Chromium(III)-substituted hydroxyapatite/silica sol–gel coating: towards novel green coating for corrosion protection of AA2024
Source abstract
Abstract
Abstract A novel Cr-substituted hydroxyapatite (Cr-HA) nanoparticles were synthesized via continuous hydrothermal technique. Moreover, the synthesized material was embedded into a silica sol–gel matrix and applied on an AA2024 substrate to evaluate the corrosion inhibition efficiency of the coating. TEM and SEM micrographs confirmed the development of Cr-HA nanorods of 20 nm width and 6 µm length. XRD diffractograms demonstrated the evolution of a new crystalline structure; the XRD pattern was analyzed by Material Studio software which confirms the replacement of Ca2+ by Cr3+. The EDX mapping revealed a uniform distribution of Ca and Cr ions within the Cr-HA crystal structure. The atomic ratio of Ca2+: Cr3+ was reported to be 4:1 respectively. The Cr-HA nanoparticles were uniformly distributed in a silica sol–gel matrix and applied on an AA2024 substrate. The corrosion performance of the Cr-HA sol–gel coating composite was evaluated using Electrochemical Impedance Spectroscopy (EIS) in an aerated 3.5% NaCl solution and the results compared to those of neat silica sol–gel coating. Whereas pitting corrosion was also observed in the case of a neat sol–gel coated sample within 5 days of immersion, Cr-HA sol–gel coated AA2024 exhibited prolonged pitting resistance over 110 days with no sign of corrosion or delamination. The EIS data fitting suggested the formation of a protective layer that is responsible for the extended corrosion resistance of the Cr-HA-coated sample. The scratch test indicated that the Cr-HA nanocomposite coating might offer short-term self-healing properties in the 3.5% NaCl corrosive media. Graphical Abstract
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Corrosion Behavior and Inhibition · Bone Tissue Engineering Materials · Magnesium Alloys: Properties and Applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (100+)
Show source-provided references
1. Ely M et al. (2017) Role of post-treatment in improved corrosion behavior of trivalent chromium protection (TCP) coating deposited on aluminum alloy 2024-T3. J Electrochem Soc 164(6):C27610.1149/2.0431706jes ↗
2. Hegde M et al. (2022) Abrasion and cavitation erosion resistance of multi-layer dip coated sol-gel coatings on AA2024-T3. Corros Mater Degrad 3(4):661–67110.3390/cmd3040036 ↗
3. Merisalu M et al. (2021) Effective corrosion protection of aluminum alloy AA2024-T3 with novel thin nanostructured oxide coating. Surf Coat Technol 411:12699310.1016/j.surfcoat.2021.126993 ↗
4. Nardeli JV et al. (2020) Novel healing coatings based on natural-derived polyurethane modified with tannins for corrosion protection of AA2024-T3. Corros Sci 162:10821310.1016/j.corsci.2019.108213 ↗
5. Yang Z et al. (2023) A multifunctional Sr (HQ) 2 filler-reinforced coating for self-healing and physical barrier properties on aluminum alloy. Prog Org Coat 180:10756710.1016/j.porgcoat.2023.107567 ↗
6. Nardeli JV et al. (2019) Tannin: a natural corrosion inhibitor for aluminum alloys. Prog Org Coat 135:368–38110.1016/j.porgcoat.2019.05.035 ↗
7. Nardeli JV et al. (2021) Biobased self-healing polyurethane coating with Zn micro-flakes for corrosion protection of AA7475. Chem Eng J 404:12647810.1016/j.cej.2020.126478 ↗
8. Mohammadi I et al. (2022) Construction of an epoxy coating with excellent protection performance on the AA 2024-T3 using ion-exchange materials loaded with eco-friendly corrosion inhibitors. Prog Org Coat 166:10678610.1016/j.porgcoat.2022.106786 ↗
