Atomistic simulation of martensitic phase transformation at the crack tip in B2 NiAl

Ya-Fang Guo, Yue-Sheng Wang, Wen-Ping Wu, Dong-Liang Zhao

Acta Materialia· Volume 55· Issue 11
Publisher page

Abstract

Abstract Mechanisms of low-temperature deformation at the crack tip in B2 NiAl are studied by molecular dynamics simulations. The stress-induced martensitic transformation is found to occur at the crack tip when a sufficiently high stress concentration exists. For cracks with 〈1 0 0〉 crack fronts, the layered structures of martensites are formed at the crack tip, which is caused by the atoms’ relative displacement on a basal plane due to the shear stress at the crack tip. The mechanism of the martensitic transformation from the B2 to the L1 0 structures occurs along the Bain path. For cracks with 〈1 1 0〉 crack fronts, the martensitic transformation occurs without any layered structures existing. The phase transformation is caused by the atoms’ relative displacements at different atoms layers in the entire martensite formed region.
Source: openaire · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Intermetallics and Advanced Alloy Properties · MXene and MAX Phase Materials · Microstructure and mechanical properties

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (27)

Show source-provided references
1. Chang · Acta Metall Mater · 1992 · 40 · 272710.1016/0956-7151(92)90343-D ↗
2. Brzeski · Mater Sci Eng · 1993 · A170 · 1110.1016/0921-5093(93)90364-K ↗
3. Schryvers · Micro Microsc Acta · 1989 · 20 · 15310.1016/0739-6260(89)90040-3 ↗
4. Hangen UD, Sauthoff G. Micro Mater (Proceedings of the Micro-Mat ’97). Berlin, 1997;412.
5. Hangen · Intermetallics · 1999 · 7 · 50110.1016/S0966-9795(98)00101-0 ↗
6. Ludwig · Acta Mater · 1998 · 46 · 313510.1016/S1359-6454(98)00013-5 ↗
7. Rubini · Phys Rev · 1993 · B 48 · 9910.1103/PhysRevB.48.99 ↗
8. Ozgen · J Phys Chem Solids · 2003 · 64 · 45910.1016/S0022-3697(02)00335-9 ↗
9. Ozgen · J Phys Chem Solids · 2004 · 65 · 86110.1016/j.jpcs.2003.09.004 ↗
10. Kazanc · Physica · 2003 · B 334 · 37510.1016/S0921-4526(03)00101-7 ↗
11. Wang · Mater Sci Eng · 2006 · A438–440 · 10210.1016/j.msea.2006.02.194 ↗
12. Li · J Appl Phys · 2004 · 95 · 169810.1063/1.1638609 ↗
13. Clapp · Modell Simul Mater Sci Eng · 1994 · 2 · 55110.1088/0965-0393/2/3A/009 ↗
14. Shao · Metall Trans · 1996 · A 27 · 147710.1007/BF02649808 ↗
15. Guénin · Mater Sci Eng · 1996 · B 37 · 19310.1016/0921-5107(95)01485-3 ↗
16. Guo · Acta Mater · 2007 · 55 · 40110.1016/j.actamat.2006.08.022 ↗
17. Farkas · Modell Simul Mater Sci Eng · 1995 · 3 · 20110.1088/0965-0393/3/2/005 ↗
18. Voter · Proc Symp Mater Res Soc · 1987 · 82 · 17510.1557/PROC-82-175 ↗
19. Becquart · Phys Rev · 1993 · B48 · 610.1103/PhysRevB.48.6 ↗
20. Clapp · Proc Symp Mater Res Soc · 1989 · 133 · 2910.1557/PROC-133-29 ↗
21. Mathematical theories of brittle facture
22. Riffkin J, Center for Simulation, University of Connecticut, CT. Available from: http:/www.ims.uconn.edu/centers/simul/.
23. Enami · Scripta Metall · 1978 · 12 · 22310.1016/0036-9748(78)90102-3 ↗
24. Martynow · Scripta Metall · 1983 · 17 · 116710.1016/0036-9748(83)90277-6 ↗
25. Murakami · Mater Trans JIM · 1992 · 33 · 28210.2320/matertrans1989.33.282 ↗
26. Balandraud · J Mech Phys Solids · 2007 · 55 · 19410.1016/j.jmps.2006.03.009 ↗
27. Mao · J Appl Phys · 1967 · 38 · 27210.1063/1.1708965 ↗