Microstructural evolution of precipitation-hardened β-type titanium alloy through high-pressure torsion

Abstract In order to elucidate the microstructural refinement mechanism and the effect of secondary phase on the microstructural evolution of β -type titanium alloy, severe plastic deformation was conducted on samples of a precipitation-hardened Ti–29Nb–13Ta–4.6Zr (TNTZ). Specifically, TNTZ that was precipitation-hardened through an aging treatment (TNTZ AT ) was subjected to high-pressure torsion (HPT) processing (TNTZ AHPT ). The microstructure of TNTZ AHPT , which has been evaluated as a function of the torsional rotation number, N , exhibits ultrafine elongated β grains. The needle-like α precipitates in TNTZ AT , which exhibit a diameter of approximately 12 nm, are homogeneously distributed within the β grains. The dislocation density and subgrain diameter, estimated by X-ray line profile analysis, saturate at approximately 4.2 × 10 16 m −2 and 12.2 nm, respectively, at N ⩾ 10. The β grains contain nanostructured subgrains having non-uniform morphologies surrounded by blurred and wavy boundaries. A saturated hardness distribution at approximately 450 HV indicates that microstructural homogeneity has been achieved at N ⩾ 10. The α precipitates enhance the β grain refinement and microstructural homogeneity is achieved in TNTZ AHPT at N ⩾ 10, whereas this occurs at later stages ( N > 20) in TNTZ which is solution-treated and therefore does not contain any α precipitates.