product did not show thermoplasticity. Thus as the drying temperature was increased, the thermoplasticity appeared at a higher temperature and finally disappeared. These changes in thermoplasticity with drying temperature were concluded to result from the progress of condensation between titanoxane polymers and/or clusters, which was evidenced in gel permeation chromatographic analysis.