9. Klumpp RE et al. (2022) A cerium-based nanocoating for corrosion protection of the AA1230 as clad material for the AA2024-T3 alloy. Mater Res. 25:9.10.1590/1980-5373-mr-2021-0616 ↗
10. Kamaraj K et al. (2012) Electropolymerised polyaniline films as effective replacement of carcinogenic chromate treatments for corrosion protection of aluminium alloys. Synth Met 162(5-6):536–54210.1016/j.synthmet.2012.01.022 ↗
11. Subasri R et al. (2019) Environmentally friendly Zn–Al layered double hydroxide (LDH)-based sol–gel corrosion protection coatings on AA 2024-T3. J Coat Technol Res 16(5):1447–146310.1007/s11998-019-00229-y ↗
12. Visser P, Terryn H, Mol JM (2018) On the importance of irreversibility of corrosion inhibitors for active coating protection of AA2024-T3. Corros Sci 140:272–28510.1016/j.corsci.2018.05.037 ↗
13. Lakshmi RV, Sampath S, Aruna ST (2021) Silica-alumina based sol-gel coating containing cerium oxide nanofibers as a potent alternative to conversion coating for AA2024 alloy. Surf Coat Technol 411:12700710.1016/j.surfcoat.2021.127007 ↗
14. Thai TT, Trinh AT, Olivier M-G (2020) Hybrid sol–gel coatings doped with cerium nanocontainers for active corrosion protection of AA2024. Prog Org Coat 138:10542810.1016/j.porgcoat.2019.105428 ↗
15. Xue B et al. (2017) Corrosion protection of AA2024-T3 by sol-gel film modified with graphene oxide. J Alloy Compd 725:84–9510.1016/j.jallcom.2017.05.091 ↗
16. Voevodin NN, Kurdziel JW, Mantz R (2006) Corrosion protection for aerospace aluminum alloys by Modified Self-assembled NAnophase Particle (MSNAP) sol–gel. Surf Coat Technol 201(3):1080–108410.1016/j.surfcoat.2006.01.028 ↗
17. Chaoshuai L et al. (2021) High nanopore volume tetrethoxysilane based aerogels prepared with addition of N, N-dimethylformamide at different stage of the sol-gel process. Mater Sci 27(3):330–333
18. Pirzada T et al. (2020) Cellulose silica hybrid nanofiber aerogels: from sol–gel electrospun nanofibers to multifunctional aerogels. Adv Funct Mater 30(5):190735910.1002/adfm.201907359 ↗
19. Styskalik A et al. (2020) Highly porous hybrid metallosilicate materials prepared by non-hydrolytic sol-gel: Hydrothermal stability and catalytic properties in ethanol dehydration. Microporous Mesoporous Mater 297:11002810.1016/j.micromeso.2020.110028 ↗
20. Poberžnik M et al. (2018) Insight into the bonding of silanols to oxidized aluminum surfaces. J Phys Chem C 122(17):9417–943110.1021/acs.jpcc.7b12552 ↗
21. Poberžnik M, Kokalj A (2019) Implausibility of bidentate bonding of the silanol headgroup to oxidized aluminum surfaces. Appl Surf Sci 492:909–91810.1016/j.apsusc.2019.04.032 ↗
22. Rodič P et al. (2018) Corrosion behaviour and chemical stability of transparent hybrid sol-gel coatings deposited on aluminium in acidic and alkaline solutions. Prog Org Coat 124:286–29510.1016/j.porgcoat.2018.02.025 ↗
23. Harb SV et al. (2016) A comparative study on graphene oxide and carbon nanotube reinforcement of PMMA-siloxane-silica anticorrosive coatings. ACS Appl Mater Interfaces 8(25):16339–1635010.1021/acsami.6b04780 ↗
24. Harb SV et al. (2015) Siloxane–PMMA hybrid anti-corrosion coatings reinforced by lignin. Surf Coat Technol 275:9–1610.1016/j.surfcoat.2015.05.002 ↗
25. Afsharimani N et al. (2020) Hybrid sol–gel silica coatings containing graphene nanosheets for improving the corrosion protection of aa2024-t3. Nanomaterials 10(6):105010.3390/nano10061050 ↗
26. Jafari-Tarzanagh Y et al. (2022) Active corrosion protection of AA2024 aluminum alloy by sol-gel coating containing inhibitor-loaded mesoporous SBA-15. Prog Org Coat 173:10716610.1016/j.porgcoat.2022.107166 ↗
