Effective preparation of crack-free silica aerogels via ambient drying

Effective ambient-drying techniques for synthesizing crack-free silica aerogel bulks from the industrial waterglass have been developed. Silica wet gels were obtained from aqueous colloidal silica sols prepared by ion-exchange of waterglass solution (4–10 wt% SiO2). Crack-free monolithic silica aerogel disks (diameter of 22 mm and thickness of 7 mm) were produced via solvent exchange/surface modification of the wet gels using isopropanol/trimethylchlorosilane/n-Hexane solution, followed by ambient drying. The effects of the silica content in sol and the molar ratio of trimethylchlorosilane/pore water on the morphology and property of final aerogel products were also investigated. The porosity, density, and specific surface area of silica aerogels were in the range of 92–94%, 0.13–0.16 g/cm3, and ∼675 m2/g, respectively. The degree of springback during the ambient drying processing of modified silica gels was 94%.