Experimental Studies on Impact Behaviour of Woven Fabric Composites: Effect of Impact Parameters
Source abstract
Abstract
Experimental studies have been presented on the impact behaviour of plain weave E-glass-epoxy laminates with different combinations of impactor mass and incident impact velocity with the same incident impact energy of 24.43 J. Four combinations of impactor mass-incident impact velocity have been considered. Impact tests have been carried out on an instrumented drop weight impact test apparatus. The unsupported area of the specimens during the impact loading was 127 mm 127 mm with clamped boundary condition. Thickness of the plate was 5 mm. Post-impact-compression testing of impacted specimens has been carried out using Compression-After-Impact test fixture as per NASA 1142 standard. It is observed that for the materials tested, damage tolerance is higher for low mass and high velocity combination as compared to high mass and low velocity combination.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Mechanical Behavior of Composites · Textile materials and evaluations · Structural Analysis of Composite Materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Aerospace Engineering Department Indian Institute of Technology Bombay, Powai, Mumbai - 400 076, India
References (39)
Show source-provided references
1. 10.1177/00219983850190010410.1177/002199838501900104 ↗
2. 10.1016/0010-4361(85)90279-410.1016/0010-4361(85)90279-4 ↗
3. 10.1177/00219983880220060210.1177/002199838802200602 ↗
4. 10.1007/BF0232136210.1007/BF02321362 ↗
5. Bishop, S.M. · 1989 · 173
6. 10.1016/0010-4361(90)90008-K10.1016/0010-4361(90)90008-K ↗
7. 10.1016/0010-4361(91)90549-V10.1016/0010-4361(91)90549-V ↗
8. 10.1177/00219983910250080310.1177/002199839102500803 ↗
9. 10.1177/00219983910250020510.1177/002199839102500205 ↗
10. 10.1177/00219983920260060310.1177/002199839202600603 ↗
11. 10.1177/00219983920260120210.1177/002199839202601202 ↗
12. 10.1115/1.311106510.1115/1.3111065 ↗
13. 10.1177/00219983940280080110.1177/002199839402800801 ↗
14. 10.1016/1359-835X(96)00074-710.1016/1359-835X(96)00074-7 ↗
15. 10.1007/BF0035309110.1007/BF00353091 ↗
16. 10.1177/00219983960300170210.1177/002199839603001702 ↗
17. 10.1177/00219983970310130410.1177/002199839703101304 ↗
18. 10.1016/S0734-743X(98)00036-010.1016/S0734-743X(98)00036-0 ↗
19. 10.1177/00219983980320120310.1177/002199839803201203 ↗
20. 10.1177/07316844980170140110.1177/073168449801701401 ↗
21. 10.1016/S0266-3538(99)00023-810.1016/S0266-3538(99)00023-8 ↗
22. 10.1016/S0266-3538(99)00080-910.1016/S0266-3538(99)00080-9 ↗
23. 10.1016/S0266-3538(99)00079-210.1016/S0266-3538(99)00079-2 ↗
24. 10.1016/S0266-3538(99)00183-910.1016/S0266-3538(99)00183-9 ↗
25. 10.1106/X80M-4UEF-CPPK-M15E10.1106/X80M-4UEF-CPPK-M15E ↗
26. Naik, N.K. · 750
27. Naik, N.K. · Journal of Reinforced Plastics and Composites · 2001 · 20 · 720
28. 10.1016/0010-4361(90)90423-T10.1016/0010-4361(90)90423-T ↗
29. 10.1016/0010-4361(93)90043-810.1016/0010-4361(93)90043-8 ↗
30. 10.1016/0263-8223(93)90018-L10.1016/0263-8223(93)90018-L ↗
31. 10.1016/0010-4361(95)96809-K10.1016/0010-4361(95)96809-K ↗
32. 10.1016/0263-8223(96)00031-110.1016/0263-8223(96)00031-1 ↗
33. 10.1016/1359-835X(96)00083-810.1016/1359-835X(96)00083-8 ↗
34. 10.1520/CTR10947J10.1520/CTR10947J ↗
35. 10.1016/S0734-743X(99)00003-210.1016/S0734-743X(99)00003-2 ↗
36. 36. Standard Tests for Toughened Resin Composites, NASA Reference Publication 1092, (1983).
37. 37. NASA/Aircraft Industry Standard Specification for Graphite Fiber Toughened Thermoset Resin Composite Materials, NASA Reference Publication 1142, (1985).
38. 10.1017/CBO978051157450410.1017/CBO9780511574504 ↗
39. 10.1080/1075941980894589510.1080/10759419808945895 ↗