27. Gautam A et al. (2022) Capped inhibitor-loaded halloysite nanoclay-based self-healing silica coatings for corrosion protection of mild steel. Ceram Int 48(20):30151–3016310.1016/j.ceramint.2022.06.288 ↗
28. Suárez-Vega A et al. (2021) Properties of hybrid sol-gel coatings with the incorporation of lanthanum 4-hydroxy cinnamate as corrosion inhibitor on carbon steel with different surface finishes. Appl Surf Sci 561:14988110.1016/j.apsusc.2021.149881 ↗
29. Mohammadpour Z, Zare HR (2021) The role of embedded 2-ABT@Cu-BTC MOF on the anti-corrosion performance of electro-assisted deposited silica sol-gel composite film. Mater Chem Phys 267:12459010.1016/j.matchemphys.2021.124590 ↗
30. Lakshmi RV, Aruna ST, Sampath S (2017) Ceria nanoparticles vis-à-vis cerium nitrate as corrosion inhibitors for silica-alumina hybrid sol-gel coating. Appl Surf Sci 393:397–40410.1016/j.apsusc.2016.10.035 ↗
31. Gobara M et al. (2018) Novel smart hydroxyapatite/silica sol–gel nanocomposite hybrid coating for corrosion protection of AA2024. J Inorg Organomet Polym Mater 28(4):1598–160810.1007/s10904-018-0790-2 ↗
32. Nenen A et al. (2022) Synthesis of antibacterial silver and zinc doped nano-hydroxyapatite with potential in bone tissue engineering applications. Ceram Int 48(23, Part A):34750–3475910.1016/j.ceramint.2022.08.064 ↗
33. Hartati YW et al. (2022) Recent advances in hydroxyapatite-based electrochemical biosensors: applications and future perspectives. Sens Bio Sens Res 38:10054210.1016/j.sbsr.2022.100542 ↗
34. Firdaus Hussin MS et al. (2022) Extraction of natural hydroxyapatite for biomedical applications—a review. Heliyon 8(8):e1035610.1016/j.heliyon.2022.e10356 ↗
35. El-Morsy MA et al. (2022) Mixed systems of hydroxyapatite Gallium oxide (Ga2O3)/Graphene oxide for medical applications: antibacterial, mechanical and morphology. Surf Interfaces 35:10246110.1016/j.surfin.2022.102461 ↗
36. Li Q et al. (2022) Continuous hydrothermal flow synthesis and characterization of ZrO2 nanoparticles doped with CeO2 in supercritical water. Nanomaterials 12(4):66810.3390/nano12040668 ↗
37. Sierra-Pallares J et al. (2016) Understanding bottom-up continuous hydrothermal synthesis of nanoparticles using empirical measurement and computational simulation. Nano Res 9:3377–338710.1007/s12274-016-1215-6 ↗
38. Darr JA et al. (2017) Continuous hydrothermal synthesis of inorganic nanoparticles: applications and future directions. Chem Rev 117(17):11125–1123810.1021/acs.chemrev.6b00417 ↗
39. Santiago E et al. (2022) Hydrothermal synthesis of fluorapatite coatings over titanium implants for enhanced osseointegration—an in vivo study in the rabbit. J Funct Biomater 13(4):24110.3390/jfb13040241 ↗
40. Jiantao Q et al. (2018) Effect of an Fe (II)-modified trivalent chromium conversion process on Cr (VI) formation during coating of AA 2024 alloy. Electrochem Commun 92:1–410.1016/j.elecom.2018.05.013 ↗
41. Proença CS et al. (2019) Trivalent chromium conversion coating on AA2024‐T3 used in aeronautical and aerospace industry. Surf Interface Anal 51(12):1298–131110.1002/sia.6653 ↗
42. Qi J et al. (2021) Formation of a trivalent chromium conversion coating on AZ91D magnesium alloy. Corros Sci 186:10945910.1016/j.corsci.2021.109459 ↗
43. Nickerson W, Matzdorf C (2012) Non-chromate aluminum pretreatments. Naval Air Systems Command Patuxent River, MD10.21236/ADA582070 ↗
44. Mitton DB et al. (2017) Selected Cr (VI) replacement options for aluminum alloys: a literature survey. Corros Rev 35(6):365–38110.1515/corrrev-2016-0059 ↗
45. Bouali AC et al. (2020) Layered double hydroxides (LDHs) as functional materials for the corrosion protection of aluminum alloys: A review. Appl Mater Today 21:10085710.1016/j.apmt.2020.100857 ↗
