Synthesis and photoluminescence properties of nanostructured mullite/α-Al2O3
Source abstract
Abstract
Abstract Phase transformation of α-Al2O3 to mullite was observed by correlated X-ray diffraction and low-temperature (7 K) time- and energy-resolved photoluminescence methods. The aluminosilicate solids with different Si:Al ratios were prepared after thermal treatment (1400 °C) of ultraporous alumina (UPA) monoliths impregnated with vapour of silica precursors at room temperature. The initial dispersion of Si is homogeneous on a size-scale of 5 nm raw UPA fibres, which grow in size during the thermal treatment stage up to ∼50–100 nm. Three phases were resolved in the considered SiO2/Al2O3 system: silica, α-Al2O3 and their interaction product 2:1 mullite (2Al2O3:SiO2). The 2:1 mullite mass increases and α-Al2O3 mass decreases with an increase of the initial silica content. At the SiO2 content in the initial system above 20 mol.%, the phase transformation to 2:1 mullite is complete and no α-Al2O3 was observed. No mullite phases with either lower or higher Si content were observed. The fundamental absorption onset energy 7.55 eV of 2:1 mullite was measured.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Advanced ceramic materials synthesis · Microwave Dielectric Ceramics Synthesis · Nuclear materials and radiation effects
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (23)
Show source-provided references
1. Aksay · J Am Ceram Soc · 1991 · 74 · 234310.1111/j.1151-2916.1991.tb06768.x ↗
2. Schneider · 2005
3. Mullite
4. Aryal · Am Mineral · 2008 · 93 · 11410.2138/am.2008.2664 ↗
5. Aryal · J Am Ceram Soc · 2012 · 95 · 207510.1111/j.1551-2916.2012.05172.x ↗
6. Aryal SR. PhD thesis, University of Missouri-Kansas City; 2012.
7. Büchner · Phys Status Solidi (b) · 1977 · 80 · 61510.1002/pssb.2220800224 ↗
8. Vignes · J Mater Sci · 2008 · 43 · 123410.1007/s10853-007-2260-z ↗
9. di Costanzo · Mater Sci Forum · 2004 · 453–454 · 31510.4028/www.scientific.net/MSF.453-454.315 ↗
10. Zimmerer · Nucl Instrum Methods Phys Res A · 1991 · 308 · 17810.1016/0168-9002(91)90620-6 ↗
11. Valbis · Rad Effects Defects Solids · 1991 · 116 · 17110.1080/10420159108221357 ↗
12. Kirm · Phys Rev B · 1999 · 60 · 50210.1103/PhysRevB.60.502 ↗
13. Museur · Phys Status Solidi RRL · 2013 · 7 · 102610.1002/pssr.201308040 ↗
14. Tippins · Phys Rev B: Condens Matter · 1970 · 1 · 12610.1103/PhysRevB.1.126 ↗
15. Gaft · J Lumin · 2012 · 132 · 285510.1016/j.jlumin.2012.04.045 ↗
16. Trinkler · Opt Mater · 2011 · 33 · 81710.1016/j.optmat.2010.12.020 ↗
17. Scherban AP, Virich VD, Solopichin AD, Kovtun GP, Nguyen HN, Amamra M, et al. In: Proc EMRS 2014 spring conference, 26–30 May, Lille.
18. Snytnikov · Kinet Catal · 2005 · 46 · 26010.1007/s10975-005-0072-1 ↗
19. Wojtowicz · Phys Rev B · 1989 · 39 · 869510.1103/PhysRevB.39.8695 ↗
20. Wen · J Am Ceram Soc · 1998 · 81 · 334510.1111/j.1151-2916.1998.tb02781.x ↗
21. Patra · Opt Mater · 2005 · 27 · 139610.1016/j.optmat.2004.10.002 ↗
22. Pan · J Cryst Growth · 2008 · 310 · 69910.1016/j.jcrysgro.2007.11.089 ↗
23. Tippins · Phys Rev B · 1970 · 1 · 12610.1103/PhysRevB.1.126 ↗