Deformation-induced grain coalescence in an electrodeposited pure iron sheet studied by in situ neutron diffraction and electron backscatter diffraction

Abstract The plastic deformation behavior of an ultrafine-grained electrodeposited pure iron sheet with a strong {1 1 1}〈 h k l 〉 texture was studied by in situ neutron diffraction during tensile deformation at room temperature and by electron backscatter diffraction (EBSD). The combination of volume-averaged crystallographic orientation changes determined by neutron diffraction and the local orientation relationship determined by EBSD reveals a texture change to {1 1 1}〈1 1 0〉 and corresponding microstructural changes with tension deformation. Related to such grain rotation, grain coalescence on deformation was found using semi in situ EBSD. The results obtained are explained using a characteristic slip model, which also gives a reason for the ultrahigh Lankford value of this material.