46. Kwok CT et al. (2009) Characterization and corrosion behavior of hydroxyapatite coatings on Ti6Al4V fabricated by electrophoretic deposition. Appl Surf Sci 255(13-14):6736–674410.1016/j.apsusc.2009.02.086 ↗
47. Hiromoto S, Yamamoto A (2009) High corrosion resistance of magnesium coated with hydroxyapatite directly synthesized in an aqueous solution. Electrochim Acta 54(27):7085–709310.1016/j.electacta.2009.07.033 ↗
48. Zoriany MY et al. (2020) Optimized silica-based hybrid coatings for the protection of aluminum against chloride-rich environment. J Sol-Gel Sci Technol 94:257–26910.1007/s10971-020-05227-w ↗
49. Wu X et al. (2013) Crystal structure determination of three polycyclic compounds and comparative Rietveld refinement between MS and GSAS programs. Chin Sci Bull 58(20):2430–243410.1007/s11434-013-5837-8 ↗
50. Altomare A et al. (2015) QUALX2. 0: a qualitative phase analysis software using the freely available database POW_COD. J Appl Crystallogr 48(2):598–60310.1107/S1600576715002319 ↗
51. Vaitkus A, Merkys A, Gražulis S (2021) Validation of the crystallography open database using the crystallographic information framework. J Appl Crystallogr 54(2):661–67210.1107/S1600576720016532 ↗
52. Gražulis S et al. (2009) Crystallography Open Database–an open-access collection of crystal structures. J Appl Crystallogr 42(4):726–72910.1107/S0021889809016690 ↗
53. Renaudin G, Gomes S, Nedelec J-M (2017) First-row transition metal doping in calcium phosphate bioceramics: A detailed crystallographic study. Materials 10(1):9210.3390/ma10010092 ↗
54. Pai Z et al. (2005) Catalytic oxidation of olefins and alcohols with hydrogen peroxide in a two-phase system giving mono-and dicarboxylic acids. Russian Chem Bull 54:1847–185410.1007/s11172-006-0047-z ↗
55. Antony C et al. (2011) FT-IR and FT-Raman study of Nasicon type phosphates, ASnFe (PO4) 3 [a= Na2, Ca, Cd]. Spectrochimica Acta Part A 78(1):415–41910.1016/j.saa.2010.11.003 ↗
56. Tiwari A et al. (2016) Synthesis, characterization and optical properties of polymer‐based ZnS nanocomposites. Luminescence 31(2):428–43210.1002/bio.2978 ↗
57. Ahmed A et al. (2018) XRD and ATR/FTIR investigations of various montmorillonite clays modified by monocationic and dicationic imidazolium ionic liquids. J Mol Struct 1173:653–66410.1016/j.molstruc.2018.07.039 ↗
58. Cecen V et al. (2008) FTIR and SEM analysis of polyester‐and epoxy‐based composites manufactured by VARTM process. J Appl Polym Sci 108(4):2163–217010.1002/app.27857 ↗
59. De G et al. (1993) FTIR studies of gel to glass conversion in TEOS-fumed silica-derived gels. J Non Crystalline solids 155(3):253–25810.1016/0022-3093(93)91259-6 ↗
60. Ivanković M et al. (2009) Preparation and properties of organic–inorganic hybrids based on poly (methyl methacrylate) and sol–gel polymerized 3-glycidyloxypropyltrimethoxysilane. Polymer 50(12):2544–255010.1016/j.polymer.2009.03.059 ↗
61. Fedel M (2017) Effect of sol–gel layers obtained from GLYMO/MTES mixtures on the delamination of a cataphoretic paint on AA1050. J Coat Technol Res 14(2):425–43510.1007/s11998-016-9860-y ↗
62. Espanol M et al. (2010) Investigation of the hydroxyapatite obtained as hydrolysis product of α-tricalcium phosphate by transmission electron microscopy. CrystEngComm 12(10):3318–332610.1039/c001754j ↗
63. Targonska S et al. (2019) A new approach to spectroscopic and structural studies of the nano-sized silicate-substituted hydroxyapatite doped with Eu 3+ ions. Dalton Trans 48(23):8303–831610.1039/C9DT01025D ↗
