Development of microstructures in rapidly-quenched Mg85Y9Zn6 alloy ribbons during heating at a constant speed examined by simultaneous small- and wide angle scattering measurements

Developments of microstructures during heating Mg85Y9Zn6 amorphous ribbons have been examined by in-situ synchrotron radiation small- and wide-angle scattering measurements. The samples show sharp crystallization peak in a DSC measurement at 450 K for a heating rate of 10 K/min. During and just after crystallization, clustering occurred first within supersaturated hcp crystallites, with concomitant hcp grain growth. Above 550 K, the spatial arrangements of the cluster became anisotropic, eventually lead to 18R LPSO structures accompanied by introduction of stacking faults.