Synthesis and Characterization of Al(OH) 3 -Y(OH) 3 -ZrB 2 Composite Particles

Jie-Guang Song, Lian-Meng Zhang, Jun-Guo Li, Jian-Rong Song

Journal of Reinforced Plastics and Composites· Volume 26· Issue 2
Publisher page
Source abstract

Abstract

In order to decrease the oxidization and improve the strength of ZrB 2 at high temperature, the surface of ZrB 2 was coated with Al(OH) 3 and Y(OH) 3 to synthesize Al(OH) 3 -Y(OH) 3 -ZrB 2 composite particles. Through TEM, EPMA and SEM analysis, when pH was about 9, Al(OH) 3 -Y(OH) 3 -ZrB 2 composite particles were successfully synthesized by co-precipitation methods. The coating layer was about 25 nm, which has compaction and conformability. Dispersibility of coated ZrB 2 with Al(OH) 3 and Y(OH) 3 particles were very good. Synthesis of Al(OH) 3 -Y(OH) 3 -ZrB 2 composite powder will lay the foundation for preparing high-performance YAG/ZrB 2 and Al 2 O 3 -YAG/ZrB 2 multiphase ceramic materials.
Source: crossref · Quality: baseline

Research context

Ceramics & glassesComposites

OpenAlex topics: Advanced ceramic materials synthesis · MXene and MAX Phase Materials · Magnesium Oxide Properties and Applications

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

State Key Lab of Advanced Technology for Materials Synthesis and Processing Wuhan University of Technology, Wuhan 430070, China,

State Key Lab of Advanced Technology for Materials Synthesis and Processing Wuhan University of Technology, Wuhan 430070, China

References (15)

Show source-provided references
1. 10.1023/A:100678511639510.1023/A:1006785116395 ↗
2. 10.1023/A:101376812952810.1023/A:1013768129528 ↗
3. 10.1023/A:100447081774410.1023/A:1004470817744 ↗
4. 10.1023/A:100452952716210.1023/A:1004529527162 ↗
5. 10.1023/A:102397622850210.1023/A:1023976228502 ↗
6. 10.1023/A:101601752170210.1023/A:1016017521702 ↗
7. 10.1007/s10910-004-1103-210.1007/s10910-004-1103-2 ↗
8. 10.1023/A:100959950213810.1023/A:1009599502138 ↗
9. Morzc, C. · Amer. Ceram. Soc. Bull. · 1995 · 74 · 165
10. 10.1016/S0955-2219(00)00026-110.1016/S0955-2219(00)00026-1 ↗
11. 10.1016/S0925-8388(01)01742-X10.1016/S0925-8388(01)01742-X ↗
12. 10.1016/S0257-8972(02)00058-010.1016/S0257-8972(02)00058-0 ↗
13. Li, W. Q. · J. Inorg. Mater. · 2000 · 15 · 155
14. Zhang, N. · J. Rare Earths · 2005 · 23 · 299
15. 10.1016/S0955-2219(99)00072-210.1016/S0955-2219(99)00072-2 ↗