64. Zhang L, Zhang J, Liu R (2015) Organic–inorganic hybrid sol–gel coatings for corrosion protection of aluminum alloys. Surf Innov 4(2):51–6910.1680/jsuin.15.00013 ↗
65. Kasten L et al. (2001) An XPS study of cerium dopants in sol–gel coatings for aluminum 2024-T3. Surf Coat Technol 140(1):11–1510.1016/S0257-8972(01)01004-0 ↗
66. Chambers BD, Taylor SR (2007) The high throughput assessment of aluminium alloy corrosion using fluorometric methods. Part II – A combinatorial study of corrosion inhibitors and synergistic combinations. Corros Sci 49(3):1597–160910.1016/j.corsci.2006.08.006 ↗
67. Lopez-Garrity OA (2013) Corrosion inhibition mechanisms of aluminum alloy 2024-T3 by selected non-chromate inhibitors. The Ohio State University, Ann Arbor, p 272
68. Buchheit RG et al. (1997) Local dissolution phenomena associated with S phase (Al2CuMg) particles in aluminum alloy 2024‐T3. J Electrochem Soc 144(8):2621–262810.1149/1.1837874 ↗
69. Yasakau KA et al. (2006) Mechanism of corrosion inhibition of AA2024 by rare-earth compounds. J Phys Chem B 110(11):5515–552810.1021/jp0560664 ↗
70. Chen GS, Gao M, Wei RP (1996) Microconstituent-induced pitting corrosion in aluminum alloy 2024-T3. Corrosion 52(1):8–1510.5006/1.3292099 ↗
71. Ho D et al. (2006) Cerium dibutylphosphate as a corrosion inhibitor for AA2024-T3 aluminum alloys. J Electrochem Soc 153(9):B39210.1149/1.2217260 ↗
72. Akid R, Gobara M, Wang H (2011) Corrosion protection performance of novel hybrid polyaniline/sol–gel coatings on an aluminium 2024 alloy in neutral, alkaline and acidic solutions. Electrochim Acta 56(5):2483–249210.1016/j.electacta.2010.12.032 ↗
73. Rosero-Navarro NC et al. (2009) Improved corrosion resistance of AA2024 alloys through hybrid organic–inorganic sol–gel coatings produced from sols with controlled polymerisation. Surf Coat Technol 203(13):1897–190310.1016/j.surfcoat.2009.01.019 ↗
74. Lakshmi R, Sampath S, Aruna S (2021) Silica-alumina based sol-gel coating containing cerium oxide nanofibers as a potent alternative to conversion coating for AA2024 alloy. Surf Coat Technol 411:12700710.1016/j.surfcoat.2021.127007 ↗
75. Gobara M et al. (2015) Corrosion behaviour of AA2024 coated with an acid-soluble collagen/hybrid silica sol–gel matrix. Prog Org Coat 89:57–6610.1016/j.porgcoat.2015.07.026 ↗
76. Zhou Z et al. (2022) Crosslinking control of hydrophobic benzoxazine-based hybrid sol-gel coating for corrosion protection on aluminum alloys. Prog Org Coat 171:10705910.1016/j.porgcoat.2022.107059 ↗
77. Kesmez Ö (2020) Hydrophobic, organic–inorganic hybrid sol–gel coatings containing boehmite nanoparticles for metal corrosion protection. Chem Pap 74(2):673–68810.1007/s11696-019-00931-6 ↗
78. Sarmento V et al. (2010) Corrosion protection of stainless steel by polysiloxane hybrid coatings prepared using the sol–gel process. Surf Coat Technol 204(16-17):2689–270110.1016/j.surfcoat.2010.02.022 ↗
79. Gnedenkov S et al. (2018) Composite coatings formed on the PEO-layers with the use of solutions of tetrafluoroethylene telomers. Surf Coat Technol 346:53–6210.1016/j.surfcoat.2018.04.036 ↗
80. Lei Q et al. (2020) Sol–gel‐based advanced porous silica materials for biomedical applications. Adv Funct Mater 30(41):190953910.1002/adfm.201909539 ↗
81. Miecznikowski K, Cox JA (2020) Electroanalysis based on stand-alone matrices and electrode-modifying films with silica sol-gel frameworks: a review. J Solid State Electrochem 24(11):2617–263110.1007/s10008-020-04697-w ↗
82. Akbarzadeh S, Paint Y, Olivier M-G (2023) A comparative study of different sol-gel coatings for sealing the plasma electrolytic oxidation (PEO) layer on AA2024 alloy. Electrochim Acta 443:14193010.1016/j.electacta.2023.141930 ↗
83. Gobara M et al. (2020) Corrosion protection mechanism of Ce4+/organic inhibitor for AA2024 in 3.5% NaCl. RSC Adv 10(4):2227–224010.1039/C9RA09552G ↗
84. Qi J, Li W (2022) Chromium-based conversion coatings. In Conversion coatings for magnesium and its alloys. Springer, pp 49–7110.1007/978-3-030-89976-9_3 ↗
85. Stoica A-I et al. (2019) Influence of post-treatment time of trivalent chromium protection coating on aluminium alloy 2024-T3 on improved corrosion resistance. Surf Coat Technol 369:186–19710.1016/j.surfcoat.2019.04.051 ↗
86. Li L, Kim DY, Swain GM (2012) Transient formation of chromate in trivalent chromium process (TCP) coatings on AA2024 as probed by Raman spectroscopy. J Electrochem Soc 159(8):C32610.1149/2.019208jes ↗
87. Cieplik F et al. (2020) Ca2+ release and buffering effects of synthetic hydroxyapatite following bacterial acid challenge. BMC Oral Health 20(1):1–810.1186/s12903-020-01080-z ↗
88. Zhang Y, Wang Y (2012) The effect of hydroxyapatite presence on the degree of conversion and polymerization rate in a model self-etching adhesive. Dent Mater 28(3):237–24410.1016/j.dental.2011.10.003 ↗
89. Wang H, Akid R (2007) A room temperature cured sol–gel anticorrosion pre-treatment for Al 2024-T3 alloys. Corros Sci 49(12):4491–450310.1016/j.corsci.2007.04.015 ↗
90. Wang H, Akid R, Gobara M (2010) Scratch-resistant anticorrosion sol–gel coating for the protection of AZ31 magnesium alloy via a low temperature sol–gel route. Corros Sci 52(8):2565–257010.1016/j.corsci.2010.04.002 ↗
91. Chowdhury ND, Ghosh K (2018) Electrochemical behaviour of dental amalgam in natural, artificial saliva and in 0.90 wt.% NaCl solution. Corros Sci 133:217–23010.1016/j.corsci.2018.01.015 ↗
92. Yang H-Q et al. (2021) Effects of immersion temperature on the performance of a marine epoxy-based organic coating for ballast tanks. J Mater Eng Perform 30(6):4458–446510.1007/s11665-021-05714-3 ↗
93. Fan C et al. (2021) Electrochemical behavior and interfacial delamination of a polymer-coated galvanized steel system in acid media. ACS omega 6(31):20331–2034010.1021/acsomega.1c02270 ↗
94. Trevisanello E et al. (2021) Polycrystalline and single crystalline NCM cathode materials—quantifying particle cracking, active surface area, and lithium diffusion. Adv Energy Mater 11(18):200340010.1002/aenm.202003400 ↗
95. Shao Z et al. (2022) High-pressure induced acceleration pathways for water diffusion in heavy duty anticorrosion coatings under deep ocean environment:(I) the samples subjected to high-pressure pre-processing. Prog Org Coat 170:10694810.1016/j.porgcoat.2022.106948 ↗
96. Li S et al. (2021) Reinforced anticorrosion performance of waterborne epoxy coating with eco-friendly L-cysteine modified Ti3C2Tx MXene nanosheets. Prog Org Coat 161:10647810.1016/j.porgcoat.2021.106478 ↗
97. Ralston KD et al. (2008) Corrosion inhibition of aluminum alloy 2024-T3 by aqueous vanadium species. J Electrochem Soc 155(7):C35010.1149/1.2907772 ↗
98. Iannuzzi M, Frankel GS (2007) Mechanisms of corrosion inhibition of AA2024-T3 by vanadates. Corros Sci 49(5):2371–239110.1016/j.corsci.2006.10.027 ↗
99. Zheng T et al. (2021) Corrosion inhibition of AA2024-T3 in alkaline solution by disodium-N-dodecyliminodiacetate: Experimental and theoretical studies. Colloids Surf A: Physicochemical Eng Asp 626:12698910.1016/j.colsurfa.2021.126989 ↗
100. Li C, Guo X, Frankel GS (2021) Corrosion inhibition of AA2024-T3 by a coating containing dual-pH sensitive, corrosion inhibitor loaded microspheres. Corros Sci 192:10983510.1016/j.corsci.2021.109835 ↗